Aliquam Steel T sectionem
Short description:
Aliquam Steel T Bar, T sectionem vel Tee profile cum gradu 201,303,304,304l, 316,316L, 316ti, 321,310s, 410,430
Cubits deStainless ferro T talea: |
Vexillum | ASTM A276, A484, A479, A580, A582, JIS G4303, Jis G4311, Laudate 1654-5, Laudate (XVII) CDXL, KS D3706, GB / T MCCXX |
Materia | 2010,202.205, XM-XIX etc. 301,303,304,304l, 304h, 309s, 310s 314,316,316L 316ti 317,321,321h, 329,330,348 etc. 409,410,416,420,430,430f, 431.440 2205,2507, S31803,2209,630,631,15-5ph, 17-4ph, 17-7ph, 904L, F51, F55,253MA etc. |
Superficies | Clara, politibus, CONDITANEUS, depilatus, nigrum, molere, molendini, speculum, hairline etc. |
Technology | Frigus instructa, calidum advolvit, ferebantur |
Cubits | ut requiratur |
Tolerantia | H9, H11, H13, K9, K11, K13 vel quod requiratur |
Aliquam Steel T sect products de sakysteleel: |
PondusStainless Steel T Bar |
Exemplar | Pondus | Exemplar | Pondus |
C * L * V * VII | 9.54 | CCCLIV * CCCLIV XVI * XVI * XVI | CXXXI |
C * C * VI * VIII | 17.2 | CCCXLVI * CLXXIV * VI * IX | 41.8 |
CXXV * LX * VI * VIII | 13,3 | CCCL * CLXXV * VII * XI | 50 |
CXXV * CXXV * 6.5 * IX | 23.8 | CCCXLIV * CCCXLVIII * X * XVI | CXV |
CXLVIII * C * VI * IX | 21,4 | CCCL * CCCL * XII * XIX | CXXXVII |
CL * LXXV * V * VII | 14.3 | CCCLXXXVIII * CDII * XV * XV | CXLI |
CL * CL * VII * X | 31.9 | CCCXC * CCC * X * XVI | CVII |
CLXXV * XC * V * VIII | 18.2 | CCCXCIV * CCCXCVIII * XI * XVIII | CXLVII |
CLXXV * CLXXV * 7.5 * XI | 40,3 | CD * CL * VIII * XIII | 55.8 |
CXCIV * CL * VI * IX | 31.2 | CCCXCVI * CXCIX * VII * XI | 56.7 |
* XCIX * XCIX * 4.5 * VII | 18,5 | CD * CC * VIII * XIII | 66 |
CC * C * 5.5 * VIII | 21,7 | CD * CD * XIII * XXI | CLXXII |
CC * CC * VIII * XII | 50.5 | CDVIII * CDVIII * XXI XXI * | CXCVII |
CC * CCIV * XII * XII | 72,28 | CDXIV * CDV * XVIII * XXVIII | CCXXXIII |
CCXLIV * CLXXV * VII * XI | 44.1 | CDXL * CCC * XI * XVIII | CXXIV |
CCXLIV * CCLII * XI * XI | 64.4 | CDXLVI * CXCIX * VII * XI | 66.7 |
CCXLVIII * CXXIV * V * VIII | 25.8 | CDL * CC * 9-14 | 76.5 |
CCL * CXXV * VI * IX | 29.7 | CDLXXXII * CCC * XI * XV | CXV |
CCL * CCL * IX * XIV | 72,4 | CDLXXXVIII * CCC * XI * XVIII | CXXIX |
CCL * CCLV * XIV * XIV | 82.2 | CDXCVI * CXCIX * IX * XIV | 79.5 |
CCXCIV * CC * VIII * XII | 57.3 | D * CC * X * XVI | 89.6 |
CCC * CL * 6.5 * IX | 37,3 | DLXXXII * CCC * XII * XVII | CXXXVII |
CCXCIV * CCCII * XII * XII | 85 | DLXXXVIII * CCC * XII * XX | CLI |
CCC * CCC * X * XV | 94,5 | DXCVI * CXCIX * X * XV | 95.1 |
* CCC * CCC * CCC * XV | CVI | DC * CC * XI * XVII | CVI |
CCCXXXVIII * CCCLI * XIII * XIII | CVI | DCC * CCC * XIII * XXIV | CLXXXV |
CCCXL * CCL * IX * XIV | 79.7 |
Plus gradusStainless ferro T talea: |
Genus | Gradus | Gradus | Chemica pars% | ||||||||||
C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | Alius | |||
Austenititic Aliquam Steel | CCI | 1Cr1117Mn6ni5N | 0.15 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | 0.060 | 0.030 | - | 1.00 | - | 0,25 | - |
201L | 03Cr17Mn6ni5N | 0.030 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | 0.060 | 0.030 | 1.00 | 0,25 | ||||
CCII | 1Cr18mn8ni5n | 0.15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | 0.060 | 0.030 | 1.00 | - | 0,25 | - | ||
CCIV | 03CR16Mn8ni2N | 0.030 | 15.00-17.00 | 1.50-3.50 | 7.00-9.00 | 0.15-0.30.30 | |||||||
1Cr18mn101ni5mo3n | 0,10 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 | 2.80-3.50 | 0.20-0.30 | |||||||
2Cr13Mn9ni4 | 0.15-0.25 | 12.00-14.00 | 3.70-5.00 | 8.00-10.00 | |||||||||
2Cr15Mn15ni2N | 0.15-0.25 | 14.00-16.00 | 1.50-3.00 | 14.00-16.00 | 0.15-0.30.30 | ||||||||
1Cr18mn101ni5mo3n | 0.15 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 | 0.060 | 0.030 | 2.8-3.5 | 1.00 | - | 0.20-0.30 | - | ||
CCCI | 1Cr17ni7 | 0.15 | 16.00-18.00 | 6.00-8.00 | 2.00 | 0.065 | 0.030 | - | 1.00 | - | - | - | |
CCCII | 1Cr18ni9 | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
CCCIII | Y1cr18ni9 | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | 0,20 | 0.030 | 1) | 1.00 | - | - | - | |
303E | Y1cr18ni9se | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | 0,20 | 0.030 | - | 1.00 | - | - | Se = 0.15 | |
CCCIV | 0CR18ni9 | 0,07 | 17.00-19.00 | 8.00-10.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
304L | 00CR19ni10 | 0.030 | 18.00-20.00 | 8.00-10.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
304N1 | 0Cr19ni9n | 0,08 | 18.00-20.00 | 7.00-10.50 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | 0.10-0.25 | - | |
304n2 | 0Cr18ni10nbn | 0,08 | 18.00-20.00 | 7.50-10.50 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | 0.15-0.30.30 | NB = 0.15 | |
304Ln | 007n1110n | 0.030 | 17.00-19.00 | 8.50-11.50 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | 0.12-0.22 | - | |
CCCV | 1Cr18ni12 | 0.12 | 17.00-19.00 | 10.50-13.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
309s | 0Cr23ni13 | 0,08 | 22.00-24.00 | 12.00-15.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
310s | 0Cr25NI20 | 0,08 | 24.00-26.00 | 19.00-22.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
CCCXVI | 0C17NI12MO2 | 0,08 | 16.00-18.50 | 10.00-14.00 | 2.00 | 0.035 | 0.030 | 2.00-3.00 | 1.00 | - | - | - | |
1Cr18ni12Mo2TI6) | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 | 0.035 | 0.030 | 1.80-2.50 | 1.00 | - | - | Ti5 (C% -0.02) ~ 0.08 | ||
0C18ni12Mo2TI | 0,08 | 16.00-19.00 | 11.00-14.00 | 2.00 | 0.035 | 0.030 | 1.80-2.50 | 1.00 | - | - | Ti5 * C% -0.70 | ||
316L | 00CR17ni14Mo2 | 0.030 | 16.00-18.00 | 12.00-15.00 | 2.00 | 0.035 | 0.030 | 2.00-3.00 | 1.00 | - | - | - | |
316n | 0Cr12ni12Mo2N | 0,08 | 16.00-18.00 | 10.00-14.00 | 2.00 | 0.035 | 0.030 | 2.00-3.00 | 1.00 | - | 0.10-0.22 | - | |
316n | 00CR17ni13Mo2N | 0.030 | 16.00-18.50 | 10.50-14.50 | 2.00 | 0.035 | 0.030 | 2.00-3.00 | 1.00 | - | 0.12-0.22 | - | |
316J1 | 0CR18NI12Mo2Cu2 | 0,08 | 17.00-19.00 | 10.00-14.50 | 2.00 | 0.035 | 0.030 | 1.20-2.75 | 1.00 | 1.00-2.50 | - | - | |
316J1LL | 00CR18ni14Mo2Cu2 | 0.030 | 17.00-19.00 | 12.00-16.00 | 2.00 | 0.035 | 0.030 | 1.20-2.75 | 1.00 | 1.00-2.50 | - | - | |
CCCXVII | 0Cr19NI13MO3 | 0.12 | 18.00-20.00 | 11.00-15.00 | 2.00 | 0.035 | 0.030 | 3.00-4.00 | 1.00 | - | - | - | |
317L | 00CR19NI13MO3 | 0,08 | 18.00-20.00 | 11.00-15.00 | 2.00 | 0.035 | 0.030 | 3.00-4.00 | 1.00 | - | - | - | |
1Cr18ni12Mo3TI6 | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 | 0.035 | 0.030 | 2.50-3.50 | 1.00 | - | - | Ti5 (C% -0.02) ~ 0.08 | ||
0CR18NI12Mo3TI | 0,08 | 16.00-19.00 | 11.00-14.00 | 2.00 | 0.035 | 0.030 | 2.50-3.50 | 1.00 | - | - | Ti5 * C% -0.70 | ||
317J1 | 0C18ni16Mo5 | 0.040 | 16.00-19.00 | 15.00-17.00 | 2.00 | 0.035 | 0.030 | 4.00-6.00 | 1.00 | - | - | - | |
CCCXXI | 1Cr18ni9ti6 | 0.12 | 17.00-19.00 | 8.00-11.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | Ti5 (C% -0.02) ~ 0.08 | |
0CR18ni10TI | 0,08 | 17.00-19.00 | 9.00-12.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | TI = V * C% | ||
CCCXLVII | 0Cr18ni11NB | 0,08 | 17.00-19.00 | 9.00-13.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | NB = X * C% | |
XM7 | 0cr18ni9cu3 | 0,08 | 17.00-19.00 | 8.50-10.50 | 2.00 | 0.035 | 0.030 | - | 1.00 | 3.00-4.00 | - | - | |
Xm15j1 | 0CR18ni13si4 | 0,08 | 15.00-20.00 | 11.50-15.00 | 2.00 | 0.035 | 0.030 | - | 3.00-5.00 | - | - | 2) | |
Austenite | 329J1 | 0Cr26ni5MO2 | 0,08 | 23.00-28.00 | 3.00-6.00 | 1.50 | 0.035 | 0.030 | 1.00-3.00 | 1.00 | - | - | 2) |
| | 1Cr18ni11si4alti | 0.10-.18 | 17.50-19.50 | 10 ..-CXX | 0,80 | 0.035 | 0.030 | - | 3.40-4.00 | - | - | 0.10-0.30; Ti 0.40-0.70 | |
Ferrite immaculatam ferro | 00ccr18ni5mosi2 | 0.030 | 18.00-19.50 | 4.50-5.50 | 1.00-2.00 | 0.035 | 0.030 | 2.50-3.00 | 1.30-2.00 | - | - | - | |
Ferrite immaculatam ferro | CDV | 0C13AL | 0,08 | 11.50-14.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | 0.10-0.30 |
410L | 00CR12 | 0.030 | 11.00-13.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
CDXXX | 1C17 | 0.12 | 16.00-18.00 | 3) | 1,25 | 0.035 | 0.030 | - | 0,75 | - | - | - | |
430f | Y1cr17 | 0.12 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
CDXXXIV | 1Cr17mo | 0.12 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.030 | 0.75-1.25 | 1.00 | - | - | - | |
447J1 | 00CR30MO2 | 0.010 | 28.50-32.00 | - | 0,40 | 0.035 | 0.030 | 1.50-2.50 | 0,40 | - | = 0.015 | - | |
Xm27 | 00Cr27mo | 0.010 | 25.00-27.50 | - | 0,40 | 0.035 | 0.030 | 0,75-1.50 | 0,40 | - | = 0.015 | - | |
Martensite immaculatam ferro | CDIII | 1Cr12 | 0.15 | 11.50-13.00 | 3) | 1.00 | 0.035 | 0.030 | - | 0,50 | - | - | - |
CDX | 1CR13 | 0.15 | 11.50-13.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
CDV | 0C13 | 0,08 | 11.50-13.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
CDXVI | Y1cr13 | 0.15 | 12.00-14.00 | 3) | 1,25 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
4101j1 | 1Cr13mo | 0.08-0..18 | 11.50-14.00 | 3) | 1.00 | 0.035 | 0.030 | 0.30-0.60 | 0.60 | - | - | - | |
4201 | 2Cr13 | 0.16-0.25 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
4202 | 3Cr13 | 0.26-0.35 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
420f | Y3cr13 | 0.26-0.40.40 | 12.00-14.00 | 3) | 1,25 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
3Cr13mo | 0.28-0.35 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | 0,50-1.00 | 0,80 | - | - | - | ||
4Cr13 | 0.36-0.45 | 12.00-14.00 | 3) | 0,80 | 0.035 | 0.030 | - | 0.60 | - | - | - | ||
CDXXXI | 1Cr17ni2 | 0.11-.17 | 16.00-18.00 | 1.50-2.50 | 0,80 | 0.035 | 0.030 | - | 0,80 | - | - | - | |
440a | 7Cr17 | 0.60-0.75 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.030 | 4) | 1.00 | - | - | - | |
440b | 8Cr17 | 0.75-0.95 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.030 | 4) | 1.00 | - | - | - | |
9Cr18 | 0,90-1.00 | 17.00-19.00 | 3) | 0,80 | 0.035 | 0.030 | 4) | 0,80 | - | - | - | ||
440c | 11Cr1017 | 0.95-1.20 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.030 | 4) | 1.00 | - | - | - | |
440f | Y11cr17 | 0.95-1.20 | 16.00-18.00 | 3) | 1,25 | 0.035 | 0.15 | 4) | 1.00 | - | - | - | |
9c18mo | 0,95-1.10 | 16.00-18.00 | 3) | 0,80 | 0.035 | 0.030 | 0.40-0.70 | 0,80 | - | - | - | ||
9Cr18Mov | 0.85-0.95 | 17.00-19.00 | 3) | 0,80 | 0.035 | 0.030 | 1.00-1.30 | 0,80 | - | - | V0.07-0..12 | ||
PH Stainless Steel | DCXXX | 0Cr17ni4Cu4nb | 0,07 | 15.50-17.50 | 6.50-7.50 | 1.00 | 0.035 | 0.030 | - | 1.00 | 3.00-5.00 | - | NB 0.15-0.45 |
DCXXXI | 0C101NI7AL | 0,09 | 16.00-18.00 | 6.50-7.50 | 1.00 | 0.035 | 0.030 | - | 1.00 | 0,50 | - | 0,75-1.50 |