| Nerjaveèi anwoulman anwoulman One Stop Showcase Sèvis: |
| 430 fèy asye purKonpozisyon chimik ak pwopriyete mekanik: |
| C% | Si% | Mn% | P% | S% | Cr% | Ni% | N% | Mo% | Ti% |
| 0.12 | 1.00 | 1.00 | 0.040 | 0.030 | 16.0-18.0 | 0.75 | - | - | - |
| T*s | Y*s | Rez nan | Elongasyon | |
| (MPA) | (MPA) | Mwatye | HB | (%) |
| 520 | 205 | - | - | 40 |
| Frèt woule430 fèy asye pur: |
1. Klas: 200 & 300 Seri
200 Seriers: 201,202, J4
300 Seriers: 301, 304, 304L, 321, 316L, 309, 310s
2. Creole: JIS, ASTM, AISI, GB, DIN, EN, Anjeneral nou itilize ASTM ak GB Creole
3. Epesè: 0.14mm-3.0mm
4. Lajè: jan yo mande
5. Sifas: 2B fini, BA fini
6. Dite: mou, 1/4h, 1/2h, FH
7. Tolerans epesè: +/- 0.02mm
8. Lajè tolerans: +/- 10mm (Mill Edge)
| Plis klas nan 430 SS Fèy: |
| Lèt | Egalize | Egalize | Eleman chimik % | |||
| Austenitik asye pur | C | Cr | Ni | Mn | ||
| 201 | 1cr17mn6ni5n | 0.15 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | |
| 201L | 03cr17mn6ni5n | 0.030 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | |
| 202 | 1cr18mn8ni5n | 0.15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | |
| 204 | 03cr16mn8ni2n | 0.030 | 15.00-17.00 | 1.50-3.50 | 7.00-9.00 | |
| 1cr18mn10ni5mo3n | 0.10 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 | ||
| 2cr13mn9ni4 | 0.15-0.25 | 12.00-14.00 | 3.70-5.00 | 8.00-10.00 | ||
| 2cr15mn15ni2n | 0.15-0.25 | 14.00-16.00 | 1.50-3.00 | 14.00-16.00 | ||
| 1cr18mn10ni5mo3n | 0.15 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 | ||
| 301 | 1cr17ni7 | 0.15 | 16.00-18.00 | 6.00-8.00 | 2.00 | |
| 302 | 1cr18ni9 | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | |
| 303 | Y1cr18ni9 | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | |
| 303se | Y1cr18ni9se | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | |
| 304 | 0cr18ni9 | 0.07 | 17.00-19.00 | 8.00-10.00 | 2.00 | |
| 304L | 00cr19Ni10 | 0.030 | 18.00-20.00 | 8.00-10.00 | 2.00 | |
| 304N1 | 0cr19ni9n | 0.08 | 18.00-20.00 | 7.00-10.50 | 2.00 | |
| 304N2 | 0cr18ni10nbn | 0.08 | 18.00-20.00 | 7.50-10.50 | 2.00 | |
| 304ln | 00Cr18NI10N | 0.030 | 17.00-19.00 | 8.50-11.50 | 2.00 | |
| 305 | 1cr18ni12 | 0.12 | 17.00-19.00 | 10.50-13.00 | 2.00 | |
| 309s | 0cr23ni13 | 0.08 | 22.00-24.00 | 12.00-15.00 | 2.00 | |
| 310s | 0cr25ni20 | 0.08 | 24.00-26.00 | 19.00-22.00 | 2.00 | |
| 316 | 0cr17ni12mo2 | 0.08 | 16.00-18.50 | 10.00-14.00 | 2.00 | |
| 1cr18ni12mo2ti6) | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 | ||
| 0cr18ni12mo2ti | 0.08 | 16.00-19.00 | 11.00-14.00 | 2.00 | ||
| 316L | 00cr17ni14mo2 | 0.030 | 16.00-18.00 | 12.00-15.00 | 2.00 | |
| 316n | 0cr17ni12mo2n | 0.08 | 16.00-18.00 | 10.00-14.00 | 2.00 | |
| 316n | 00cr17ni13mo2n | 0.030 | 16.00-18.50 | 10.50-14.50 | 2.00 | |
| 316J1 | 0cr18ni12mo2cu2 | 0.08 | 17.00-19.00 | 10.00-14.50 | 2.00 | |
| 316J1L | 00cr18NI14MO2CU2 | 0.030 | 17.00-19.00 | 12.00-16.00 | 2.00 | |
| 317 | 0Cr19Ni13MO3 | 0.12 | 18.00-20.00 | 11.00-15.00 | 2.00 | |
| 317L | 00cr19Ni13MO3 | 0.08 | 18.00-20.00 | 11.00-15.00 | 2.00 | |
| 1cr18ni12mo3ti6 | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 | ||
| 0cr18ni12mo3ti | 0.08 | 16.00-19.00 | 11.00-14.00 | 2.00 | ||
| 317J1 | 0cr18ni16mo5 | 0.040 | 16.00-19.00 | 15.00-17.00 | 2.00 | |
| 321 | 1cr18ni9ti6 | 0.12 | 17.00-19.00 | 8.00-11.00 | 2.00 | |
| 0cr18ni10ti | 0.08 | 17.00-19.00 | 9.00-12.00 | 2.00 | ||
| 347 | 0Cr18NI11NB | 0.08 | 17.00-19.00 | 9.00-13.00 | 2.00 | |
| XM7 | 0cr18ni9cu3 | 0.08 | 17.00-19.00 | 8.50-10.50 | 2.00 | |
| XM15J1 | 0cr18ni13si4 | 0.08 | 15.00-20.00 | 11.50-15.00 | 2.00 | |