Kout deskripsyon:
| Espesifikasyon nan tiyo asye pur poli: |
| 1. pwodwi | Asye pur soude tiyo |
| 2. Materyèl | 201,202,301,302,304,309,310s, 316L, 321,347,410,430,409LetC. |
| 3. estanda | ASTM, ASME, DIN, EN, ISO, JIS, GOST, ETC. |
| 4. ranje gwosè | OD: Soti nan 6mm a 1219mm (NPS soti nan 1/8 "a 40") |
| WT: soti nan 0.7mm 38mm (orè soti nan 5s xxs) | |
| Longè: ranje longè oswa un-ranje longè, max 30meters | |
| 5. pwodwi pwosesis | soude, cho koube; rezistans soude; tèmik ekspansyon elatriye. |
| 6. sifas | 2b, marinated, 180g, 320g, saten, felur, 400g, 500g, 600g |
| , 800g, glas fini | |
| 7. Marking | Saky, klas, san pwoblèm, estanda, gwosè, chalè pa gen okenn. |
| 8. pake | Offres ak twal ki enpèmeyab deyò. |
| oswa bwat playwoud. | |
| 9. longè | 5.8m, 6m, 12m oswa jan sa nesesè |
| Pwopriyete tipik mekanik pou 304 alyaj asye pur: |
| Egalize | Fòs rupture (MPa) | Fòs konpresyon (MPa) | Prèv estrès 0.2% (MPa) | Elongasyon A5 (%) | Dite Rockwell B |
| 304 | 520-720 | 210 | 210 | 45 min | 92 |
| 304L | 500-670 | 200 | 45 min | ||
| 304h | 520-720 | 210 | 45min |
| Klas nan tiyo asye pur poli: |
| Lèt | Egalize | Egalize | Eleman chimik % | ||||
| Austenitik asye pur | C | Cr | Ni | Mn | |||
| 201 | 1cr17mn6ni5n | 0.15 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | ||
| 201L | 03cr17mn6ni5n | 0.030 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | ||
| 202 | 1cr18mn8ni5n | 0.15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | ||
| 204 | 03cr16mn8ni2n | 0.030 | 15.00-17.00 | 1.50-3.50 | 7.00-9.00 | ||
| 1cr18mn10ni5mo3n | 0.10 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 | |||
| 2cr13mn9ni4 | 0.15-0.25 | 12.00-14.00 | 3.70-5.00 | 8.00-10.00 | |||
| 2cr15mn15ni2n | 0.15-0.25 | 14.00-16.00 | 1.50-3.00 | 14.00-16.00 | |||
| 1cr18mn10ni5mo3n | 0.15 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 | |||
| 301 | 1cr17ni7 | 0.15 | 16.00-18.00 | 6.00-8.00 | 2.00 | ||
| 302 | 1cr18ni9 | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | ||
| 303 | Y1cr18ni9 | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | ||
| 303se | Y1cr18ni9se | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | ||
| 304 | 0cr18ni9 | 0.07 | 17.00-19.00 | 8.00-10.00 | 2.00 | ||
| 304L | 00cr19Ni10 | 0.030 | 18.00-20.00 | 8.00-10.00 | 2.00 | ||
| 304N1 | 0cr19ni9n | 0.08 | 18.00-20.00 | 7.00-10.50 | 2.00 | ||
| 304N2 | 0cr18ni10nbn | 0.08 | 18.00-20.00 | 7.50-10.50 | 2.00 | ||
| 304ln | 00Cr18NI10N | 0.030 | 17.00-19.00 | 8.50-11.50 | 2.00 | ||
| 305 | 1cr18ni12 | 0.12 | 17.00-19.00 | 10.50-13.00 | 2.00 | ||
| 309s | 0cr23ni13 | 0.08 | 22.00-24.00 | 12.00-15.00 | 2.00 | ||
| 310s | 0cr25ni20 | 0.08 | 24.00-26.00 | 19.00-22.00 | 2.00 | ||
| 316 | 0cr17ni12mo2 | 0.08 | 16.00-18.50 | 10.00-14.00 | 2.00 | ||
| 1cr18ni12mo2ti6) | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 | |||
| 0cr18ni12mo2ti | 0.08 | 16.00-19.00 | 11.00-14.00 | 2.00 | |||
| 316L | 00cr17ni14mo2 | 0.030 | 16.00-18.00 | 12.00-15.00 | 2.00 | ||
| 316n | 0cr17ni12mo2n | 0.08 | 16.00-18.00 | 10.00-14.00 | 2.00 | ||
| 316n | 00cr17ni13mo2n | 0.030 | 16.00-18.50 | 10.50-14.50 | 2.00 | ||
| 316J1 | 0cr18ni12mo2cu2 | 0.08 | 17.00-19.00 | 10.00-14.50 | 2.00 | ||
| 316J1L | 00cr18NI14MO2CU2 | 0.030 | 17.00-19.00 | 12.00-16.00 | 2.00 | ||
| 317 | 0Cr19Ni13MO3 | 0.12 | 18.00-20.00 | 11.00-15.00 | 2.00 | ||
| 317L | 00cr19Ni13MO3 | 0.08 | 18.00-20.00 | 11.00-15.00 | 2.00 | ||
| 1cr18ni12mo3ti6 | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 | |||
| 0cr18ni12mo3ti | 0.08 | 16.00-19.00 | 11.00-14.00 | 2.00 | |||
| 317J1 | 0cr18ni16mo5 | 0.040 | 16.00-19.00 | 15.00-17.00 | 2.00 | ||
| 321 | 1cr18ni9ti6 | 0.12 | 17.00-19.00 | 8.00-11.00 | 2.00 | ||
| 0cr18ni10ti | 0.08 | 17.00-19.00 | 9.00-12.00 | 2.00 | |||
| 347 | 0Cr18NI11NB | 0.08 | 17.00-19.00 | 9.00-13.00 | 2.00 | ||
| XM7 | 0cr18ni9cu3 | 0.08 | 17.00-19.00 | 8.50-10.50 | 2.00 | ||
| XM15J1 | 0cr18ni13si4 | 0.08 | 15.00-20.00 | 11.50-15.00 | 2.00 | ||
| Ustenit Ferit asye pur | 329J1 | 0cr26ni5mo2 | 0.08 | 23.00-28.00 | 3.00-6.00 | 1.50 | 0.035 | 0.030 | 1.00-3.00 | 1.00 | - | - | 2) |
| 1cr18ni11si4alti | 0.10-0.18 | 17.50-19.50 | 10. --120 .. | 0.80 | 0.035 | 0.030 | - | 3.40-4.00 | - | - | Al 0.10-0.30; Ti 0.40-0.70 | ||
| 00cr18ni5mosi2 | 0.030 | 18.00-19.50 | 4.50-5.50 | 1.00-2.00 | 0.035 | 0.030 | 2.50-3.00 | 1.30-2.00 | - | - | - | ||
| Ferit asye pur | 405 | 0cr13al | 0.08 | 11.50-14.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | Al 0.10-0.30 |
| 410L | 00cr12 | 0.030 | 11.00-13.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
| 430 | 1cr17 | 0.12 | 16.00-18.00 | 3) | 1.25 | 0.035 | 0.030 | - | 0.75 | - | - | - | |
| 430f | Y1cr17 | 0.12 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
| 434 | 1cr17mo | 0.12 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.030 | 0.75-1.25 | 1.00 | - | - | - | |
| 447J1 | 00CR30MO2 | 0.010 | 28.50-32.00 | - | 0.40 | 0.035 | 0.030 | 1.50-2.50 | 0.40 | - | 0.015 | - | |
| XM27 | 00cr27mo | 0.010 | 25.00-27.50 | - | 0.40 | 0.035 | 0.030 | 0.75-1.50 | 0.40 | - | 0.015 | - |
| Martensite asye pur | 403 | 1cr12 | 0.15 | 11.50-13.00 | 3) | 1.00 | 0.035 | 0.030 | - | 0.50 | - | - | - |
| 410 | 1CR13 | 0.15 | 11.50-13.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
| 405 | 0cr13 | 0.08 | 11.50-13.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
| 416 | Y1cr13 | 0.15 | 12.00-14.00 | 3) | 1.25 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
| 410J1 | 1cr13mo | 0.08-0.18 | 11.50-14.00 | 3) | 1.00 | 0.035 | 0.030 | 0.30-0.60 | 0.60 | - | - | - | |
| 420J1 | 2Cr13 | 0.16-0.25 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
| 420J2 | 3cr13 | 0.26-0.35 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
| 420F | Y3cr13 | 0.26-0.40 | 12.00-14.00 | 3) | 1.25 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
| 3cr13mo | 0.28-0.35 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | 0.50-1.00 | 0.80 | - | - | - | ||
| 4cr13 | 0.36-0.45 | 12.00-14.00 | 3) | 0.80 | 0.035 | 0.030 | - | 0.60 | - | - | - | ||
| 431 | 1cr17ni2 | 0.11-0.17 | 16.00-18.00 | 1.50-2.50 | 0.80 | 0.035 | 0.030 | - | 0.80 | - | - | - | |
| 440A | 7cr17 | 0.60-0.75 | 16.00-18.00 | 3) | 1.00 | 0.035 |