Pajp tal-istainless steel illustrat
Deskrizzjoni qasira:
| Speċifikazzjonijiet tal-pajp tal-istainless steel illustrat: |
| 1. Prodott | Pajp iwweldjat tal-azzar li ma jsaddadx |
| 2. Materjal | 201,202.301.302,304,309,310s, 316L, 321.347.410,430,409LETC. |
| 3. Standard | ASTM, ASME, DIN, EN, ISO, JIS, GOST, ETC. |
| 4. Firxa tad-daqs | OD: minn 6mm sa 1219mm (NPs minn 1/8 "sa 40") |
| WT: Minn 0.7mm sa 38mm (skeda minn 5s sa xxs) | |
| Tul: Waħħal it-tul jew it-tul mhux fiss, massimu 30metri | |
| 5. Ipproduċi proċess | iwweldjat, liwi sħun; iwweldjar tar-reżistenza; espansjoni termali eċċ. |
| 6. wiċċ | 2b, imnaddfin, 180g, 320g, satin, linja tax-xagħar, 400g, 500g, 600g |
| , 800g, finitura mera | |
| 7. Immarkar | Saky, grad, bla xkiel, standard, daqs, sħana nru. |
| 8. Pakkett | Qatet b'ċarruta li ma jgħaddix ilma minn barra. |
| jew kaxxa tal-plajwud. | |
| 9. Tul | 5.8m, 6m, 12m jew kif meħtieġ |
| Propjetajiet mekkaniċi tipiċi għal 304 ligi tal-istainless steel: |
| Grad | Qawwa tat-tensjoni (MPA) | Qawwa tal-Kompressjoni (MPA) | Stress tal-Prova 0.2% (MPA) | Titwil A5 (%) | Ebusija rockwell b |
| 304 | 520-720 | 210 | 210 | 45 min | 92 |
| 304L | 500-670 | 200 | 45 min | ||
| 304h | 520-720 | 210 | 45min |
| Gradi ta 'pajp tal-istainless steel illustrat: |
| Tip | Grad | Grad | Komponent Kimiku% | ||||
| L-istainless steel awstenitiku | C | Cr | Ni | Mn | |||
| 201 | 1Cr17Mn6ni5n | 0.15 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | ||
| 201L | 03CR17MN6NI5N | 0.030 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | ||
| 202 | 1CR18Mn8NI5N | 0.15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | ||
| 204 | 03CR16Mn8NI2N | 0.030 | 15.00-17.00 | 1.50-3.50 | 7.00-9.00 | ||
| 1CR18MN10NI5MO3N | 0.10 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 | |||
| 2CR13MN9NI4 | 0.15-0.25 | 12.00-14.00 | 3.70-5.00 | 8.00-10.00 | |||
| 2CR15MN15NI2N | 0.15-0.25 | 14.00-16.00 | 1.50-3.00 | 14.00-16.00 | |||
| 1CR18MN10NI5MO3N | 0.15 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 | |||
| 301 | 1Cr17ni7 | 0.15 | 16.00-18.00 | 6.00-8.00 | 2.00 | ||
| 302 | 1CR18NI9 | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | ||
| 303 | Y1CR18NI9 | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | ||
| 303SE | Y1CR18NI9SE | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | ||
| 304 | 0CR18NI9 | 0.07 | 17.00-19.00 | 8.00-10.00 | 2.00 | ||
| 304L | 00CR19NI10 | 0.030 | 18.00-20.00 | 8.00-10.00 | 2.00 | ||
| 304n1 | 0CR19NI9N | 0.08 | 18.00-20.00 | 7.00-10.50 | 2.00 | ||
| 304n2 | 0CR18NI10NBN | 0.08 | 18.00-20.00 | 7.50-10.50 | 2.00 | ||
| 304ln | 00CR18NI10N | 0.030 | 17.00-19.00 | 8.50-11.50 | 2.00 | ||
| 305 | 1CR18NI12 | 0.12 | 17.00-19.00 | 10.50-13.00 | 2.00 | ||
| 309s | 0CR23NI13 | 0.08 | 22.00-24.00 | 12.00-15.00 | 2.00 | ||
| 310s | 0CR25NI20 | 0.08 | 24.00-26.00 | 19.00-22.00 | 2.00 | ||
| 316 | 0CR17NI12MO2 | 0.08 | 16.00-18.50 | 10.00-14.00 | 2.00 | ||
| 1CR18NI12MO2TI6) | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 | |||
| 0CR18NI12MO2ti | 0.08 | 16.00-19.00 | 11.00-14.00 | 2.00 | |||
| 316L | 00CR17NI14MO2 | 0.030 | 16.00-18.00 | 12.00-15.00 | 2.00 | ||
| 316n | 0CR17NI12MO2N | 0.08 | 16.00-18.00 | 10.00-14.00 | 2.00 | ||
| 316n | 00CR17NI13MO2N | 0.030 | 16.00-18.50 | 10.50-14.50 | 2.00 | ||
| 316J1 | 0CR18NI12MO2CU2 | 0.08 | 17.00-19.00 | 10.00-14.50 | 2.00 | ||
| 316J1L | 00CR18NI14MO2CU2 | 0.030 | 17.00-19.00 | 12.00-16.00 | 2.00 | ||
| 317 | 0CR19NI13MO3 | 0.12 | 18.00-20.00 | 11.00-15.00 | 2.00 | ||
| 317L | 00CR19NI13MO3 | 0.08 | 18.00-20.00 | 11.00-15.00 | 2.00 | ||
| 1CR18NI12MO3TI6 | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 | |||
| 0CR18NI12MO3ti | 0.08 | 16.00-19.00 | 11.00-14.00 | 2.00 | |||
| 317J1 | 0CR18NI16MO5 | 0.040 | 16.00-19.00 | 15.00-17.00 | 2.00 | ||
| 321 | 1CR18NI9TI6 | 0.12 | 17.00-19.00 | 8.00-11.00 | 2.00 | ||
| 0CR18NI10TI | 0.08 | 17.00-19.00 | 9.00-12.00 | 2.00 | |||
| 347 | 0CR18NI11NB | 0.08 | 17.00-19.00 | 9.00-13.00 | 2.00 | ||
| Xm7 | 0CR18NI9CU3 | 0.08 | 17.00-19.00 | 8.50-10.50 | 2.00 | ||
| XM15J1 | 0CR18NI13SI4 | 0.08 | 15.00-20.00 | 11.50-15.00 | 2.00 | ||
| Austenite Ferrite Stainless Steel | 329J1 | 0CR26NI5MO2 | 0.08 | 23.00-28.00 | 3.00-6.00 | 1.50 | 0.035 | 0.030 | 1.00-3.00 | 1.00 | - | - | 2) |
| 1CR18NI11SI4ALTI | 0.10-0.18 | 17.50-19.50 | 10.–120 .. | 0.80 | 0.035 | 0.030 | - | 3.40-4.00 | - | - | Al 0.10-0.30; Ti 0.40-0.70 | ||
| 00CR18NI5MOSI2 | 0.030 | 18.00-19.50 | 4.50-5.50 | 1.00-2.00 | 0.035 | 0.030 | 2.50-3.00 | 1.30-2.00 | - | - | - | ||
| Ferrite Stainless Steel | 405 | 0Cr13al | 0.08 | 11.50-14.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | AL 0.10-0.30 |
| 410L | 00CR12 | 0.030 | 11.00-13.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
| 430 | 1Cr17 | 0.12 | 16.00-18.00 | 3) | 1.25 | 0.035 | 0.030 | - | 0.75 | - | - | - | |
| 430f | Y1CR17 | 0.12 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
| 434 | 1Cr17mo | 0.12 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.030 | 0.75-1.25 | 1.00 | - | - | - | |
| 447J1 | 00CR30MO2 | 0.010 | 28.50-32.00 | - | 0.40 | 0.035 | 0.030 | 1.50-2.50 | 0.40 | - | 0.015 | - | |
| Xm27 | 00cr27mo | 0.010 | 25.00-27.50 | - | 0.40 | 0.035 | 0.030 | 0.75-1.50 | 0.40 | - | 0.015 | - |
| Martensite Stainless Steel | 403 | 1Cr12 | 0.15 | 11.50-13.00 | 3) | 1.00 | 0.035 | 0.030 | - | 0.50 | - | - | - |
| 410 | 1Cr13 | 0.15 | 11.50-13.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
| 405 | 0CR13 | 0.08 | 11.50-13.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
| 416 | Y1CR13 | 0.15 | 12.00-14.00 | 3) | 1.25 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
| 410J1 | 1Cr13mo | 0.08-0.18 | 11.50-14.00 | 3) | 1.00 | 0.035 | 0.030 | 0.30-0.60 | 0.60 | - | - | - | |
| 420J1 | 2CR13 | 0.16-0.25 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
| 420J2 | 3CR13 | 0.26-0.35 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
| 420f | Y3CR13 | 0.26-0.40 | 12.00-14.00 | 3) | 1.25 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
| 3CR13MO | 0.28-0.35 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | 0.50-1.00 | 0.80 | - | - | - | ||
| 4CR13 | 0.36-0.45 | 12.00-14.00 | 3) | 0.80 | 0.035 | 0.030 | - | 0.60 | - | - | - | ||
| 431 | 1CR17NI2 | 0.11-0.17 | 16.00-18.00 | 1.50-2.50 | 0.80 | 0.035 | 0.030 | - | 0.80 | - | - | - | |
| 440a | 7CR17 | 0.60-0.75 | 16.00-18.00 | 3) | 1.00 | 0.035 |