Penerangan ringkas:
Bar keluli tahan karat, bahagian T atau profil tee dengan gred 201,303,304,304L, 316,316L, 316ti, 321,310s, 410,430
SpesifikasiBar keluli tahan karat T: |
Standard | ASTM A276, A484, A479, A580, A582, JIS G4303, JIS G4311, DIN 1654-5, DIN 17440, KS D3706, GB/T 1220 |
Bahan | 201,202,205, XM-19 dll. 301,303,304,304L, 304h, 309s, 310s, 314,316,316L, 316ti, 317,321,321h, 329,330,348 dll. 409,410,416,420,430,430F, 431,440 2205,2507, S31803,2209,630,631,15-5PH, 17-4PH, 17-7PH, 904L, F51, F55,253MA dll. |
Permukaan | Cerah, menggilap, jeruk, dikupas, hitam, pengisaran, kilang, cermin, garis rambut dan lain -lain |
Teknologi | Dingin ditarik, panas digulung, dipalsukan |
Spesifikasi | seperti yang diperlukan |
Toleransi | H9, H11, H13, K9, K11, K13 atau seperti yang diperlukan |
Produk Bahagian T Stainless Steel dari Sakysteel: |
BeratBar keluli tahan karat |
Model | Berat | Model | Berat |
100*50*5*7 | 9.54 | 344*354*16*16 | 131 |
100*100*6*8 | 17.2 | 346*174*6*9 | 41.8 |
125*60*6*8 | 13.3 | 350*175*7*11 | 50 |
125*125*6.5*9 | 23.8 | 344*348*10*16 | 115 |
148*100*6*9 | 21.4 | 350*350*12*19 | 137 |
150*75*5*7 | 14.3 | 388*402*15*15 | 141 |
150*150*7*10 | 31.9 | 390*300*10*16 | 107 |
175*90*5*8 | 18.2 | 394*398*11*18 | 147 |
175*175*7.5*11 | 40.3 | 400*150*8*13 | 55.8 |
194*150*6*9 | 31.2 | 396*199*7*11 | 56.7 |
198*99*4.5*7 | 18.5 | 400*200*8*13 | 66 |
200*100*5.5*8 | 21.7 | 400*400*13*21 | 172 |
200*200*8*12 | 50.5 | 400*408*21*21 | 197 |
200*204*12*12 | 72.28 | 414*405*18*28 | 233 |
244*175*7*11 | 44.1 | 440*300*11*18 | 124 |
244*252*11*11 | 64.4 | 446*199*7*11 | 66.7 |
248*124*5*8 | 25.8 | 450*200*9-14 | 76.5 |
250*125*6*9 | 29.7 | 482*300*11*15 | 115 |
250*250*9*14 | 72.4 | 488*300*11*18 | 129 |
250*255*14*14 | 82.2 | 496*199*9*14 | 79.5 |
294*200*8*12 | 57.3 | 500*200*10*16 | 89.6 |
300*150*6.5*9 | 37.3 | 582*300*12*17 | 137 |
294*302*12*12 | 85 | 588*300*12*20 | 151 |
300*300*10*15 | 94.5 | 596*199*10*15 | 95.1 |
300*305*15*15 | 106 | 600*200*11*17 | 106 |
338*351*13*13 | 106 | 700*300*13*24 | 185 |
340*250*9*14 | 79.7 |
Lebih banyak gredBar keluli tahan karat T: |
Jenis | Gred | Gred | Komponen kimia % | ||||||||||
C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | Yang lain | |||
Keluli tahan karat austenit | 201 | 1cr17mn6ni5n | 0.15 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | 0.060 | 0.030 | - | 1.00 | - | 0.25 | - |
201l | 03cr17mn6ni5n | 0.030 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | 0.060 | 0.030 | 1.00 | 0.25 | ||||
202 | 1cr18mn8ni5n | 0.15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | 0.060 | 0.030 | 1.00 | - | 0.25 | - | ||
204 | 03cr16mn8ni2n | 0.030 | 15.00-17.00 | 1.50-3.50 | 7.00-9.00 | 0.15-0.30 | |||||||
1cr18mn10ni5mo3n | 0.10 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 | 2.80-3.50 | 0.20-0.30 | |||||||
2cr13mn9ni4 | 0.15-0.25 | 12.00-14.00 | 3.70-5.00 | 8.00-10.00 | |||||||||
2cr15mn15ni2n | 0.15-0.25 | 14.00-16.00 | 1.50-3.00 | 14.00-16.00 | 0.15-0.30 | ||||||||
1cr18mn10ni5mo3n | 0.15 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 | 0.060 | 0.030 | 2.8-3.5 | 1.00 | - | 0.20-0.30 | - | ||
301 | 1cr17ni7 | 0.15 | 16.00-18.00 | 6.00-8.00 | 2.00 | 0.065 | 0.030 | - | 1.00 | - | - | - | |
302 | 1cr18ni9 | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
303 | Y1cr18ni9 | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | 0.20 | 0.030 | 1) | 1.00 | - | - | - | |
303se | Y1cr18ni9se | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | 0.20 | 0.030 | - | 1.00 | - | - | SE = 0.15 | |
304 | 0cr18ni9 | 0.07 | 17.00-19.00 | 8.00-10.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
304L | 00CR19NI10 | 0.030 | 18.00-20.00 | 8.00-10.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
304n1 | 0cr19ni9n | 0.08 | 18.00-20.00 | 7.00-10.50 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | 0.10-0.25 | - | |
304n2 | 0cr18ni10nbn | 0.08 | 18.00-20.00 | 7.50-10.50 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | 0.15-0.30 | Nb = 0.15 | |
304ln | 00CR18NI10N | 0.030 | 17.00-19.00 | 8.50-11.50 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | 0.12-0.22 | - | |
305 | 1cr18ni12 | 0.12 | 17.00-19.00 | 10.50-13.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
309s | 0CR23NI13 | 0.08 | 22.00-24.00 | 12.00-15.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
310s | 0CR25NI20 | 0.08 | 24.00-26.00 | 19.00-22.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
316 | 0CR17NI12MO2 | 0.08 | 16.00-18.50 | 10.00-14.00 | 2.00 | 0.035 | 0.030 | 2.00-3.00 | 1.00 | - | - | - | |
1cr18ni12mo2ti6) | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 | 0.035 | 0.030 | 1.80-2.50 | 1.00 | - | - | Ti5 (C%-0.02) ~ 0.08 | ||
0cr18ni12mo2ti | 0.08 | 16.00-19.00 | 11.00-14.00 | 2.00 | 0.035 | 0.030 | 1.80-2.50 | 1.00 | - | - | Ti5*C%-0.70 | ||
316L | 00CR17NI14MO2 | 0.030 | 16.00-18.00 | 12.00-15.00 | 2.00 | 0.035 | 0.030 | 2.00-3.00 | 1.00 | - | - | - | |
316n | 0cr17ni12mo2n | 0.08 | 16.00-18.00 | 10.00-14.00 | 2.00 | 0.035 | 0.030 | 2.00-3.00 | 1.00 | - | 0.10-0.22 | - | |
316n | 00CR17NI13MO2N | 0.030 | 16.00-18.50 | 10.50-14.50 | 2.00 | 0.035 | 0.030 | 2.00-3.00 | 1.00 | - | 0.12-0.22 | - | |
316J1 | 0CR18NI12MO2CU2 | 0.08 | 17.00-19.00 | 10.00-14.50 | 2.00 | 0.035 | 0.030 | 1.20-2.75 | 1.00 | 1.00-2.50 | - | - | |
316J1L | 00CR18NI14MO2CU2 | 0.030 | 17.00-19.00 | 12.00-16.00 | 2.00 | 0.035 | 0.030 | 1.20-2.75 | 1.00 | 1.00-2.50 | - | - | |
317 | 0CR19NI13MO3 | 0.12 | 18.00-20.00 | 11.00-15.00 | 2.00 | 0.035 | 0.030 | 3.00-4.00 | 1.00 | - | - | - | |
317L | 00CR19NI13MO3 | 0.08 | 18.00-20.00 | 11.00-15.00 | 2.00 | 0.035 | 0.030 | 3.00-4.00 | 1.00 | - | - | - | |
1cr18ni12mo3ti6 | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 | 0.035 | 0.030 | 2.50-3.50 | 1.00 | - | - | Ti5 (C%-0.02) ~ 0.08 | ||
0cr18ni12mo3ti | 0.08 | 16.00-19.00 | 11.00-14.00 | 2.00 | 0.035 | 0.030 | 2.50-3.50 | 1.00 | - | - | Ti5*C%-0.70 | ||
317J1 | 0cr18ni16mo5 | 0.040 | 16.00-19.00 | 15.00-17.00 | 2.00 | 0.035 | 0.030 | 4.00-6.00 | 1.00 | - | - | - | |
321 | 1cr18ni9ti6 | 0.12 | 17.00-19.00 | 8.00-11.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | Ti5 (C%-0.02) ~ 0.08 | |
0cr18ni10ti | 0.08 | 17.00-19.00 | 9.00-12.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | Ti = 5*c% | ||
347 | 0cr18ni11nb | 0.08 | 17.00-19.00 | 9.00-13.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | Nb = 10*c% | |
Xm7 | 0cr18ni9cu3 | 0.08 | 17.00-19.00 | 8.50-10.50 | 2.00 | 0.035 | 0.030 | - | 1.00 | 3.00-4.00 | - | - | |
XM15J1 | 0CR18NI13SI4 | 0.08 | 15.00-20.00 | 11.50-15.00 | 2.00 | 0.035 | 0.030 | - | 3.00-5.00 | - | - | 2) | |
Austenite | 329J1 | 0cr26ni5mo2 | 0.08 | 23.00-28.00 | 3.00-6.00 | 1.50 | 0.035 | 0.030 | 1.00-3.00 | 1.00 | - | - | 2) |
| | 1cr18ni11si4alti | 0.10-0.18 | 17.50-19.50 | 10.-120 .. | 0.80 | 0.035 | 0.030 | - | 3.40-4.00 | - | - | AL 0.10-0.30; Ti 0.40-0.70 | |
Keluli tahan karat ferit | 00CR18NI5MOSI2 | 0.030 | 18.00-19.50 | 4.50-5.50 | 1.00-2.00 | 0.035 | 0.030 | 2.50-3.00 | 1.30-2.00 | - | - | - | |
Keluli tahan karat ferit | 405 | 0cr13al | 0.08 | 11.50-14.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | AL 0.10-0.30 |
410L | 00CR12 | 0.030 | 11.00-13.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
430 | 1cr17 | 0.12 | 16.00-18.00 | 3) | 1.25 | 0.035 | 0.030 | - | 0.75 | - | - | - | |
430f | Y1cr17 | 0.12 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
434 | 1cr17mo | 0.12 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.030 | 0.75-1.25 | 1.00 | - | - | - | |
447J1 | 00CR30MO2 | 0.010 | 28.50-32.00 | - | 0.40 | 0.035 | 0.030 | 1.50-2.50 | 0.40 | - | = 0.015 | - | |
XM27 | 00cr27mo | 0.010 | 25.00-27.50 | - | 0.40 | 0.035 | 0.030 | 0.75-1.50 | 0.40 | - | = 0.015 | - | |
Martensite keluli tahan karat | 403 | 1cr12 | 0.15 | 11.50-13.00 | 3) | 1.00 | 0.035 | 0.030 | - | 0.50 | - | - | - |
410 | 1cr13 | 0.15 | 11.50-13.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
405 | 0CR13 | 0.08 | 11.50-13.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
416 | Y1cr13 | 0.15 | 12.00-14.00 | 3) | 1.25 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
410J1 | 1cr13mo | 0.08-0.18 | 11.50-14.00 | 3) | 1.00 | 0.035 | 0.030 | 0.30-0.60 | 0.60 | - | - | - | |
420J1 | 2cr13 | 0.16-0.25 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
420J2 | 3cr13 | 0.26-0.35 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
420f | Y3CR13 | 0.26-0.40 | 12.00-14.00 | 3) | 1.25 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
3cr13mo | 0.28-0.35 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | 0.50-1.00 | 0.80 | - | - | - | ||
4cr13 | 0.36-0.45 | 12.00-14.00 | 3) | 0.80 | 0.035 | 0.030 | - | 0.60 | - | - | - | ||
431 | 1cr17ni2 | 0.11-0.17 | 16.00-18.00 | 1.50-2.50 | 0.80 | 0.035 | 0.030 | - | 0.80 | - | - | - | |
440A | 7cr17 | 0.60-0.75 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.030 | 4) | 1.00 | - | - | - | |
440b | 8cr17 | 0.75-0.95 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.030 | 4) | 1.00 | - | - | - | |
9CR18 | 0.90-1.00 | 17.00-19.00 | 3) | 0.80 | 0.035 | 0.030 | 4) | 0.80 | - | - | - | ||
440C | 11CR17 | 0.95-1.20 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.030 | 4) | 1.00 | - | - | - | |
440f | Y11CR17 | 0.95-1.20 | 16.00-18.00 | 3) | 1.25 | 0.035 | 0.15 | 4) | 1.00 | - | - | - | |
9cr18mo | 0.95-1.10 | 16.00-18.00 | 3) | 0.80 | 0.035 | 0.030 | 0.40-0.70 | 0.80 | - | - | - | ||
9cr18mov | 0.85-0.95 | 17.00-19.00 | 3) | 0.80 | 0.035 | 0.030 | 1.00-1.30 | 0.80 | - | - | V0.07-0.12 | ||
PH keluli tahan karat | 630 | 0cr17ni4cu4nb | 0.07 | 15.50-17.50 | 6.50-7.50 | 1.00 | 0.035 | 0.030 | - | 1.00 | 3.00-5.00 | - | NB 0.15-0.45 |
631 | 0cr17ni7al | 0.09 | 16.00-18.00 | 6.50-7.50 | 1.00 | 0.035 | 0.030 | - | 1.00 | 0.50 | - | AL 0.75-1.50 |