Tuubbada birta ee birta ah
Sharraxaadda Gaaban:
Faahfaahinta tuubbada birta ee birta ah ee birta la dhalaaliyay: |
1. Wax soo saarka | Birta la jeexjeexay tuubbada |
2. Qalabka | 201,202,301,302,304,309,310S,316L,321,347,410,430,409Letc. |
3. Heerka | ASTM, ASME, DIN, En, ISO, JIS, GOST, iwm. |
4. Cabbirka xajmiga | OD: Laga soo bilaabo 6mm illaa 1219mm (NPS laga bilaabo 1/8 "ilaa 40") |
WT: laga bilaabo 0.7mm ilaa 38mm (Jadwalka 5-yada illaa XXS) | |
Dhererka: hagaajinta dhererka ama dhererka aan hagaajinayn, ugu badnaan 30mitir 30mitir | |
5. Soosaarida geedi socodka | Weelka, leexashada kulul; ka caabitaanka alxanka; ballaarinta kuleylka iwm. |
6. Dusha sare | 2b, 180g, 320g, satin, timaha timaha, 400g, 500g, 600g |
, 800g, muraayad dhamaato | |
7. Calaamadeynta | SAKY, Fasalka, Kala-jajabinta, Heerka, Cabbirka, kuleylka maya. |
8. Xidhmo | Xidhmooyin biyo-aan biyo-bixin ah oo bannaanka ah. |
ama sanduuqa plywood. | |
9. Dhererka | 5.8m, 6m, 12m ama sidii loogu baahnaa |
Hantida farsamada ee caadiga ah ee 304 ekooro bir ah oo bir ah: |
Heer u qaybin | Xoog TSensile (MPA) | Xoogga cadaadiska (MPA) | Cadaadis caddeyn 0.2% (MPA) | Elongation A5 (%) | Adkaanta adag b |
304 | 520-720 | 210 | 210 | 45 daqiiqo | 92 |
304l | 500-670 | 200 | 45 daqiiqo | ||
304h | 520-720 | 210 | 45min |
Darajooyinka birta birta birta ah ee birta ah |
Teeb ku qorid | Heer u qaybin | Heer u qaybin | Qeybta kiimikada% | ||||
Bir bir ah oo aan caadi ahayn | C | Cr | Ni | Mn | |||
201 | 1cr17mn6n6n | 0.15 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | ||
2012 | 03cr17mn6n6n | 0.030 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | ||
202 | 1cr18mn8ni5n | 0.15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | ||
204 | 03cr16mn8ni2n | 0.030 | 15.00-17.00 | 1.50-3.50 | 7.00-9.00 | ||
1cr18mn10ni5mo3n | 0.10 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 | |||
2c13mn9n9 | 0.15-0.25 | 12.00-14.00 | 3.70-5.00 | 8.00-10.00 | |||
2cr15mn15n | 0.15-0.25 | 14.00-16.00 | 1.50-3.00 | 14.00-16.00 | |||
1cr18mn10ni5mo3n | 0.15 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 | |||
301 | 1cr17ni7 | 0.15 | 16.00-18.00 | 6.00-8.00 | 2.00 | ||
302 | 1cr18ni9 | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | ||
303 | Y1cr18ni9 | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | ||
3035s | Y1cr18ni9se | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | ||
304 | 0cr18ni9 | 0.07 | 17.00-19.00 | 8.00-10.00 | 2.00 | ||
304l | 00cr19nni10 | 0.030 | 18.00-20.00 | 8.00-10.00 | 2.00 | ||
304N1 | 0cr19ni9n | 0.08 | 18.00-20.00 | 7.00-10.50 | 2.00 | ||
304n2 | 0cr18ni10nbn | 0.08 | 18.00-20.00 | 7.50-10.50 | 2.00 | ||
304ln | 00cr18ni10n | 0.030 | 17.00-19.00 | 8.50-11.50 | 2.00 | ||
305 | 1cr18ni12 | 0.12 | 17.00-19.00 | 10.50-13.00 | 2.00 | ||
309s | 0cr23ni13 | 0.08 | 22.00-24.00 | 12.00-15.00 | 2.00 | ||
310s | 0cr25nI20 | 0.08 | 24.00-26.00 | 19.00-22.00 | 2.00 | ||
316 | 0cr17ni12mo2 | 0.08 | 16.00-18.50 | 10.00-14.00 | 2.00 | ||
1cr18ni12mo2Ti6) | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 | |||
0cr18ni12mo2Ti | 0.08 | 16.00-19.00 | 11.00-14.00 | 2.00 | |||
316l | 00cr17ni14mo2 | 0.030 | 16.00-18.00 | 12.00-15.00 | 2.00 | ||
316n | 0cr17ni12mo2n | 0.08 | 16.00-18.00 | 10.00-14.00 | 2.00 | ||
316n | 00cr17ni13mo2n | 0.030 | 16.00-18.50 | 10.50-14.50 | 2.00 | ||
316J1 | 0cr18ni12mo2Cu2 | 0.08 | 17.00-19.00 | 10.00-14.50 | 2.00 | ||
316j1l | 00cr18ni14mo2Cu2 | 0.030 | 17.00-19.00 | 12.00-16.00 | 2.00 | ||
317 | 0cr19ni13mo3 | 0.12 | 18.00-20.00 | 11.00-15.00 | 2.00 | ||
317l | 00cr19ni13mo3 | 0.08 | 18.00-20.00 | 11.00-15.00 | 2.00 | ||
1cr18ni12mo3Ti6 | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 | |||
0cr18ni12mo3Ti | 0.08 | 16.00-19.00 | 11.00-14.00 | 2.00 | |||
317J1 | 0cr18ni16mo5 | 0.040 | 16.00-19.00 | 15.00-17.00 | 2.00 | ||
321 | 1cr18ni9ti6 | 0.12 | 17.00-19.00 | 8.00-11.00 | 2.00 | ||
0cr18ni10ti | 0.08 | 17.00-19.00 | 9.00-12.00 | 2.00 | |||
347 | 0cr18ni11Nb | 0.08 | 17.00-19.00 | 9.00-13.00 | 2.00 | ||
Xm7 | 0cr18ni9Cu3 | 0.08 | 17.00-19.00 | 8.50-10.50 | 2.00 | ||
XM15J1 | 0cr18ni13si4 | 0.08 | 15.00-20.00 | 11.50-15.00 | 2.00 |
Austite Ferrite bir aan lahayn | 329J1 | 0cr26ni5mo2 | 0.08 | 23.00-28.00 | 3.00-6.00 | 1.50 | 0.035 | 0.030 | 1.00-3.00 | 1.00 | - | - | 2) |
1cr18ni11si4lti | 0.10-0.18 | 17.50-19.50 | 10.-120 .. | 0.80 | 0.035 | 0.030 | - | 3.40-4.00 | - | - | Al 0.10-0.30; Ti 0.40-0.70 | ||
00cr18ni5mosi2 | 0.030 | 18.00-19.50 | 4.50-5.50 | 1.00-2.00 | 0.035 | 0.030 | 2.50-3.00 | 1.30-2.00 | - | - | - | ||
Ferrite bir aan lahayn | 405 | 0cr13l | 0.08 | 11.50-14.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | Al 0.10-0.30 |
410l | 00cr12 | 0.030 | 11.00-13.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
430 | 1cr17 | 0.12 | 16.00-18.00 | 3) | 1.25 | 0.035 | 0.030 | - | 0.75 | - | - | - | |
430f | Y1cr17 | 0.12 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
434 | 1cr17mo | 0.12 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.030 | 0.75-1.25 | 1.00 | - | - | - | |
447J1 | 00cr30mo2 | 0.010 | 28.50-32.00 | - | 0.40 | 0.035 | 0.030 | 1.50-2.50 | 0.40 | - | 0.015 | - | |
Xm27 | 00cr27mo | 0.010 | 25.00-27.50 | - | 0.40 | 0.035 | 0.030 | 0.75-1.50 | 0.40 | - | 0.015 | - |
Martensite steel aan sal lahayn | 403 | 1c12 | 0.15 | 11.50-13.00 | 3) | 1.00 | 0.035 | 0.030 | - | 0.50 | - | - | - |
410 | 1cr13 | 0.15 | 11.50-13.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
405 | 0cr13 | 0.08 | 11.50-13.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
416 | Y1cr13 | 0.15 | 12.00-14.00 | 3) | 1.25 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
410J1 | 1cr13mo | 0.08-0.18 | 11.50-14.00 | 3) | 1.00 | 0.035 | 0.030 | 0.30-0.60 | 0.60 | - | - | - | |
420J1 | 2cr13 | 0.16-0.25 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
420J2 | 3cr13 | 0.26-0.35 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
420f | Y3cr13 | 0.26-0.40 | 12.00-14.00 | 3) | 1.25 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
3cr13mo | 0.28-0.35 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | 0.50-1.00 | 0.80 | - | - | - | ||
4cr13 | 0.36-0.45 | 12.00-14.00 | 3) | 0.80 | 0.035 | 0.030 | - | 0.60 | - | - | - | ||
431 | 1cr17ni2 | 0.11-0.17 | 16.00-18.00 | 1.50-2.50 | 0.80 | 0.035 | 0.030 | - | 0.80 | - | - | - | |
440A | 7cr17 | 0.60-0.75 | 16.00-18.00 | 3) | 1.00 | 0.035 |