stainless steel kawat las
ER308LSI 309 316L 317L 347 410 kawat las
- rincian
- Spesifikasi
- Packing Dan Pengiriman
- keuntungan
-
|
Molde
|
standar
|
Deposit Komposisi
|
properti mekanik
|
|
|
AWS
|
C
|
Si
|
M N
|
cr
|
Ni
|
Mo
|
S.P
|
rm(MPa)
|
A5(%)
|
|
LA307
|
E307T0-1
E307T0-4
|
0.09
|
0.6
|
4.25
|
19.47
|
1.15
|
1.3
|
≤0.03
|
613
|
46
|
|
LA308L
|
E308LT1-1
E308LT1-4
|
0.028
|
0.69
|
1.26
|
20.27
|
10.82
|
|
≤0.03
|
553
|
43
|
|
LA309L
|
E309LT0-1
E309LT0-4
|
0.030
|
0.59
|
1.21
|
23.11
|
13.56
|
0.04
|
≤0.03
|
557
|
42
|
|
LA309Mo
|
E309LoMoT0-1
E309LoMot0-4
|
0.027
|
0.71
|
1.17
|
23.68
|
14.86
|
2.49
|
≤0.03
|
541
|
35
|
|
LA316L
|
E316LT0-1
E316LT0-4
|
0.029
|
0.57
|
1.33
|
18.35
|
12.49
|
2.42
|
≤0.03
|
516
|
44
|
-
|
ER308LSI 309 316L 317L 347 410 kawat las
|
|
Merek
|
(mm)
diameter
|
Gas perisai
|
Komposisi kimia dari Deposit Logam(%)
|
|
C
|
Si
|
M N
|
P
|
S
|
cr
|
Ni
|
Mo
|
cu
|
|
ER308
|
0.6-4.0
|
Ar +
-2%CO2
|
0.08
|
0.3-0.65
|
1.0-2.5
|
0.03
|
0.03
|
19.5-22.0
|
9.0
-11.0
|
0.75
|
0.75
|
|
ER308L
|
0.6-4.0
|
Ar +
-2%CO2
|
0.03
|
0.3-0.65
|
1.0-2.5
|
0.03
|
0.03
|
19.5-22.0
|
9.0
-11.0
|
0.75
|
0.75
|
|
ER308LSI
|
0.6-4.0
|
Ar +
-2%CO2
|
0.03
|
0.65-1.0
|
1.0-2.5
|
0.03
|
0.03
|
19.5-22.0
|
9.0
-11.0
|
0.75
|
0.75
|
|
ER309
|
0.6-4.0
|
Ar +
-2%CO2
|
0.12
|
0.3-0.65
|
1.0-2.5
|
0.03
|
0.03
|
23.0-25.0
|
12.0
-14.0
|
0.75
|
0.75
|
|
ER309L
|
0.6-4.0
|
Ar +
-2%CO2
|
0.03
|
0.3-0.65
|
1.0-2.5
|
0.03
|
0.03
|
23.0-25.0
|
12.0
-14.0
|
0.75
|
0.75
|
|
ER310
|
0.6-4.0
|
Ar +
-2%CO2
|
0.08-0.15
|
03-0.65
|
1.0-2.5
|
0.03
|
0.03
|
25.0-28.0
|
20.0
-22.5
|
0.75
|
0.75
|
|
ER312
|
0.6-4.0
|
Ar +
-2%CO2
|
0.15
|
0.3-0.62
|
1.0-2.5
|
0.03
|
0.03
|
28.0-32.0
|
8.0
-10.5
|
0.75
|
0.75
|
|
ER316
|
0.6-4.0
|
Ar +
-2%CO2
|
0.08
|
0.3-0.65
|
1.0-2.5
|
0.03
|
0.03
|
18.0-20.0
|
11.0
-14.0
|
2.0-3.0
|
0.75
|
|
ER316L
|
0.6-4.0
|
Ar +
-2%CO2
|
0.03
|
0.3-0.65
|
1.0-2.5
|
0.03
|
0.03
|
18.0-20.0
|
11.0
-14.0
|
2.0-3.0
|
0.75
|
|
ER316LSI
|
0.6-4.0
|
Ar +
-2%CO2
|
0.03
|
0.65-1.0
|
1.0-2.5
|
0.03
|
0.03
|
18.0-20.0
|
11.4
-14.0
|
2.0-3.0
|
0.75
|
|
ER410
|
0.6-4.0
|
Ar +
-2%CO2
|
0.12
|
0.5
|
0.6
|
0.03
|
0.03
|
11.5-13.5
|
0.6
|
0.75
|
0.75
|
|
ER430
|
0.6-4.0
|
Ar +
-2%CO2
|
0.1
|
0.5
|
0.6
|
0.03
|
0.03
|
15.5-17.0
|
0.6
|
0.75
|
0.75
|
Komposisi kimia dari logam diendapkan
|
C
|
Si
|
M N
|
cr
|
Ni
|
S
|
P
|
Mo
|
cu
|
|
≤0.08
|
0.30~ 0.65
|
1.00~
|
19.00~ 22.00
|
9.0~ 11.0
|
≤0.03
|
≤0.03
|
≤0.75
|
≤0.75
|
Sifat mekanik logam diendapkan
|
Daya tarik
|
elongasi tertentu
|
|
MPa
|
%
|
|
570~ 610
|
36~ 42
|
-
ER308LSI 309 316L 317L 347 410 kawat las:
(1)MIG / MAG Stainless steel otomatis kawat las
1)1kg per spool:D100 luar diameter 100mm, diameter dalam dari spool lubang adalah 15mm, tingginya 38mm
2)5kg per spool:D200 luar diameter 200mm, diameter dalam dari spool lubang adalah 54mm, tingginya 45mm
3)12.5kg per spool dan 15kg per spool:D300 luar diameter 300mm adalah, diameter dalam dari spool lubang adalah 52mm, tingginya 90mm
(2)TIG stainless steel kawat las
panjang dipotong 1000mm, packing batin 5kg per kasus plastik, luar kemasan adalah kasus kayu. (kemasan di drum, 1m / line,5kg/drum,10kg / drum). Semua spool dan ukuran drum yang tersedia.
-
1) Kecepatan transportasi cepat
2) Kualitas tinggi,kuantitas dengan perlakuan
3) Produk yang disertifikasi oleh ISO9001:2008 kualitas sistem otentikasi.
4) Perusahaan baja stainless terkenal di Cina dan luar negeri.
5) Kemampuan yang kuat untuk memasok
6) Bermerek stainless steel
7) Lebih dari 200 pola
8) harga bawah
9) Kualitas handal dan pelayanan
10) Spesifikasi pembeli diterima
11) berpengalaman R & D Department