Saky Steel memproduksi lembaran baja tahan karat martensit 440 seri 440A, 440B, 440C
AISI 440A, UNS S44002, JIS SUS440A, W.-nr. 1.4109 (DIN X70CrMo15) lembaran baja tahan karat, piring, flat
AISI 440B, UNS S44003, JIS SUS440B, W.-nr. 1.4112 (DIN X90CrMoV18) lembaran baja tahan karat, piring, flat
AISI 440C, UNS S44004, JIS SUS440C, W.-nr. 1.4125 (DIN X105CrMo17) lembaran baja tahan karat, piring, flat
440A 440B 440C komponen kimia:
| sasmita | C | Si | Mn | S | P | Cr | Ni | Mo |
| 440A | 0.60~0.75 | ≤1 | ≤1 | ≤0,030 | ≤0,040 | 16.00-18.00 | - | ≤0,75 |
| 440B | 0,85~0,95 | ≤1 | ≤1 | ≤0,030 | ≤0,035 | 16.00-18.00 | ≤0.60 | ≤0,75 |
| 440C | 0.95 – 1.20 | ≤1 | ≤1 | ≤0,030 | ≤0,040 | 16.00-18.00 | - | ≤0,75 |
Isi karbon lan atose 440A-440B-440C tambah berturut-turut saka ABC (A-0,75%, B-0,9%, C-1,2%). 440C minangka baja tahan karat dhuwur sing apik banget kanthi kekerasan 56-58 RC. Telu baja iki nduweni ketahanan karat sing apik, 440A paling apik, lan 440C paling murah. 440C iku umum banget. Komposisi kimia baja tahan karat martensit ditondoi kanthi tambahan unsur kayata molibdenum, tungsten, vanadium, lan niobium adhedhasar kombinasi komponen beda 0,1% -1,0% C lan 12% -27% Cr. Wiwit struktur jaringan minangka struktur kubik sing dipusatake ing awak, kekuwatane mudhun banget ing suhu dhuwur. Ing ngisor 600 ° C, kekuatan suhu dhuwur paling dhuwur ing antarane kabeh jinis baja tahan karat, lan kekuatan creep uga paling dhuwur. 440A nduweni sifat quenching lan hardening lan kekerasan dhuwur. Nduwe kateguhan sing luwih dhuwur tinimbang baja 440B lan baja 440C. 440B digunakake kanggo alat nglereni, alat ukur, bantalan lan katup. Wis atose luwih saka 440A baja lan kateguhan luwih saka 440C baja. 440C nduweni kekerasan paling dhuwur ing kabeh baja tahan karat lan baja tahan panas lan digunakake kanggo nozel lan bantalan. 440F minangka kelas baja sing nambah sifat baja 440C sing gampang dipotong kanggo mesin bubut otomatis.