Igwe igwe anaghị agba nchara oyi
Nkọwa dị mkpirikpi:
Igwe igwe anaghị agba nchara Otu ihe ngosi ọrụ: |
Ngwakọta kemịkalụ na akụrụngwa akụrụngwa |
C% | Si% | Mn% | P% | S% | kr% | Ni% | N% | mo% | Ti% |
0.08 | 0.75 | 2.0 | 0,045 | 0,030 | 18.0-20.0 | 8.0-10.5 | 0.10 | - | - |
T*S | Y*S | Isi ike | Ogologo oge | |
(Mpa) | (Mpa) | HRB | HB | (%) |
520 | 205 | - | - | 40 |
Nkọwa nke igwe anaghị agba nchara oyi akpọrepu: |
Nkọwa | Igwe igwe anaghị agba nchara oyi akpọrepu |
Ihe onwunwe | 201, 202,304, 304L,316,316L,317,317L,321,347H,309,309S ,310,310S,410, 420, 430, wdg. |
ọkọlọtọ | ASTM A240, JIS G4304, G4305, GB/T 4237, GB/T 8165, BS 1449, DIN17460, DIN 17441 |
Nha | Ọkpụrụkpụ: 0.03-3mm Ogologo: 8-600mm, |
Ngwucha elu | 2B, BA, 2D, No.1, No.4, No.8,8K, (enyo), polished, HL (hairline), wdg |
Ngwa | a) Ụlọ ọrụ na-eje ozi n'ozuzu (petroleum, nri, kemịkalụ, akwụkwọ, fatịlaịza, akwa, ụgbọ elu na nuklia) b) Nrụgide na nnyefe ọkụ c) Ihe owuwu na ihe ịchọ mma |
ngwugwu | Ngwunye ọkọlọtọ mbupụ: igbe osisi jikọtara ọnụ ma ọ bụ achọrọ; |
Oge Mbuga ozi | Dị ka ọnụ ọgụgụ ndị ahịa si dị. |
Ịkwụ ụgwọ | T/T, L/C, na Western Union |
Ahịa | Europe, South America, Africa, Oceania, dị ka: USA,Germany,India,Iran,Dubai,Iraq,Vietnam,Ireland, Singapore, na ndị ọzọ |
Akara ule ndị ọzọeriri igwe anaghị agba nchara oyi akpọrepu: |
Ọkwa | Si | Mn | p | S | Cr | Mo | Ni | ọzọ |
201 | 0.15 | 1.00 | 5.5-7.5 | 0.06 | 0.03 | 16-18 | - | 1.0 |
202 | 0.15 | 1.00 | 7.5-10.0 | 0.06 | 0.03 | 17-19 | - | 4.0-6.0 |
301 | 0.15 | 1.00 | 2.00 | 0,045 | 0.03 | 16-18 | - | 6.0-8.0 |
304 | 0.08 | 1.00 | 2.00 | 0,045 | 0.03 | 18-20 | - | 8-10.5 |
304l | 0.03 | 1.00 | 2.00 | 0,045 | 0.03 | 18-20 | - | 9-13 |
309s | 0.08 | 1.00 | 2.00 | 0,045 | 0.03 | 22-24 | - | 12-15 |
310s | 0.08 | 1.5 | 2.00 | 0,045 | 0.03 | 24-26 | - | 19-22 |
316 | 0.03 | 1.00 | 2.00 | 0,045 | 0.03 | 16-18 | 2-3 | 10-14 |
316L | 0.03 | 1.00 | 2.00 | 0,045 | 0.03 | 16-18 | 2-3 | 12-15 |
321 | 0.08 | 1.00 | 2.00 | 0,045 | 0.03 | 17-19 | - | 9-13 |
430 | 0.12 | 0.75 | 1.00 | 0.04 | 0.03 | 16-18 | - | =0.6 |