347 yaiku stainless steel austenit sing ora ana, nalika 347h minangka versi karbon sing dhuwur. Ing babagan komposisi,347Bisa dideleng minangka wesi sing asale saka nambah Niobium menyang dasar 304 stainless steel. Niobium minangka unsur bumi sing langka sing fungsine padha karo titanium. Yen ditambahake aloi, bisa nyaring struktur gandum, nolak karat intergranular, lan promosi Hardening.
Ⅰ.corresponden kanggo standar nasional
| China | Gbit 20878-200007 | 06cr18ni11nb | 07Cr18ni11nb (1cr19NI11nb) |
| US | ASTM A240-15A | S34700,347 | S34709,347H |
| Jis | J1S G 4304: 2005 | SUS 347 | - |
| Din | Ing 10088-1-2005 | X6crninb18-10 1.4550 | X7crninb18-10 1.4912 |
Ⅱ.chemical komposisi saka S34700 bar stainless steel
| Kelas | C | Mn | Si | S | P | Fe | Ni | Cr |
| 347 | 0,08 Max | 2.00Max | 1.0 Max | 0,030MAX | 0,045 Max | 62.74 min | 9-12xx | 17.00-19.00 |
| 347h | 0,04 - 0.10 | 2.0 Max | 1.0 Max | 0,030 Max | 0,045 Max | 63.72 min | 9-12xx | 17.00 - 19.00 |
Ⅲ.347 347H sifat mekanisme bar baja tahan karat stainless
| Kapadhetan | Titik lebur | Kekuwatan tensile (MPA) min | Kekuwatan Ngasilake 0,2% Bukti (MPA) min | Elongation (% ing 50mm) min |
| 8.0 g / cm3 | 1454 ° C (2650 ° F) | PSI - 75000, MPA - 515 | PSI - 30000, MPA - 205 | 40 |
Properti ⅳ.Material
Rintangan karat ①Excellent dibandhingake karo 304 baja stainless.
② Antarane 427 ~ 816 ℃, bisa nyandhet pembentukan kromium karbida, tahan sensitif, lan nduweni resistensi sing apik kanggo karat intergranular.
Isih isih resistensi creep tartamtu ing lingkungan pengoksidaan sing kuwat kanthi suhu 816 ℃.
④Easy kanggo ngluwihi lan mbentuk, gampang kanggo weld.
⑤Good kekurangan suhu angel.
Eval
Kinerja suhu sing dhuwur saka347 & 347HStainless steel luwih apik tinimbang 304 lan 321. Digunakake kanthi akeh ing Aviation, Pangan, Kertas lan Industri Khusus Mesin Aircraft, lan ing kakehan cilik lan suhu ora luwih saka 850 ° C. Bagéan sing bisa digunakake ing kahanan, lsp.