Incazelo emfushane:
| Ukucaciswa kwepayipi lensimbi elingagqwali |
| 1. Umkhiqizo | Ipayipi le-welded engenasici |
| 2. Izinto ezibonakalayo | 31,301,309, 32110, 321,347,410,430,409Letan. |
| 3. Okujwayelekile | I-ASTM, ASME, DIN, EN, ISO, JIS, Gost, njll. |
| 4. Usayizi Usayizi | I-OD: kusuka ku-6mm kuya ku-1219mm (NPS kusuka ku-1/8 "kuya ku-40") |
| Wt: kusuka ku-0.7mm kuya ku-38mm (Isheduli kusuka kuma-5s kuya kuma-xxs) | |
| Ubude: Lungisa ubude noma ubude be-UN-fix, max 30meters | |
| 5. Khiqiza inqubo | i-welded, ukugoba okushisayo; ukumelana nokuphikiswa; ukunwebeka okushisayo njll. |
| 6. Ubuso | I-2B, ethathwe, ngo-180g, 320g, satin, hairline, 400g, 500g, 600g |
| , 800g, isibuko ukuqeda | |
| 7. Ukumaka | I-Saky, ibanga, abangenamthungo, okujwayelekile, ubukhulu, ukushisa cha. |
| 8. Iphakheji | Izinyanda ngendwangu engenamanzi ngaphandle. |
| noma ibhokisi le-plywood. | |
| 9. Ubude | 5.8m, 6m, 12m noma njengoba kudingeka |
| Izakhiwo ezejwayelekile zemishini yama-alloys wensimbi angama-304 angenasici: |
| Khuphuka | Amandla we-Tensile (MPA) | Amandla okucindezela (MPA) | Ukucindezela kwe-Proof 0.2% (MPA) | I-Elongation A5 (%) | UHardness Rocwell B |
| 30 | 520-720 | 210 | 210 | 45 min | 92 |
| I-304L | 500-670 | -Mashumi | 45 min | ||
| 304h | 520-720 | 210 | I-45min |
| Amamaki wepayipi ensimbi elingagqwali |
| Ukuthayipha | Khuphuka | Khuphuka | Ingxenye yamakhemikhali% | ||||
| Insimbi engenacala | C | Cr | Ni | Mn | |||
| 201 | I-1CR17MN6NI5N | 0.15 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | ||
| I-201L | 03CR17MN6NI5N | 0.030 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | ||
| 202 | I-1CR18MN8NI5N | 0.15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | ||
| 204 | 03CR16MN8NI2N | 0.030 | 15.00-17.00 | 1.50-3.50 | 7.00-9.00 | ||
| I-1CR18MN10NI5MO3N | 0.10 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 | |||
| I-2CR13MN9NI4 | 0.15-0.25 | 12.00-14.00 | 3.70-5.00 | 8.00-10.00 | |||
| I-2Cr15MN15NI2N | 0.15-0.25 | 14.00-16.00 | 1.50-3,00 | 14.00-16.00 | |||
| I-1CR18MN10NI5MO3N | 0.15 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 | |||
| 301 | I-1CR17NI7 | 0.15 | 16.00-18.00 | 6.00-8.00 | I-2.00 | ||
| 302 | I-1CR18NI9 | 0.15 | 17.00-19.00 | 8.00-10.00 | I-2.00 | ||
| 305 | Y1cr18ni9 | 0.15 | 17.00-19.00 | 8.00-10.00 | I-2.00 | ||
| I-303se | Y1CR18NI9SE | 0.15 | 17.00-19.00 | 8.00-10.00 | I-2.00 | ||
| 30 | 0Cr18NI9 | 0.07 | 17.00-19.00 | 8.00-10.00 | I-2.00 | ||
| I-304L | 00crm19NI10 | 0.030 | 18.00-20.00 | 8.00-10.00 | I-2.00 | ||
| 304N1 | 0rcr19NINI9N | 0.08 | 18.00-20.00 | 7.00-10.50 | I-2.00 | ||
| 304N2 | 0rcr18NI10nbn | 0.08 | 18.00-20.00 | 7.50-10.50 | I-2.00 | ||
| 304ln | 00crm18NI10n | 0.030 | 17.00-19.00 | 8.50-11.50 | I-2.00 | ||
| 305 | 1Cr18NI12 | 0.12 | 17.00-19.00 | 10.5050-13.00 | I-2.00 | ||
| 309s | 0Cr23NI13 | 0.08 | 22.00-24.00 | 12.00-15.00 | I-2.00 | ||
| Ama-310s | 0crrd25ni20 | 0.08 | 24.00-26.00 | 19.00-22.00 | I-2.00 | ||
| I-316 | 0Cr17NI12mo2 | 0.08 | 16.00-18.50 | 10.00-14.00 | I-2.00 | ||
| I-1CR18NI12MO2TI6) | 0.12 | 16.00-19.00 | 11.00-14.00 | I-2.00 | |||
| 0cr18ni12mo2ti | 0.08 | 16.00-19.00 | 11.00-14.00 | I-2.00 | |||
| I-316L | 00cr17ni14mo2 | 0.030 | 16.00-18.00 | 12.00-15.00 | I-2.00 | ||
| I-316N | 0Cr17NI12mo2n | 0.08 | 16.00-18.00 | 10.00-14.00 | I-2.00 | ||
| I-316N | 00crm17NI13mo2n | 0.030 | 16.00-18.50 | 10.5050-14.50 | I-2.00 | ||
| I-316J1 | 0rcr18ni12mo2cu2 | 0.08 | 17.00-19.00 | 10.00-14.50 | I-2.00 | ||
| I-316J1l | 00crm18ni14mo2cu2 | 0.030 | 17.00-19.00 | 12.00-16.00 | I-2.00 | ||
| I-317 | 0rcr19NI13MO3 | 0.12 | 18.00-20.00 | 11.00-15.00 | I-2.00 | ||
| I-317l | 00cr19NI13mo3 | 0.08 | 18.00-20.00 | 11.00-15.00 | I-2.00 | ||
| I-1CR18NI12MO3TI6 | 0.12 | 16.00-19.00 | 11.00-14.00 | I-2.00 | |||
| 0Cr18NI12mo3ti | 0.08 | 16.00-19.00 | 11.00-14.00 | I-2.00 | |||
| I-317J1 | 0rcr18ni16mo5 | 0.040 | 16.00-19.00 | 15.00-17.00 | I-2.00 | ||
| 321 | I-1CR18NI9TI6 | 0.12 | 17.00-19.00 | 8.00-11.00 | I-2.00 | ||
| 0cr18ni10ti | 0.08 | 17.00-19.00 | 9.00-12.00 | I-2.00 | |||
| 347 | 0Cr18NI111NB | 0.08 | 17.00-19.00 | 9.00-13.00 | I-2.00 | ||
| I-XM7 | I-0Cr18NI9CU3 | 0.08 | 17.00-19.00 | 8.50-10.50 | I-2.00 | ||
| Xm15j1 | 0Cr18NI13SI4 | 0.08 | 15.00-20.00 | 11.50-15.00 | I-2.00 | ||
| Ouden Insimbi yensimbi engenacala | 329j1j1 | 0cr26ni5mo2 | 0.08 | 23.00-28.00 | 3.00-6.00 | I-1.50 | 0.035 | 0.030 | 1.00-3.00 | 1.00 | - | - | 2) |
| 1Cr18NI11SI4ATI | 0.10-0.18 | 17.50-19.50 | 10.-120.. | I-0.80 | 0.035 | 0.030 | - | 3.40-4.00 | - | - | Al 0,10-0.30; TI 0.40-0.70 | ||
| 00cr18ni5mosi2 | 0.030 | 18.00-19.50 | 4.50-5.50 | 1.00-2.00 | 0.035 | 0.030 | 2.50-3,00 | 1.30-2.00 | - | - | - | ||
| Insimbi yensimbi engenacala | 405 | 0cr13AL | 0.08 | 11.50-14.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | Al 0.10-0.30 |
| I-410L | 00cr12 | 0.030 | 11.00-13.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
| 430 | I-1CR17 | 0.12 | 16.00-18.00 | 3) | I-1.25 | 0.035 | 0.030 | - | 0.75 | - | - | - | |
| I-430f | Y1cr17 | 0.12 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
| 434 | I-1CR17MO | 0.12 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.030 | 0.75-1.25 | 1.00 | - | - | - | |
| 447jj1 | 00crm3mo2 | 0.010 | 28.50-32.00 | - | 0.40 | 0.035 | 0.030 | 1.50-2.50 | 0.40 | - | 0.015 | - | |
| I-XM27 | 00crm2mo | 0.010 | 25.00-27.50 | - | 0.40 | 0.035 | 0.030 | 0.75-1.50 | 0.40 | - | 0.015 | - |
| Insimbi yensimbi engenacala | 403 | I-1CR12 | 0.15 | 11.50-13.00 | 3) | 1.00 | 0.035 | 0.030 | - | 0.50 | - | - | - |
| 410 | I-1CR13 | 0.15 | 11.50-13.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
| 405 | 0cr13 | 0.08 | 11.50-13.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
| 416 | Y1cr13 | 0.15 | 12.00-14.00 | 3) | I-1.25 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
| I-410j1 | I-1CR13MO | 0.08-0.18 | 11.50-14.00 | 3) | 1.00 | 0.035 | 0.030 | 0.30-0.60 | I-0.60 | - | - | - | |
| I-420j1 | I-2CR13 | 0.166-0.25 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
| I-420j2 | 3Cr13 | 0.26-0.35 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
| I-420F | Y3cr13 | 0.26-0.40 | 12.00-14.00 | 3) | I-1.25 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
| 3Cr13MO | 0.28-0.35 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | 0.50-1.00 | I-0.80 | - | - | - | ||
| I-4Cr13 | 0.36-0.45 | 12.00-14.00 | 3) | I-0.80 | 0.035 | 0.030 | - | I-0.60 | - | - | - | ||
| 431 | 1Cr17NI2 | 0.11-0.17 | 16.00-18.00 | 1.50-2.50 | I-0.80 | 0.035 | 0.030 | - | I-0.80 | - | - | - | |
| 440a | I-7cr17 | 0.60-0.75 | 16.00-18.00 | 3) | 1.00 | 0.035 |