430 karatasi ya chuma cha puaMuundo wa Kemikali na Sifa za Mitambo: |
C% | Si% | Mn% | P% | S% | Cr% | Ni% | N% | Mo% | Ti% |
0.12 | 1.00 | 1.00 | 0.040 | 0.030 | 16.0-18.0 | 0.75 | - | - | - |
T*S | Y*S | Ugumu | Kurefusha |
(Mpa) | (Mpa) | HRB | HB | (%) |
520 | 205 | - | - | 40 |
Baridi Iliyoviringishwa430 karatasi ya chuma cha pua: |
1. Daraja: 200 & 300 mfululizo
200 mfululizo: 201,202, J4
mfululizo 300: 301, 304, 304L, 321, 316L, 309, 310S
2. Kawaida: JIS, ASTM, AISI, GB, DIN, EN, kwa kawaida tunatumia ASTM na GB Standard
3. Unene: 0.14mm-3.0mm
4. Upana: inavyohitajika
5. Uso: 2B imekamilika, BA imekamilika
6. Ugumu: laini, 1/4H, 1/2H, FH
7. Uvumilivu wa Unene: +/-0.02mm
8. Uvumilivu wa Upana: +/-10mm(makali ya kinu)
Alama zaidi za karatasi 430 ss: |
Aina | Daraja | Daraja | Kipengele cha Kemikali |
Austenitic chuma cha pua | | | C | Cr | Ni | Mn |
201 | 1Cr17Mn6Ni5N | 0.15 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 |
201L | 03Cr17Mn6Ni5N | 0.030 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 |
202 | 1Cr18Mn8Ni5N | 0.15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 |
204 | 03Cr16Mn8Ni2N | 0.030 | 15.00-17.00 | 1.50-3.50 | 7.00-9.00 |
| 1Cr18Mn10Ni5Mo3N | 0.10 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 |
| 2Cr13Mn9Ni4 | 0.15-0.25 | 12.00-14.00 | 3.70-5.00 | 8.00-10.00 |
| 2Cr15Mn15Ni2N | 0.15-0.25 | 14.00-16.00 | 1.50-3.00 | 14.00-16.00 |
| 1Cr18Mn10Ni5Mo3N | 0.15 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 |
301 | 1Cr17Ni7 | 0.15 | 16.00-18.00 | 6.00-8.00 | 2.00 |
302 | 1Cr18Ni9 | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 |
303 | Y1Cr18Ni9 | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 |
Sekunde 303 | Y1Cr18Ni9Se | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 |
304 | 0Cr18Ni9 | 0.07 | 17.00-19.00 | 8.00-10.00 | 2.00 |
304L | 00Cr19Ni10 | 0.030 | 18.00-20.00 | 8.00-10.00 | 2.00 |
304N1 | 0Cr19Ni9N | 0.08 | 18.00-20.00 | 7.00-10.50 | 2.00 |
304N2 | 0Cr18Ni10NbN | 0.08 | 18.00-20.00 | 7.50-10.50 | 2.00 |
304LN | 00Cr18Ni10N | 0.030 | 17.00-19.00 | 8.50-11.50 | 2.00 |
305 | 1Cr18Ni12 | 0.12 | 17.00-19.00 | 10.50-13.00 | 2.00 |
309S | 0Cr23Ni13 | 0.08 | 22.00-24.00 | 12.00-15.00 | 2.00 |
310S | 0Cr25Ni20 | 0.08 | 24.00-26.00 | 19.00-22.00 | 2.00 |
316 | 0Cr17Ni12Mo2 | 0.08 | 16.00-18.50 | 10.00-14.00 | 2.00 |
| 1Cr18Ni12Mo2Ti6) | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 |
| 0Cr18Ni12Mo2Ti | 0.08 | 16.00-19.00 | 11.00-14.00 | 2.00 |
316L | 00Cr17Ni14Mo2 | 0.030 | 16.00-18.00 | 12.00-15.00 | 2.00 |
316N | 0Cr17Ni12Mo2N | 0.08 | 16.00-18.00 | 10.00-14.00 | 2.00 |
316N | 00Cr17Ni13Mo2N | 0.030 | 16.00-18.50 | 10.50-14.50 | 2.00 |
316J1 | 0Cr18Ni12Mo2Cu2 | 0.08 | 17.00-19.00 | 10.00-14.50 | 2.00 |
316J1L | 00Cr18Ni14Mo2Cu2 | 0.030 | 17.00-19.00 | 12.00-16.00 | 2.00 |
317 | 0Cr19Ni13Mo3 | 0.12 | 18.00-20.00 | 11.00-15.00 | 2.00 |
317L | 00Cr19Ni13Mo3 | 0.08 | 18.00-20.00 | 11.00-15.00 | 2.00 |
| 1Cr18Ni12Mo3Ti6 | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 |
| 0Cr18Ni12Mo3Ti | 0.08 | 16.00-19.00 | 11.00-14.00 | 2.00 |
317J1 | 0Cr18Ni16Mo5 | 0.040 | 16.00-19.00 | 15.00-17.00 | 2.00 |
321 | 1Cr18Ni9Ti6 | 0.12 | 17.00-19.00 | 8.00-11.00 | 2.00 |
| 0Cr18Ni10Ti | 0.08 | 17.00-19.00 | 9.00-12.00 | 2.00 |
347 | 0Cr18Ni11Nb | 0.08 | 17.00-19.00 | 9.00-13.00 | 2.00 |
XM7 | 0Cr18Ni9Cu3 | 0.08 | 17.00-19.00 | 8.50-10.50 | 2.00 |
XM15J1 | 0Cr18Ni13Si4 | 0.08 | 15.00-20.00 | 11.50-15.00 | 2.00 |