303 bar rata keluli tahan karat
Penerangan ringkas:
Sakysteel adalahBar rata tahan karatPengilang dan pembekal di China, khusus dalam penyelidikan, pembangunan dan pengeluaran 303 bar rata keluli tahan karat.
| C% | Si% | Mn% | P% | S% | CR% | Ni% | N% | Mo% | Ti% |
| <0.15 | <1.0 | <2.0 | <0.20 | <0.15 | 17.0-19.0 | 8.0-10.0 | - | - | - |
| Spesifikasi 303 bar rata keluli tahan karat: |
| Standard | ASTM A276, A484, A479, A580, A582, JIS G4303, JIS G4311, DIN 1654-5, DIN 17440, KS D3706, GB/T 1220 |
| Bahan | 201,202,205, XM-19 dll. 301,303,304,304L, 304h, 309s, 310s, 314,316,316L, 316ti, 317,321,321h, 329,330,348 dll. 409,410,416,420,430,430F, 431,440 2205,2507, S31803,2209,630,631,15-5PH, 17-4PH, 17-7PH, 904L, F51, F55,253MA dll. |
| Permukaan | Jeruk, dikupas, hitam, letupan pasir, cerah, kilang, cermin, garis rambut dan lain -lain |
| Teknologi | Hot rolled, dikimpal, bengkok |
| Spesifikasi | 20*3mm -100*10mm atau seperti yang diperlukan |
| Toleransi | +-2% |
| 316 produk bar rata keluli tahan karat dari Sakysteel: |
 bar rata keluli tahan karat jeruk |  Sample_logo kanan |
| Permohonan bar rata keluli tahan karat 303 |
1.Domesti
2.Transourt: Sistem Ekzos, Kereta Trim/Grilles, Tangki Jalan, Kapal Kapal, Kapal Kapal Kimia
3. Moil dan Gas: Penginapan Platform, Dulang Kabel
4.Medical: Instrumen pembedahan, implan pembedahan, pengimbas MRI.
5. Makanan dan Minuman: Peralatan katering, pembuatan bir, penyulingan, pemprosesan makanan
6. Air: Rawatan air dan kumbahan, tiub air, tangki air panas
7.General: mata air, pengikat (bolt, kacang dan mesin basuh), dawai
8. Chemical /Pharmaceutical: Kapal Tekanan, Paip Proses
9. Kejuruteraan Awah/Kejuruteraan Awam: pelapisan, keretapi, pintu dan kelengkapan tingkap, perabot jalanan, struktur, bahagian, mengukuhkan bar, lajur pencahayaan, lintel, sokongan batu
| Komposisi kimia bar rata keluli tahan karat: |
| Austenite Keluli tahan karat ferit | 329J1 | 0cr26ni5mo2 | <0.08 | 23.00-28.00 | 3.00-6.00 | <1.50 | <0.035 | <0.030 | 1.00-3.00 | <1.00 | - | 2) |
| 1cr18ni11si4alti | 0.10-0.18 | 17.50-19.50 | 10.-120 .. | <0.80 | <0.035 | <0.030 | - | 3.40-4.00 | - | AL 0.10-0.30; Ti 0.40-0.70 | ||
| 00CR18NI5MOSI2 | <0.030 | 18.00-19.50 | 4.50-5.50 | 1.00-2.00 | <0.035 | <0.030 | 2.50-3.00 | 1.30-2.00 | - | - | ||
| Keluli tahan karat ferit | 405 | 0cr13al | <0.08 | 11.50-14.50 | 3) | <1.00 | <0.035 | <0.030 | - | <1.00 | - | AL 0.10-0.30 |
| 410L | 00CR12 | <0.030 | 11.00-13.00 | 3) | <1.00 | <0.035 | <0.030 | - | <1.00 | - | - | |
| 430 | 1cr17 | <0.12 | 16.00-18.00 | 3) | <1.25 | <0.035 | <0.030 | - | <0.75 | - | - | |
| 430f | Y1cr17 | <0.12 | 16.00-18.00 | 3) | <1.00 | <0.035 | <0.15 | 1) | <1.00 | - | - | |
| 434 | 1cr17mo | <0.12 | 16.00-18.00 | 3) | <1.00 | <0.035 | <0.030 | 0.75-1.25 | <1.00 | - | - | |
| 447J1 | 00CR30MO2 | <0.010 | 28.50-32.00 | - | <0.40 | <0.035 | <0.030 | 1.50-2.50 | <0.40 | <0.015 | - | |
| XM27 | 00cr27mo | <0.010 | 25.00-27.50 | - | <0.40 | <0.035 | <0.030 | 0.75-1.50 | <0.40 | <0.015 | - |
| Martensite keluli tahan karat | 403 | 1cr12 | <0.15 | 11.50-13.00 | 3) | <1.00 | <0.035 | <0.030 | - | <0.50 | - | - |
| 410 | 1cr13 | <0.15 | 11.50-13.50 | 3) | <1.00 | <0.035 | <0.030 | - | <1.00 | - | - | |
| 405 | 0CR13 | <0.08 | 11.50-13.50 | 3) | <1.00 | <0.035 | <0.030 | - | <1.00 | - | - | |
| 416 | Y1cr13 | <0.15 | 12.00-14.00 | 3) | <1.25 | <0.035 | <0.15 | 1) | <1.00 | - | - | |
| 410J1 | 1cr13mo | <0.08-0.18 | 11.50-14.00 | 3) | <1.00 | <0.035 | <0.030 | 0.30-0.60 | <0.60 | - | - | |
| 420J1 | 2cr13 | 0.16-0.25 | 12.00-14.00 | 3) | <1.00 | <0.035 | <0.030 | - | <1.00 | - | - | |
| 420J2 | 3cr13 | 0.26-0.35 | 12.00-14.00 | 3) | <1.00 | <0.035 | <0.030 | - | <1.00 | - | - | |
| 420f | Y3CR13 | 0.26-0.40 | 12.00-14.00 | 3) | <1.25 | <0.035 | <0.15 | 1) | <1.00 | - | - | |
| 3cr13mo | 0.28-0.35 | 12.00-14.00 | 3) | <1.00 | <0.035 | <0.030 | 0.50-1.00 | <0.80 | - | - | ||
| 4cr13 | 0.36-0.45 | 12.00-14.00 |