303 zanglamaydigan po'latdan yasalgan tekis bar
Qisqacha tavsif:
Sakysteel buZanglamaydigan tekis barXitoyda ishlab chiqaruvchi va etkazib beruvchilar, 303 zanglamaydigan po'latdan yasalgan tekis barni tadqiq qilish, ishlab chiqish va ishlab chiqarishga ixtisoslashgan.
| C% | Si% | Mn% | P% | S% | Cr% | Ni% | N% | Mo% | Ti% |
| <0,15 | <1,0 | <2,0 | <0,20 | <0,15 | 17,0-19,0 | 8,0-10,0 | - | - | - |
| 303 zanglamaydigan po'latdan yasalgan tekis barning texnik xususiyatlari: |
| Standart | ASTM A276, A484, A479, A580, A582, JIS G4303, JIS G4311, DIN 1654-5, DIN 17440, KS D3706, GB/T 1220 |
| Material | 201,202,205, XM-19 va boshqalar. 301,303,304,304L, 304H, 309S, 310S, 314,316,316L, 316Ti, 317,321,321H, 329,330,348 va boshqalar. 409,410,416,420,430,430F,431,440 2205,2507,S31803,2209,630,631,15-5PH,17-4PH,17-7PH,904L,F51,F55,253MA va boshqalar. |
| Yuzaki | Tuzlangan, tozalangan, qora, qum portlashi, yorqin, tegirmon, oyna, soch chizig'i va boshqalar |
| Texnologiya | Issiq haddelenmiş, payvandlangan, egilgan |
| Texnik xususiyatlari | 20 * 3 mm -100 * 10 mm yoki kerak bo'lganda |
| Tolerantlik | +-2% |
| Sakysteeldan 316 zanglamaydigan po'latdan yasalgan tekis bar mahsulotlari: |
 tuzlangan zanglamaydigan po'latdan yasalgan tekis bar |  Sample_Logo To'g'ri |
| 303 zanglamaydigan po'latdan yasalgan tekis barni qo'llash |
1.Maishiy: vilkalar pichoqlari, lavabolar, kostryulkalar, kir yuvish mashinasining barabanlari, mikroto'lqinli pechlar, ustara pichoqlari
2.Transourt: egzoz tizimlari, avtomobil bezaklari / panjaralari, yo'l tankerlari, kema konteynerlari, kemalar kimyoviy tankerlari
3.Neft va gaz: platformadagi turar joy, kabel yotqizgichlari
4.Tibbiyot: Jarrohlik asboblari, jarrohlik implantlari, MRI skanerlari.
5. Oziq-ovqat va ichimliklar: umumiy ovqatlanish uskunalari, pivo tayyorlash, distillash, oziq-ovqat mahsulotlarini qayta ishlash
6.Suv: Suv va kanalizatsiya tozalash, suv quvurlari, issiq suv idishlari
7.Umumiy: buloqlar, mahkamlagichlar (murvatlar, gaykalar va yuvish vositalari), sim
8.Kimyoviy/farmatsevtika: bosimli idishlar, texnologik quvurlar
9.Arxitektura/qurilish muhandisligi: qoplama, tutqichlar, eshik va deraza armaturalari, ko'cha mebellari, konstruktiv, uchastkalar, armatura panjaralari, yoritish ustunlari, lintellar, devor tayanchlari
| Zanglamaydigan po'latdan yasalgan tekis barning kimyoviy tarkibi: |
| Ostenit Ferrit zanglamaydigan po'lat | 329J1 | 0Cr26Ni5Mo2 | <0,08 | 23.00-28.00 | 3.00-6.00 | <1,50 | <0,035 | <0,030 | 1.00-3.00 | <1,00 | - | 2) |
| 1Cr18Ni11Si4AlTi | 0,10-0,18 | 17.50-19.50 | 10.–120.. | <0,80 | <0,035 | <0,030 | - | 3.40-4.00 | - | Al 0,10-0,30; Ti 0,40-0,70 | ||
| 00Cr18Ni5MoSi2 | <0,030 | 18.00-19.50 | 4.50-5.50 | 1.00-2.00 | <0,035 | <0,030 | 2.50-3.00 | 1.30-2.00 | - | - | ||
| Ferrit zanglamaydigan po'lat | 405 | 0Cr13Al | <0,08 | 11.50-14.50 | 3) | <1,00 | <0,035 | <0,030 | - | <1,00 | - | Al 0,10-0,30 |
| 410 l | 00Cr12 | <0,030 | 11.00-13.00 | 3) | <1,00 | <0,035 | <0,030 | - | <1,00 | - | - | |
| 430 | 1Cr17 | <0,12 | 16.00-18.00 | 3) | <1,25 | <0,035 | <0,030 | - | <0,75 | - | - | |
| 430F | Y1Cr17 | <0,12 | 16.00-18.00 | 3) | <1,00 | <0,035 | <0,15 | 1) | <1,00 | - | - | |
| 434 | 1Cr17Mo | <0,12 | 16.00-18.00 | 3) | <1,00 | <0,035 | <0,030 | 0,75-1,25 | <1,00 | - | - | |
| 447J1 | 00Cr30Mo2 | <0,010 | 28.50-32.00 | - | <0,40 | <0,035 | <0,030 | 1,50-2,50 | <0,40 | <0,015 | - | |
| XM27 | 00Cr27Mo | <0,010 | 25.00-27.50 | - | <0,40 | <0,035 | <0,030 | 0,75-1,50 | <0,40 | <0,015 | - |
| Martensit zanglamaydigan po'lat | 403 | 1Cr12 | <0,15 | 11.50-13.00 | 3) | <1,00 | <0,035 | <0,030 | - | <0,50 | - | - |
| 410 | 1Cr13 | <0,15 | 11.50-13.50 | 3) | <1,00 | <0,035 | <0,030 | - | <1,00 | - | - | |
| 405 | 0Cr13 | <0,08 | 11.50-13.50 | 3) | <1,00 | <0,035 | <0,030 | - | <1,00 | - | - | |
| 416 | Y1Cr13 | <0,15 | 12.00-14.00 | 3) | <1,25 | <0,035 | <0,15 | 1) | <1,00 | - | - | |
| 410J1 | 1Cr13Mo | <0,08-0,18 | 11.50-14.00 | 3) | <1,00 | <0,035 | <0,030 | 0,30-0,60 | <0,60 | - | - | |
| 420J1 | 2Cr13 | 0,16-0,25 | 12.00-14.00 | 3) | <1,00 | <0,035 | <0,030 | - | <1,00 | - | - | |
| 420J2 | 3Cr13 | 0,26-0,35 | 12.00-14.00 | 3) | <1,00 | <0,035 | <0,030 | - | <1,00 | - | - | |
| 420F | Y3Cr13 | 0,26-0,40 | 12.00-14.00 | 3) | <1,25 | <0,035 | <0,15 | 1) | <1,00 | - | - | |
| 3Cr13Mo | 0,28-0,35 | 12.00-14.00 | 3) | <1,00 | <0,035 | <0,030 | 0,50-1,00 | <0,80 | - | - | ||
| 4Cr13 | 0,36-0,45 | 12.00-14.00 |