440C stainless steel flat barminangka produk baja tahan karat berkualitas tinggi sing dikenal kanthi kombinasi sing luar biasa saka resistensi nyandhang lan tahan karat. Iku belongs kanggo kulawarga stainless steel martensitic lan digunakake digunakake ing macem-macem industri kanggo kinerja unggul.
Standar Baja Tahan Karat 440C lan Kelas Baja Setara
| negara | USA | BS & DIN | Jepang |
| Standar | ASTM A276 | EN 10088 | JIS G4303 |
| biji | S44004/440C | X105CrMo17/1.4125 | SUS440C |
ASTM A276 440C Komposisi Kimia Baja lan Setara
| Standar | sasmita | C | Mn | P | S | Si | Cr | Mo |
| ASTM A276 | S44004/440C | 0.95-1.20 | ≦1.00 | ≦0.04 | ≦0.03 | ≦1.00 | 16.0-18.0 | ≦0.75 |
| EN10088 | X105CrMo17/1.4125 | 0.95-1.20 | ≦1.00 | ≦0.04 | ≦0.03 | ≦1.00 | 16.0-18.0 | 0.40-0.80 |
| JIS G4303 | SUS 440C | 0.95-1.20 | ≦1.00 | ≦0.04 | ≦0.03 | ≦1.00 | 16.0-18.0 | ≦0.75 |
Baja tahan karat 440CMekanikProperti
| Suhu Tempering (°C) | Kekuwatan Tarik (MPa) | Kekuwatan Ngasilake 0,2% Bukti (MPa) | Elongation (% ing 50mm) | Hardness Rockwell (HRC) | Dampak Charpy V (J) |
| Anil* | 758 | 448 | 14 | 269HB maks# | - |
| 204 | 2030 | 1900 | 4 | 59 | 9 |
| 260 | 1960 | 1830 | 4 | 57 | 9 |
| 306 | 1860 | 1740 | 4 | 56 | 9 |
| 371 | 1790 | 1660 | 4 | 56 | 9 |
Ing ngisor iki sawetara poin penting kanggo ngenalake bar warata stainless steel 440C:
1. Komposisi: 440C stainless steel flat bar utamané dumadi saka kromium (16-18%), karbon (0.95-1.20%), lan jumlah cilik saka unsur kaya manganese, silikon, lan molibdenum.
2. Wear Resistance: 440C stainless steel flat bar misuwur kanggo resistance nyandhang pinunjul, nggawe cocok kanggo aplikasi nglibatno bahan abrasive, alat nglereni, bantalan, lan komponen nyandhang-tahan.
3. Resistance Korosi: Senadyan kang dhuwur-karbon stainless steel, 440C nuduhake resistance karat apik.
4. Kekerasan lan Kekuwatan: 440C stainless steel flat bar nduweni atose banget lan kekuatan dhuwur, nyediakake kekiatan lan dhowo umure ing aplikasi nuntut.
Wektu kirim: Jul-05-2023