Ⅰ.Ipilẹ imọran ti itọju ooru.
A.The ipilẹ Erongba ti ooru itọju.
Awọn ipilẹ eroja ati awọn iṣẹ tiitọju ooru:
1. Alapapo
Idi naa ni lati gba aṣọ-aṣọ kan ati eto austenite itanran.
2.Ti o mu
Ibi-afẹde ni lati rii daju pe iṣẹ-iṣẹ naa gbona daradara ati lati ṣe idiwọ decarburization ati ifoyina.
3.Cooling
Ibi-afẹde ni lati yi austenite pada si oriṣiriṣi awọn microstructures.
Microstructures lẹhin Heat Itoju
Lakoko ilana itutu agbaiye lẹhin alapapo ati didimu, austenite yipada si oriṣiriṣi awọn microstructures ti o da lori iwọn itutu agbaiye. Awọn oriṣiriṣi microstructures ṣe afihan awọn ohun-ini oriṣiriṣi.
B.The ipilẹ Erongba ti ooru itọju.
Pipin Da lori Alapapo ati Awọn ọna Itutu, bakanna bi Microstructure ati Awọn ohun-ini ti Irin
1.Conventional Ooru Itọju (Iwoye Itọju Ooru):Tempering,Annealing, Normalizing,Quenching
2.Surface Heat Treatment: Iwaju Idaju, Imudaniloju Imudanu Alapapo Imudara, Imudanu Iyẹwu Imọlẹ Ina, Itanna Olubasọrọ Alapapo Dada Quenching.
3.Chemical Heat Itoju: Carburizing, Nitriding, Carbonitriding.
4.Other Awọn itọju Ooru:Itọju Ooru Atmosphere Iṣakoso,Itọju Ooru Igbale,Itọju Ooru ibajẹ.
C.Critical otutu ti Irin
Iwọn otutu iyipada to ṣe pataki ti irin jẹ ipilẹ pataki fun ṣiṣe ipinnu alapapo, didimu, ati awọn ilana itutu agbaiye lakoko itọju ooru. O ti pinnu nipasẹ aworan atọka alakoso irin-erogba.
Ipari bọtini:Awọn gangan lominu ni iyipada otutu ti irin nigbagbogbo lags sile awọn tumq si lominu ni iyipada otutu. Eyi tumọ si pe a nilo igbona pupọ lakoko alapapo, ati itutu agbaiye jẹ pataki lakoko itutu agbaiye.
Ⅱ.Annealing ati Normalizing ti Irin
1. Definition ti Annealing
Annealing jẹ irin alapapo si iwọn otutu loke tabi isalẹ aaye pataki Ac₁ dimu ni iwọn otutu yẹn, ati lẹhinna tutu laiyara, nigbagbogbo laarin ileru, lati ṣaṣeyọri eto ti o sunmọ iwọntunwọnsi.
2. Idi ti Annealing
① Ṣatunṣe Lile fun Ṣiṣe ẹrọ: Ṣiṣeyọri lile lile ẹrọ ni iwọn HB170 ~ 230.
② Yiyọ Wahala Iku silẹ: Ṣe idilọwọ ibajẹ tabi fifọ lakoko awọn ilana ti o tẹle.
③Ṣatunto Ilana Ọkà: Ṣe ilọsiwaju microstructure.
④ Igbaradi fun Itọju Ooru Ikẹhin: Ngba granular (spheroidized) pearlite fun piparẹ ati iwọn otutu ti o tẹle.
3.Spheroidizing Annealing
Awọn alaye ilana: otutu alapapo wa nitosi aaye Ac₁.
Idi: Lati spheroidize cementite tabi carbides ninu irin, Abajade ni granular (spheroidized) pearlite.
Iwọn to wulo: Ti a lo fun awọn irin pẹlu eutectoid ati awọn akojọpọ hypereutectoid.
4.Diffusing Annealing (Homogenizing Annealing)
Awọn alaye ilana: Awọn iwọn otutu alapapo jẹ die-die ni isalẹ laini solvus lori aworan atọka alakoso.
Idi: Lati yọkuro ipinya.
①Fun kekere-erogba, irinpẹlu akoonu erogba ti o kere ju 0.25%, deede jẹ ayanfẹ ju annealing bi itọju ooru igbaradi.
②Fun irin alabọde-erogba pẹlu akoonu erogba laarin 0.25% ati 0.50%, boya annealing tabi deede le ṣee lo bi itọju ooru igbaradi.
③Fun irin alabọde-si erogba-giga pẹlu akoonu erogba laarin 0.50% ati 0.75%, a ṣe iṣeduro ifasilẹ ni kikun.
④ Fun giga-erogba, irinpẹlu akoonu erogba ti o tobi ju 0.75%, deede jẹ lilo akọkọ lati yọkuro Fe₃C nẹtiwọọki, atẹle nipa annealing spheroidizing.
Ⅲ.Quenching ati Tempering ti Irin
A.Quenching
1. Itumọ ti Quenching: Quenching pẹlu alapapo irin si iwọn otutu kan loke Ac₃ tabi Ac₁ ojuami, dimu ni iwọn otutu yẹn, ati lẹhinna itutu rẹ ni iwọn ti o tobi ju iwọn itutu agbaiye pataki lati dagba martensite.
2. Idi ti Quenching: Ifojusi akọkọ ni lati gba martensite (tabi nigbakan bainite kekere) lati mu líle ati wọ resistance ti irin. Quenching jẹ ọkan ninu awọn ilana itọju ooru pataki julọ fun irin.
3.Determining Quenching Temperatures for different Types of Steel
Irin Hypoeutectoid: Ac₃ + 30°C si 50°C
Eutectoid ati Irin Hypereutectoid: Ac₁ + 30°C si 50°C
Irin Alloy: 50 ° C si 100 ° C loke iwọn otutu to ṣe pataki
4.Cooling Awọn abuda ti Alabọde Quenching Ideal:
Itutu agbaiye ti o lọra Ṣaaju “Imu” Iwọn otutu: Lati dinku aapọn gbona ni kikun.
Agbara Itutu giga Nitosi “Imu” otutu: Lati yago fun dida awọn ẹya ti kii ṣe martensitic.
Itutu agbaiye ti o lọra nitosi aaye M₅: Lati dinku wahala ti o fa nipasẹ iyipada martensitic.
5.Quenching Awọn ọna ati Awọn abuda wọn:
Quenching ti o rọrun: Rọrun lati ṣiṣẹ ati pe o dara fun kekere, awọn iṣẹ ṣiṣe ti o rọrun-sókè. Abajade microstructure jẹ martensite (M).
② Quenching ilọpo meji: Idiju diẹ sii ati nira lati ṣakoso, ti a lo fun irin-irin giga-erogba ti o ni iwọn eka ati awọn iṣẹ iṣẹ irin alloy nla. Abajade microstructure jẹ martensite (M).
③ Quenching Baje: Ilana ti o ni eka diẹ sii, ti a lo fun nla, awọn ohun elo irin alloy ti o ni iwọn eka. Abajade microstructure jẹ martensite (M).
④ Isothermal Quenching: Ti a lo fun kekere, awọn iṣẹ ṣiṣe ti o ni iwọn eka pẹlu awọn ibeere giga. Abajade microstructure jẹ bainite kekere (B).
6.Awọn okunfa ti o ni ipa Hardenability
Ipele ti lile da lori iduroṣinṣin ti supercooled austenite ni irin. Ti o ga ni iduroṣinṣin ti supercooled austenite, ti o dara julọ lile lile, ati ni idakeji.
Awọn Okunfa ti o ni ipa Iduroṣinṣin ti Supercooled Austenite:
Ipo ti C-Curve: Ti C-curve ba yipada si apa ọtun, oṣuwọn itutu agbaiye ti o ṣe pataki fun piparẹ dinku, imudara hardenability.
Ipari bọtini:
Eyikeyi ifosiwewe ti o iṣinipo awọn C-tẹ si ọtun mu ki awọn irin ká hardenability.
Okunfa akọkọ:
Tiwqn Kemikali: Ayafi fun koluboti (Co), gbogbo awọn eroja alloying ni tituka ni austenite ilosoke hardenability.
Isunmọ akoonu erogba jẹ si akojọpọ eutectoid ninu irin erogba, diẹ sii ni C-curve ti n yipada si apa ọtun, ati pe o ga ni lile.
7.Determination ati Asoju ti Hardenability
① Ipari Quench Hardenability Test: Hardenability jẹ iwọn lilo ọna idanwo ipari-pa.
② Ọna Diamita Quench Critical: Iwọn ila opin ti o ṣe pataki (D₀) duro fun iwọn ila opin ti o pọju ti irin ti o le ni lile ni kikun ni alabọde piparẹ kan pato.
B.Tmpering
1. Definition ti Tempering
Iwọn otutu jẹ ilana itọju ooru nibiti irin ti o ti pa ti tun gbona si iwọn otutu ni isalẹ aaye A₁, ti o waye ni iwọn otutu yẹn, ati lẹhinna tutu si iwọn otutu yara.
2. Idi ti Tempering
Din tabi Imukuro Wahala Ikuku: Ṣe idilọwọ abuku tabi fifọ ti iṣẹ-ṣiṣe.
Din tabi Imukuro Austenite iyokù: Ṣe iduroṣinṣin awọn iwọn ti iṣẹ-ṣiṣe.
Imukuro Brittleness ti Irin Quenched: Ṣe atunṣe microstructure ati awọn ohun-ini lati pade awọn ibeere iṣẹ iṣẹ.
Akiyesi pataki: Irin yẹ ki o wa ni tutu ni kiakia lẹhin ti o pa.
3.Tempering Awọn ilana
1.Low Tempering
Idi: Lati dinku aapọn piparẹ, mu toughness ti awọn workpiece, ki o si se aseyori ga líle ati wọ resistance.
Iwọn otutu: 150°C ~ 250°C.
Išẹ: Lile: HRC 58 ~ 64. Giga lile ati ki o wọ resistance.
Awọn ohun elo: Awọn irin-iṣẹ, awọn apẹrẹ, awọn bearings, awọn ẹya ti a fi silẹ, ati awọn ohun elo ti o lagbara.
2.High Tempering
Idi: Lati ṣaṣeyọri lile lile pẹlu agbara to ati lile.
Iwọn otutu: 500°C ~ 600°C.
Iṣe: Lile: HRC 25 ~ 35. Awọn ohun-ini imọ-ẹrọ gbogbogbo ti o dara.
Awọn ohun elo: Awọn ọpa, awọn jia, awọn ọpa asopọ, ati bẹbẹ lọ.
Gbona isọdọtun
Itumọ: Quenching ti o tẹle pẹlu iwọn otutu otutu ni a pe ni isọdọtun gbona, tabi ni irọrun. Irin ti a tọju nipasẹ ilana yii ni iṣẹ gbogbogbo ti o dara julọ ati pe o lo pupọ.
Ⅳ.Itọju Ooru Dada ti Irin
A.Surface Quenching ti Irin
1. Definition ti dada Hardening
Idoju oju jẹ ilana itọju ooru ti a ṣe apẹrẹ lati teramo Layer dada ti iṣẹ-ṣiṣe kan nipa gbigbona ni iyara lati yi Layer dada pada si austenite ati lẹhinna ni iyara itutu rẹ. Ilana yii ni a ṣe laisi iyipada akojọpọ kemikali irin tabi eto ipilẹ ti ohun elo naa.
2. Awọn ohun elo ti a lo fun Imudaniloju Ilẹ-ilẹ ati Itumọ-lile-lẹhin
Awọn ohun elo ti a lo fun Ilile Ilẹ
Awọn ohun elo Aṣoju: Irin erogba alabọde ati irin alloy carbon alabọde.
Itọju-tẹlẹ: Ilana Aṣoju: Itoju. Ti awọn ohun-ini mojuto ko ba ṣe pataki, deede le ṣee lo dipo.
Ranse si-lile Be
Igbekale Dada: Layer dada ni igbagbogbo ṣe agbekalẹ igbekalẹ lile gẹgẹbi martensite tabi bainite, eyiti o pese líle giga ati atako wọ.
Ipilẹ Mojuto: Ipilẹ ti irin ni gbogbo igba ṣe idaduro igbekalẹ atilẹba rẹ, gẹgẹbi pearlite tabi ipo ibinu, da lori ilana iṣaaju-itọju ati awọn ohun-ini ti ohun elo ipilẹ. Eyi ṣe idaniloju pe mojuto n ṣetọju lile ati agbara to dara.
B.Awọn abuda ti fifa irọbi dada lile
1.High Heating Temperature ati Rapid Temperature Rise: Induction dada hardening ojo melo ni awọn iwọn otutu alapapo giga ati awọn oṣuwọn alapapo iyara, gbigba fun alapapo iyara laarin igba diẹ.
2.Fine Austenite Grain Structure in the Surface Layer: Nigba ti o yara alapapo ati ọwọ quenching ilana, awọn dada Layer fọọmu itanran austenite oka. Lẹhin quenching, awọn dada akọkọ oriširiši ti itanran martensite, pẹlu líle ojo melo 2-3 HRC ti o ga ju mora quenching.
3.Good Surface Quality: Nitori awọn kukuru alapapo akoko, awọn workpiece dada jẹ kere prone to ifoyina ati decarburization, ati quenching-induced abuku ti wa ni o ti gbe sėgbė, aridaju ti o dara dada didara.
4.High Fatigue Strength: Awọn martensitic alakoso transformation ni dada Layer gbogbo compressive wahala, eyi ti o mu ki awọn rirẹ agbara ti awọn workpiece.
5.High Production Efficiency: Induction dada hardening ni o dara fun ibi-gbóògì, laimu ga operational ṣiṣe.
C.Classification ti kemikali ooru itọju
Carburizing, Carburizing, Carburizing, Chromizing, Siliconizing, Siliconizing, Siliconizing, Carbonitriding, Borocarburizing
D. Gaasi Carburizing
Gaasi Carburizing jẹ ilana kan nibiti a ti gbe iṣẹ kan sinu ileru gaasi ti o ni edidi ati kikan si iwọn otutu ti o yi irin pada si austenite. Lẹhinna, oluranlowo carburizing ti wa ni ṣiṣan sinu ileru, tabi oju-aye carburizing ti wa ni ifihan taara, gbigba awọn ọta erogba lati tan kaakiri sinu Layer dada ti workpiece. Ilana yii ṣe alekun akoonu erogba (wc%) lori dada iṣẹ.
√ Awọn Aṣoju Iwa-ọkọ:
• Awọn gaasi Ọlọrọ Erogba: Iru bii gaasi eedu, gaasi epo olomi (LPG), ati bẹbẹ lọ.
•Organic Liquids: Bii kerosene, methanol, benzene, ati bẹbẹ lọ.
√Ilana Ilana Gbigbe:
• Iwọn otutu ti npa: 920 ~ 950 ° C.
• Akoko gbigbe: Da lori ijinle ti o fẹ ti Layer carburized ati iwọn otutu carburizing.
E.Heat Itoju Lẹhin Carburizing
Irin gbọdọ faragba itọju ooru lẹhin carburizing.
Ilana Itọju Ooru Lẹhin Carburizing:
√Quenching + Iwọn otutu kekere
1.Direct Quenching After Pre-Cooling + Low-Temperature Tempering: Awọn workpiece ti wa ni lai-tutu lati carburizing otutu si o kan loke awọn mojuto ká Ar₁ otutu ati ki o si lẹsẹkẹsẹ quenched, atẹle nipa kekere-otutu tempering ni 160 ~ 180 ° C.
2.Single Quenching After Pre-Cooling + Low-Temperature Tempering: Lẹhin ti carburizing, awọn workpiece ti wa ni laiyara tutu si yara otutu, ki o si reheated fun quenching ati kekere-otutu tempering.
3.Double Quenching Lẹhin Pre-Cooling + Low-Temperature Tempering: Lẹhin ti carburizing ati ki o lọra itutu agbaiye, awọn workpiece undergoes meji ipo ti alapapo ati quenching, atẹle nipa kekere-otutu tempering.
Ⅴ.Kemikali Ooru Itoju ti Irin
1.Definition ti Kemikali Ooru Itọju
Itọju gbigbona kemikali jẹ ilana itọju ooru ninu eyiti a gbe iṣẹ irin kan sinu alabọde kan pato ti nṣiṣe lọwọ, kikan, ati mu ni iwọn otutu, gbigba awọn ọta ti nṣiṣe lọwọ ni alabọde lati tan kaakiri sinu dada ti workpiece. Eyi ṣe ayipada akopọ kemikali ati microstructure ti dada workpiece, nitorinaa yiyipada awọn ohun-ini rẹ pada.
2.Ipilẹ Ilana ti Itọju Kemikali Ooru
Ibajẹ: Lakoko alapapo, alabọde ti nṣiṣe lọwọ decomposes, dasile awọn ọta ti nṣiṣe lọwọ.
Gbigba: Awọn ọta ti nṣiṣe lọwọ ti wa ni adsorbed nipasẹ oju irin ati tu sinu ojutu to lagbara ti irin.
Itankale: Awọn ọta ti nṣiṣe lọwọ ti o gba ati tituka lori dada ti irin yi lọ si inu inu.
Orisi ti Induction Dada Hardening
a.High-Igbohunsafẹfẹ fifa irọbi Alapapo
Igbohunsafẹfẹ lọwọlọwọ: 250 ~ 300 kHz.
Ijinle Layer lile: 0.5 ~ 2.0 mm.
Awọn ohun elo: Alabọde ati awọn jia module kekere ati kekere si awọn ọpa iwọn alabọde.
b.Alabọde-Igbohunsafẹfẹ fifa irọbi Alapapo
Igbohunsafẹfẹ lọwọlọwọ: 2500 ~ 8000 kHz.
Ijinle Layer lile: 2 ~ 10 mm.
Awọn ohun elo: Awọn ọpa ti o tobi ju ati nla si awọn ohun elo module alabọde.
c.Power-Igbohunsafẹfẹ fifa irọbi Alapapo
Igbohunsafẹfẹ lọwọlọwọ: 50 Hz.
Ijinle Layer lile: 10 ~ 15 mm.
Awọn ohun elo: Awọn iṣẹ ṣiṣe to nilo Layer lile ti o jinlẹ pupọ.
3. Fifa irọbi dada Hardening
Ilana Ipilẹ ti Idoju Ilẹ Induction
Ipa Awọ:
Nigbati alternating lọwọlọwọ ninu okun fifa irọbi nfa lọwọlọwọ lori dada ti workpiece, pupọ julọ ti lọwọlọwọ ti o fa wa ni idojukọ nitosi dada, lakoko ti o fẹrẹ jẹ pe ko si lọwọlọwọ ti o kọja nipasẹ inu inu iṣẹ naa. Iyatọ yii ni a mọ ni ipa awọ ara.
Ilana Imudaniloju Ilẹ Ibẹrẹ:
Da lori ipa awọ ara, dada ti workpiece ti nyara kikan si iwọn otutu austenitizing (dide si 800 ~ 1000 ° C ni iṣẹju-aaya diẹ), lakoko ti inu ilohunsoke ti iṣẹ-iṣẹ naa wa ni aibikita. Awọn workpiece ti wa ni ki o si tutu nipa omi spraying, iyọrisi dada líle.
4.Temper Brittleness
Tempering Brittleness ni Quenched Irin
Ibanujẹ iwọn otutu n tọka si lasan nibiti ipa lile ti irin parun dinku ni pataki nigbati iwọn otutu ni awọn iwọn otutu kan.
First Iru ti tempering Brittleness
Iwọn otutu: 250°C si 350°C.
Awọn abuda: Ti irin ti o pa jẹ iwọn otutu ni iwọn otutu yii, o ṣee ṣe gaan lati ṣe idagbasoke iru bii brittleness yii, eyiti ko le yọkuro.
Solusan: Yago fun iwọn otutu ti o wa ni iwọn otutu yii.
Ni igba akọkọ ti iru ti tempering brittleness ni a tun mo bi kekere-otutu tempering brittleness tabi irreversible tempering brittleness.
Ⅵ.Ìbínú
1.Tempering jẹ ilana itọju ooru ikẹhin ti o tẹle quenching.
Kini idi ti awọn irin ti a parun nilo imunibinu?
Microstructure Lẹhin Quenching: Lẹhin piparẹ, microstructure ti irin ni igbagbogbo ni martensite ati austenite to ku. Mejeji jẹ awọn ipele metastable ati pe yoo yipada labẹ awọn ipo kan.
Awọn ohun-ini ti Martensite:Martensite jẹ ijuwe nipasẹ líle giga ṣugbọn tun brittleness giga (paapaa ni abẹrẹ erogba giga-bii martensite), eyiti ko pade awọn ibeere iṣẹ fun ọpọlọpọ awọn ohun elo.
Awọn abuda ti Iyipada Martensitic: Iyipada si martensite waye ni iyara pupọ. Lẹhin piparẹ, iṣẹ naa ni awọn aapọn inu inu ti o le ja si abuku tabi fifọ.
Ipari: Ohun elo iṣẹ ko le ṣee lo taara lẹhin pipa! Tempering jẹ pataki lati dinku awọn aapọn inu ati ilọsiwaju lile ti iṣẹ iṣẹ, jẹ ki o dara fun lilo.
2.Difference Laarin Hardenability ati Agbara:
Agbara:
Hardenability ntokasi si agbara ti irin lati se aseyori kan awọn ijinle líle (ijinle Layer lile) lẹhin quenching. O da lori akojọpọ irin ati igbekalẹ, ni pataki awọn eroja alloying rẹ ati iru irin. Hardenability jẹ wiwọn ti bii irin ṣe le ṣe lile jakejado sisanra rẹ lakoko ilana piparẹ.
Lile (Agbara Lile):
Lile, tabi agbara lile, n tọka si líle ti o pọju ti o le ṣe aṣeyọri ninu irin lẹhin piparẹ. O ni ipa pupọ nipasẹ akoonu erogba ti irin. Akoonu erogba ti o ga julọ ni gbogbogbo nyorisi líle agbara ti o ga julọ, ṣugbọn eyi le ni opin nipasẹ awọn eroja alloying irin ati imunadoko ilana piparẹ.
3.Hardenability ti Irin
√ Erongba ti Hardenability
Hardenability tọka si agbara irin lati ṣaṣeyọri ijinle kan ti líle martensitic lẹhin piparẹ lati iwọn otutu austenitizing. Ni awọn ọrọ ti o rọrun, o jẹ agbara ti irin lati ṣe agbekalẹ martensite lakoko piparẹ.
Idiwon ti Hardenability
Iwọn líle jẹ itọkasi nipasẹ ijinle ti Layer lile ti a gba labẹ awọn ipo ti o pato lẹhin piparẹ.
Àiya Layer Ijinle: Eyi ni ijinle lati dada ti awọn workpiece si agbegbe ibi ti awọn be ni idaji martensite.
Media Quenching ti o wọpọ:
• Omi
Awọn abuda: Ti ọrọ-aje pẹlu agbara itutu agba to lagbara, ṣugbọn o ni iwọn itutu agbaiye giga nitosi aaye farabale, eyiti o le ja si itutu agbaiye pupọ.
Ohun elo: Ni igbagbogbo lo fun awọn irin erogba.
Omi Iyọ: Ojutu ti iyo tabi alkali ninu omi, eyiti o ni agbara itutu agbaiye ti o ga julọ ni awọn iwọn otutu ti o ga julọ ti a fiwewe si omi, ti o jẹ ki o dara fun awọn irin erogba.
• Epo
Awọn abuda: Pese iwọn itutu agbaiye ti o lọra ni awọn iwọn otutu kekere (nitosi aaye farabale), eyiti o dinku ifarahan fun abuku ati fifọ, ṣugbọn ni agbara itutu agba ni awọn iwọn otutu giga.
Ohun elo: Dara fun awọn irin alloy.
Awọn oriṣi: Pẹlu epo ti npa, epo ẹrọ, ati epo diesel.
Alapapo Time
Akoko alapapo ni awọn oṣuwọn alapapo mejeeji (akoko ti o gba lati de iwọn otutu ti o fẹ) ati akoko idaduro (akoko ti a tọju ni iwọn otutu ibi-afẹde).
Awọn ilana fun Ipinnu Akoko Alapapo: Rii daju pinpin iwọn otutu aṣọ ile jakejado iṣẹ ṣiṣe, mejeeji inu ati ita.
Rii daju pe austenitization pipe ati pe austenite ti o ṣẹda jẹ aṣọ ati itanran.
Ipilẹ fun Ipinnu Akoko Alapapo: Nigbagbogbo ifoju ni lilo awọn agbekalẹ ti o ni agbara tabi pinnu nipasẹ idanwo.
Quenching Media
Awọn ẹya pataki meji:
a.Cooling Rate: Iwọn itutu agbaiye ti o ga julọ ṣe igbega dida martensite.
b.Residual Wahala: Iwọn itutu agbaiye ti o ga julọ nmu aapọn aloku pọ si, eyiti o le ja si ifarahan nla fun abuku ati fifọ ni iṣẹ-ṣiṣe.
Ⅶ.Normalizing
1. Definition ti Normalizing
Normalizing jẹ ilana itọju ooru ninu eyiti irin jẹ kikan si iwọn otutu 30 ° C si 50 ° C loke iwọn otutu Ac3, ti o waye ni iwọn otutu yẹn, ati lẹhinna tutu-tutu lati gba microstructure kan ti o sunmọ ipo iwọntunwọnsi. Akawe si annealing, normalizing ni a yiyara itutu oṣuwọn, Abajade ni a finer pearlite be (P) ati ki o ga agbara ati líle.
2. Idi ti Normalizing
Awọn idi ti normalizing jẹ iru si ti annealing.
3. Awọn ohun elo ti Normalizing
• Imukuro cementite Atẹle nẹtiwọki.
• Sin bi itọju ooru ikẹhin fun awọn ẹya pẹlu awọn ibeere kekere.
• Ṣiṣe bi itọju ooru igbaradi fun kekere ati alabọde erogba igbekale irin lati mu ilọsiwaju ṣiṣẹ.
4.Orisi ti Annealing
Oriṣi Annealing akọkọ:
Idi ati Iṣẹ: Ibi-afẹde kii ṣe lati fa iyipada alakoso ṣugbọn lati yipada irin lati ipo aitunwọnsi si ipo iwọntunwọnsi.
Awọn oriṣi:
• Diffusion Annealing: Ni ero lati homogenize awọn tiwqn nipa yiyo ipinya.
• Recrystallization Annealing: Mu pada ductility nipa imukuro awọn ipa ti iṣẹ lile.
• Annealing Relief Annealing: Din awọn aapọn inu lai yi ohun elo microstructure pada.
Irisi Annealing Keji:
Idi ati Iṣẹ: Ni ero lati yi microstructure ati awọn ohun-ini pada, ṣiṣe aṣeyọri microstructure ti o jẹ gaba lori pearlite. Iru yii tun ṣe idaniloju pe pinpin ati morphology ti pearlite, ferrite, ati carbides pade awọn ibeere pataki.
Awọn oriṣi:
• Annealing ni kikun: Ooru irin loke iwọn otutu Ac3 ati lẹhinna rọra rọra lati ṣe agbejade eto pearlite aṣọ kan.
• Annealing ti ko pe: Ooru irin laarin Ac1 ati awọn iwọn otutu Ac3 lati yi eto pada ni apakan.
• Isothermal Annealing: Gbona irin si oke Ac3, atẹle nipa itutu agbaiye iyara si iwọn otutu isothermal ati didimu lati ṣaṣeyọri eto ti o fẹ.
• Spheroidizing Annealing: Ṣe agbejade igbekalẹ carbide spheroidal, imudara ẹrọ ati lile.
Ⅷ.1.Itumọ Itọju Ooru
Itọju igbona tọka si ilana kan ninu eyiti irin ti wa ni kikan, ti o waye ni iwọn otutu kan pato, ati lẹhinna tutu lakoko ti o wa ni ipo to lagbara lati paarọ eto inu inu ati microstructure, nitorinaa iyọrisi awọn ohun-ini ti o fẹ.
2.Awọn abuda ti Itọju Ooru
Ooru itọju ko ni yi awọn apẹrẹ ti awọn workpiece; dipo, o alters awọn ti abẹnu be ati microstructure ti awọn irin, eyi ti o ni Tan yi awọn irin ká ini.
3.Purpose of Heat Treatment
Idi ti itọju ooru ni lati mu ilọsiwaju ẹrọ tabi awọn ohun-ini sisẹ ti irin (tabi awọn ohun elo iṣẹ), lo agbara ti irin ni kikun, mu didara iṣẹ iṣẹ pọ si, ati fa igbesi aye iṣẹ rẹ pọ si.
4.Key Ipari
Boya awọn ohun-ini ohun elo le ni ilọsiwaju nipasẹ itọju igbona da lori pataki lori boya awọn ayipada wa ninu microstructure ati igbekalẹ lakoko ilana alapapo ati itutu agbaiye.