    Hastelloy c-4 (ans no6455)

    Izici zeHastelloy C-4 nezicelo Ukubuka konke:
    I-Alloy yi-auntenitic nickel-molybdenum-chromium alloy. Umehluko omkhulu phakathi kwe-nicrofer 6616 HMO namanye ama-alloys okuhlanganiswa okufanayo kwamakhemikhali aqalile ngaphambili yikhabhoni ephansi, i-silicon, i-iron ne-tungsten. Lokhu kuhlanganiswa kwamakhemikhali kuhlinzeka ngokuqina okuhle ngo-650-1040 ° C. Ukumelana okuthuthukile kokugqwala komoya, ukugwema ukuqina komugqa we-corlosion kuncipha kanye nokugqwala kwe-hal yeWeld ngaphansi kwezimo ezifanele zokukhiqiza. I-Alloy isetshenziswa ezinhlelweni zegesi ze-Flue Susselfurization, isitshalo sokuvutha kanye nesisindo se-acid kanye ne-acetic acid namakhemikhali ezolimo, i-titanium dioxide ukukhiqizwa (indlela ye-chlorium), i-electoride atting.
    Hastelloy c-4 brand efanayo:
    NS335 (China) W.NR.2.4610 NIMO16CR1TI (Germany)
    I-Hastelloy C-4 Chemical Composition:

    Ingxubevange
    Khuphuka

    %

    Ni

    Cr

    Fe

    Mo

    Nb

    Co

    C

    Mn

    Si

    S

    Cu

    Al

    Ti

    Hastelloy c-4

    Uku

    Image

    14.5

     

    14.0

                     

    Okusekugcineni

    17.5

    I-3.0

    17.0

     

    I-2.0

    0.009

    1.0

    0.05

    0.01

       

    0.7

    Izakhiwo ze-Hastelloy C-4 ngokomzimba:

    Incekusana
    g / cm3

    Iphuzu elincibilikayo

    Ukuvuselelwa okushisayo
    λ / (w / m • ℃)

    Umthamo othize wokushisa
    J / kg • ℃

    I-Elastic Modulus
    Uhlobo

    I-Shear modulus
    Uhlobo

    Ukumelanakabisa
    • m

    Isilinganiso sikaPoisson

    Umugqa wokunwetshwa komugqa
    A / 10-6 ℃ -1

    8.6

    1335
    1380

    10.1 (100 ℃)

    408

    211

     

    I-1.24

     

    10.9 (100 ℃)

    I-Hastelloy C-4 Mechanical Properties: (Izakhiwo eziphansi zemishini ngo-20 ℃):

    Izindlela Zokushisa Zokushisa

    I-Tensile CerterΣB / MPA

    Isivuno Sokukhiqiza0.2 / MPA

    Isilinganiso se-elongation σ5 /%

    I-Brinell Hardness Hbs

    Ukwelashwa kwesisombululo

    I-690

    275

    40

     

    Amazinga wokukhiqiza we-Hastelloy C-4:

    -Vamile

    Nqabela

    Ukuthethelelwa

    Ipuleti (nge) Material

    Uwaya

    Ipayipi

    Umphakathi waseMelika wokuhlola nezinto zokwakha

    I-ASTM B574

    I-ASTM B336

    I-ASTM B575

     

    I-ASTM B622
    I-ASTM B619
    I-ASTM B626

    Izinto ze-American Aerospace Material Propectifition technical

             

    I-American Society of Enjiniyela Emishini

    I-ASME SB574

    I-ASME SB336

    I-ASME SB575

     

    I-ASTM SB622
    I-ASTM SB619
    I-ASTM SB626

    I-Hastelloy C-4 Process Performance Nezidingo:

    1, kwinqubo yokwelashwa kokushisa ayikwazi ukuxhumana nesibabule, i-phosphorus, ukuhola kanye nezinye izinsimbi eziphansi ezincibilikayo, noma i-alloy izoba yi-brittle, kufanele inake ukususa okunjengopende wokumaka, amakhrayoni okushisa, amakhrayoni anemibala, amafutha nokunye ukungcola. Ukwehlisa okuqukethwe kwe-sulfur kwamafutha kangcono, okuqukethwe se-sulfur yegesi yemvelo kufanele kube ngaphansi kwe-0,1%, okuqukethwe i-sulfur yamafutha asindayo kufanele kube ngaphansi kwe-0,5%. Ukushisa isithando se-Electric Isinqumo esingcono, ngoba isithando sikagesi singalawula ngokunembile izinga lokushisa kanye negesi yesithando selihlanzekile. Uma igesi isitofu igesi ihlanzekile ngokwanele, ungakhetha.
    2, Alloy thermal ukucubungula uhla lokushisa lwe-1080 ℃ ~ 900 ℃, indlela yokupholisa yokupholisa amanzi noma okunye ukuphola okusheshayo. Ukuqinisekisa ukumelana nokugqwala okuhle kakhulu, ukwelashwa kokushisa kufanele kwenziwe ngemuva kokwelashwa okushisa kwesixazululo.