Kowiri Tirohanga Matao Kowiri tira
Whakaahuatanga Poto:
Kowiri Kowiri tira Whakaaturanga Ratonga kotahi: |
Te Hanga Matū me nga ahuatanga Miihini |
C% | Si% | Mn% | P% | S% | Kr% | Ni% | N% | Mo% | Ti% |
0.08 | 0.75 | 2.0 | 0.045 | 0.030 | 18.0-20.0 | 8.0-10.5 | 0.10 | – | – |
T*S | Y*S | Te pakeke | Te whakaroa | |
(Mpa) | (Mpa) | HRB | HB | (%) |
520 | 205 | – | – | 40 |
Whakaahuatanga o te kowiri tira kowiri tira makariri: |
Whakaahuatanga | Kowiri tira kowiri tira makariri |
Rauemi | 201, 202,304, 304L,316,316L,317,317L,321,347H,309,309S,310,310S,410,420,430, etc |
paerewa | ASTM A240, JIS G4304, G4305, GB/T 4237, GB/T 8165, BS 1449, DIN17460, DIN 17441 |
Rahi | Matotoru: 0.03-3mm Whānui: 8-600mm, |
Whakamutu mata | 2B,BA,2D,No.1,No.4,No.8,8K,(whakaata), orohia,HL(raina makawe), etc |
Taupānga | a) Nga ahumahi ratonga whanui (hinu, kai, matū, pepa, tongi, papanga, rererangi me te karihi) b) Te pehanga me te whakawhiti wera c) Te hanga me te whakapaipai |
Mōkī | Kaweake paerewa paerewa: pouaka rakau paihere, ka hiahiatia ranei; |
Te wa tuku | E ai ki te nui o te kaihoko. |
Utu | T / T, L / C, me Western Union |
Te maakete | Europe, Amerika ki te Tonga, Awherika, Oceania, penei: USA, Tiamana, Inia, Iran, Dubai, Iraq, Vietnam, Ireland, Singapore, me era atu |
Ētahi atu māka oKowiri tira kowiri tira makariri: |
Kōeke | Si | Mn | p | S | Cr | Mo | Ni | atu |
201 | 0.15 | 1.00 | 5.5-7.5 | 0.06 | 0.03 | 16-18 | - | 1.0 |
202 | 0.15 | 1.00 | 7.5-10.0 | 0.06 | 0.03 | 17-19 | - | 4.0-6.0 |
301 | 0.15 | 1.00 | 2.00 | 0.045 | 0.03 | 16-18 | - | 6.0-8.0 |
304 | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | 18-20 | - | 8-10.5 |
304l | 0.03 | 1.00 | 2.00 | 0.045 | 0.03 | 18-20 | - | 9-13 |
309s | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | 22-24 | - | 12-15 |
310s | 0.08 | 1.5 | 2.00 | 0.045 | 0.03 | 24-26 | - | 19-22 |
316 | 0.03 | 1.00 | 2.00 | 0.045 | 0.03 | 16-18 | 2-3 | 10-14 |
316L | 0.03 | 1.00 | 2.00 | 0.045 | 0.03 | 16-18 | 2-3 | 12-15 |
321 | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | 17-19 | - | 9-13 |
430 | 0.12 | 0.75 | 1.00 | 0.04 | 0.03 | 16-18 | - | =0.6 |