430 pepa kowiri tiraHangarau matū me nga taonga miihini: |
C% | Si% | MN% | P% | S% | Kr% | Ni% | N% | Mo% | TI% |
0.12 | 1.00 | 1.00 | 0.040 | 0.030 | 16.0-18.0 | 0.75 | - | - | - |
T * s | Y * s | Mamaehau | Rei |
(MPA) | (MPA) | Hrb | HB | (%) |
520 | 205 | - | - | 40 |
Ka hurihia te makariri430 pepa kowiri tira: |
1. Akoranga: 200 & 300 raupapa
200 Kaihono: 201,202, J4
300 Kaitohu: 301, 304, 304l, 321, 316L, 309, 310
2. Paerewa: JIS, ASTM, AISI, GB, Din, En, Ko te tikanga ka whakamahi maatau i te paerewa ASTM me te GB
3. matotoru: 0.14mm-3.0mm
4. Whanui: e hiahia ana
5. Mata: 2b kua oti, ka oti
6. Hardness: ngohengohe, 1/4h, 1 / 2h, fh
7. Te tahua matotoru: +/- 0.02mm
8. Whanui Te Manawanui: +/- 10mm (Mill Land)
He maha atu nga tohu o te 430 SS pepa: |
Tuhinga | Kōeke | Kōeke | Waahanga matū% |
Austenitic kowiri tira | | | C | Cr | Ni | Mn |
201 | 1cr17n6ni5n | 0.15 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 |
201l | 03CR17MEN6NI5N | 0.030 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 |
202 | 1cr18mn8ni5n | 0.15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 |
204 | 03cr16mn8ni2n | 0.030 | 15.00-17.00 | 1.50-3.50 | 7.00-9.00 |
| 1cr18mn10ni5mo3n | 0.10 | 17.00-19.00 | 4.00-6.00 | 8.50-120-12.00 |
| 2cr13MMN9ni4 | 0.15-0.25 | 12.00-14.00 | 3.70-5.00 | 8.00-10.00 |
| 2cr15mn15ni2n | 0.15-0.25 | 14.00-16.00 | 1.50-3.00 | 14.00-16.00 |
| 1cr18mn10ni5mo3n | 0.15 | 17.00-19.00 | 4.00-6.00 | 8.50-120-12.00 |
301 | 1cr17ni7 | 0.15 | 16.00-18.00 | 6.00-8.00 | 2.00 |
302 | 1cr18ni9 | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 |
303 | Y1CR18NI9 | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 |
303SE | Y1cr18ni9se | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 |
304 | 0cr18ni9 | 0.07 | 17.00-19.00 | 8.00-10.00 | 2.00 |
304L | 00cr19ni10 | 0.030 | 18.00-20.00 | 8.00-10.00 | 2.00 |
304n1 | 0cr19ni9n | 0.08 | 18.00-20.00 | 7.00-10.50 | 2.00 |
304n2 | 0cr18ni10nbn | 0.08 | 18.00-20.00 | 7.50-10.50 | 2.00 |
304LN | 00cr18ni10n | 0.030 | 17.00-19.00 | 8.50-1150 | 2.00 |
305 | 1cr18ni12 | 0.12 | 17.00-19.00 | 10.50-150-135.00 | 2.00 |
309s | 0cr23ni13 | 0.08 | 22.00-24.00 | 12.00-15.00 | 2.00 |
310s | 0cr25ni20 | 0.08 | 24.00-26.00 | 19.00-22.00 | 2.00 |
316 | 0cr17ni12Mo2 | 0.08 | 16.00-18.50 | 10.00-14.00 | 2.00 |
| 1cr18ni12Mo2To6) | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 |
| 0cr18ni12Mo2Ti | 0.08 | 16.00-19.00 | 11.00-14.00 | 2.00 |
316L | 00cr17ni14Mo2 | 0.030 | 16.00-18.00 | 12.00-15.00 | 2.00 |
316n | 0cr17ni12Mo2N | 0.08 | 16.00-18.00 | 10.00-14.00 | 2.00 |
316n | 00cr17ni13Mo2N | 0.030 | 16.00-18.50 | 10.50-150-14.50 | 2.00 |
316J1 | 0cr18ni12Mo2cu2 | 0.08 | 17.00-19.00 | 10.00-14.50 | 2.00 |
316J1l | 00cr18ni14Mo2cu2 | 0.030 | 17.00-19.00 | 12.00-16.00 | 2.00 |
317 | 0cr19ni13Mo3 | 0.12 | 18.00-20.00 | 11.00-15.00 | 2.00 |
317L | 00cr19ni13Mo3 | 0.08 | 18.00-20.00 | 11.00-15.00 | 2.00 |
| 1cr18ni12To3ti6 | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 |
| 0cr18ni12To3ti | 0.08 | 16.00-19.00 | 11.00-14.00 | 2.00 |
317J1 | 0cr18ni16mo5 | 0.040 | 16.00-19.00 | 15.00-17.00 | 2.00 |
321 | 1cr18ni9ti6 | 0.12 | 17.00-19.00 | 8.00-11.00 | 2.00 |
| 0cr18ni10ti | 0.08 | 17.00-19.00 | 9.00-12.00 | 2.00 |
347 | 0cr18ni11NB | 0.08 | 17.00-19.00 | 9.00-13.00 | 2.00 |
Xm7 | 0cr18ni9cu3 | 0.08 | 17.00-19.00 | 8.50-10.50 | 2.00 |
XM15J1 | 0cr18ni13si13si | 0.08 | 15.00-20.00 | 11.50-15.00 | 2.00 |
O mua: He kowiri tira kowiri tira Tō muri mai: He kowiri tira kowiri