    Hastelloy C-4 (UNS NO6455)

    Hastelloy C-4 Features et Applications Overview:
    stannum austeniticum est offensio carbonis humilis Nickel-molybdaeno-chromium. Praecipua differentia inter Nicrofer 6616 hMo et alia mixtura compositionis chemicae similis, quae ante exculta est, est gravis carbonis, pii, ferri et tungsten. Haec compositio chemica optimam stabilitatem praebet in 650-1040 ° C et repugnantiam emendavit ad corrosionem intergranularem, vitando aciem corrosionis rectae susceptibilitatem et corrosionem redactam HAZ sub congruis conditionibus fabricandis. Admiscuit systemata desulfurizationis in flue gas, plantarum regenerationis acidorum et salsamentorum, aceticorum aceticorum chemicorum productionis agriculturae, productionis dioxidis titanium (modus chloride ), plating electrolytica.
    Hastelloy C-4 Similes faces:
    NS335 (Sina) W.Nr.2.4610 NiMo16Cr16Ti (Germania)
    Hastelloy C-4 Chemica compositio:

    Alloy
    Gradus

    %

    Ni

    Cr

    Fe

    Mo

    Nb

    Co

    C

    Mn

    Si

    S

    Cu

    Al

    Ti

    Hastelloy C-4

    Min

    Margin

    14.5

     

    14.0

                     

    Maximum

    17.5

    3.0

    17.0

     

    2.0

    0.009

    1.0

    0.05

    0.01

       

    0.7

    Hastelloy C-IV Physica;

    Density
    g/cm3

    punctum liquescens

    Scelerisque conductivity
    λ/(W/m•℃)

    Imprimis calor facultatem
    J/kg•℃

    Modulus elasticus
    GPa

    tondendas modulus
    GPa

    Resistentia
    µΩ•m

    Ratio Poisson

    Expansio linearis coefficiens
    a/10-6℃-1

    8.6

    1335
    1380

    10.1(100℃)

    408

    211

     

    1.24

     

    10.9(100℃)

    Hastelloy C-4 Proprietates Mechanicae: (pericula mechanica ad 20 );

    Calefacere modi curatio

    Robora distrahentes / MPa

    Cede Strengthσp0.2/MPa

    Prolongatio rate σ5 /%

    Brinell duritia HBS

    Solutio curatio

    690

    275

    40

     

    Hastelloy C-4 signa productionis:

    Standard

    Bar

    Forgings

    Materia (cum)

    Filum

    Pipe

    Societas Americana ad probationes et materias

    ASTM B574

    ASTM B336

    ASTM B575

     

    ASTM B622
    ASTM B619
    ASTM B626

    American Aerospace Materials Technical Specification

             

    American Societatis Scientiarum mechanicarum

    ASME SB574

    ASME SB336

    ASME SB575

     

    ASTM SB622
    ASTM SB619
    ASTM SB626

    Hastelloy C-4 processus perficiendi et requisita:

    1, In caloris curationis processu non attingere cum sulphure, phosphoro, plumbo et aliis metallis punctum liquescens, vel mixturae fragilis fiet, observandum est ad tollendum ut pingere pingere, temperatura indicator pingere, coloratus crayons, unguenta, cibus et alii fimum. Sulphuris contentum escae inferiorem eo melius, sulphur contentum gasi naturalis minus quam 0.1% esse debet, sulphur contentum olei gravis minus quam 0,5% esse debet. Fornax electrica calefactio melior est electio, quia fornax electrica accurate temperare potest, et fornax gas mundi est. Si satis purus fumus gasi gasi, eligere potes.
    II, mixtura scelerisque processus temperatus range ex 1080 ~ 900 , methodus refrigerandi aquae refrigerationis vel alia celeri refrigerationis. Ut optima repugnantia corrosio, curatio caloris peragi debet post curatio solutionis caloris.