Deskripsyon kout:
304 Nerjaveèi asye wonn tiyo, oswa EN 1.4301 tiyo inox tib, X6CRNI18-10 Nerjaveèi tib wonn
| Konpozisyon chimik: |
| Klas | C% | Si% | Mn% | P% | S% | Cr% | Ni% | Mo% | Cu% |
| 304 | 0.08 | 1.0 | 2.0 | 0.045 | 0.03 | 18.0-20.0 | 8.0-10.0 | - | – |
| Espesifikasyon nan304 tiyo asye pur: |
| Non | 304 tiyo asye pur, 304 tib asye pur 304 tib Nerjaveèi 304 ss tib 304 tiyo echapman asye pur ss 304 tiyo 304 ss tiyo ss 304 lis pri tiyo tiyo ss 304 ss 304 gwosè tiyo Nerjaveèi asye 304 tiyo 304 tiyo Nerjaveèi 304 ss tiyo 304 tib Nerjaveèi 304 gwosè tib asye pur Nerjaveèi asye 304 tib Nerjaveèi asye 304 gwosè tiyo 304 tiyo echapman pur tiyo asye pur klas 304 tib inox 304L tib inox 304 | |||||
| Estanda | GB/T14975, GB/T14976, GB13296-91, GB9948, ASTM A312, ASTM A213, | |||||
| ASTM A269, ASTM A511, JIS349, DIN17456, ASTM A789, ASTM A790, DIN17456, DIN17458, EN10216-5, JIS3459, GOST 9941-81 | ||||||
| Materyèl Klas | 304, 304L, 316, 316L, 321, 321H, 310S, 347H, 309.317.0cr18N9, 0Cr25Ni20 | |||||
| 00Cr19Ni10,08X18H10T,S31803,S31500,S32750 | ||||||
| Dyamèt Eksteryè | 6mm rive 1219mm | |||||
| Epesè | 0.8mm - 40mm | |||||
| Gwosè | OD (6-1219) mm x (0.9-40)mm x MAX 13000mm | |||||
| Tolerans | anba estanda ASTM A312 A269 A213 | |||||
| anba estanda ASTM A312 A269 A213 | ||||||
| anba estanda ASTM A312 A269 A213 | ||||||
| Sifas | 180G, 320G Saten / Hairline (Fini Mat, Bwòs, Fini Mat) | |||||
| PICKLING & RECUIT | ||||||
| Aplikasyon | Transpò likid ak gaz, dekorasyon, konstriksyon, ekipman medikal, avyasyon, | |||||
| chodyè chalè-changeur ak lòt jaden | ||||||
| Tès | Tès plat, tès idrostatik, tès korozyon entègranulè, tès plat, tès Eddy, elatriye. | |||||
| Customized | lòt espesifikasyon selon kondisyon kliyan yo | |||||
| Tan livrezon | jiska kantite lòd la | |||||
| Anbalaj | Fourni ak sache plastik knitted, ka an bwa oswa selon demann kliyan yo. | |||||
| Pwopriyete mekanik | Atik materyèl | 304 | 304L | 304 | 316L | Top Teknoloji |
| Fòs rupture | 520 | 485 | 520 | 485 | ||
| Sede fòs | 205 | 170 | 205 | 170 | ||
| Ekstansyon | 35% | 35% | 35% | 35% | ||
| Dite (HV) | <90 | <90 | <90 | <90 | ||
| Klas | Konpozisyon chimik (%) | |||||||
| C | Si | Mn | P | S | Ni | Cr | Mo | |
| 201 | 0.15 | 1.00 | 5.5 ~ 7.5 | 0.060 | 0.030 | 3.50 ~ 5.50 | 16.00 ~ 18.00 | |
| 301 | 0.15 | 1.00 | 2.00 | 0.045 | 0.030 | 6.00 ~ 8.00 | 16.00 ~ 18.00 | |
| 302 | 0.15 | 1.00 | 2.00 | 0.045 | 0.030 | 8.00 ~ 10.00 | 17.00 ~ 19.00 | |
| 304 | 0.08 | 1.00 | 2.00 | 0.045 | 0.030 | 8.00 ~ 10.50 | 18.00 ~ 20.00 | - |
| 304L | 0.030 | 1.00 | 2.00 | 0.045 | 0.030 | 9.00 ~ 13.50 | 18.00 ~ 20.00 | - |
| 316 | 0.045 | 1.00 | 2.00 | 0.045 | 0.030 | 10.00 ~ 14.00 | 10.00 ~ 18.00 | 2.00 ~ 3.00 |
| 316L | 0.030 | 1.00 | 2.00 | 0.045 | 0.030 | 12.00 ~ 15.00 | 16.00 ~ 18.00 | 2.00 ~ 3.00 |
| 430 | 0.12 | 0.75 | 1.00 | 0.040 | 0.030 | 0.60 | 16.00 ~ 18.00 | - |
| 430A | 0.06 | 0.50 | 0.50 | 0.030 | 0.50 | 0.25 | 14.00 ~ 17.00 | - |
| Pwodwi | Materyèl nan tiyo asye pur | Estanda | Espesifikasyon (mm) | Aplikasyon |
| Tiyo asye pur | 06Cr19Ni10 | GB/T14975-2002 | 6-630 * 0.5-60 | Nikleyè, chimik, lwil oliv, transpò Chodyè, echanjeur chalè, kondansasyon, elatriye |
| 00Cr19Ni10 | GB/T14976-2002 | |||
| 00Cr25Ni20 | GB13296-2007 | |||
| 06Cr17Ni12Mo2 | ASTM A213 | |||
| 00Cr17Ni14Mo2 | ASTM A269 | |||
| 1Cr18Ni9Ti | ASTM A312 | |||
| 0Cr18Ni10Ti | JIS G3459 | |||
| 0Cr18Ni11Nb | DIN 17458 |
Avantaj:
1.Wooden ka pake ki se fò ak apwopriye pou transpò lanmè se metòd prensipal nou an pake tiyo yo. Ak metòd la anbalaj ekonomik tankou chaje nan offres tou akeyi pa kèk kliyan.
2.Kontwòl tolerans nou itilize se D4/T4 (+/-0.1mm) sou tou de anndan kou deyò Dyamèt ak epesè miray la, ki pi wo pase estanda entènasyonal ASTM, DIN.
3.Kondisyon sifas la se youn nan avantaj prensipal nou an: yo nan lòd yo satisfè kondisyon diferan pou kondisyon sifas, nou gen sifas rkwir ak marinated, sifas rkwir klere, OD sifas poli, OD & ID sifas poli elatriye.
4.Nan lòd pou kenbe sifas andedan tiyo a pwòp epi fè li gratis nan ebavurage, konpayi nou an devlope teknoloji inik ak espesyal - Eponj Lave ak presyon ki wo.8.Nou gen sèvis konplè apre-sale fè fas ak pwoblèm yo nan tan. .