Stainless hlau t tshooj
Cov lus piav qhia luv luv:
Stainless hlau t bar, t Seem lossis Tee profile nrog qeb xyoo 201,304,304L, 316,316L, 311,310s, 410,430
Cov lus qhia tshwj xeeb ntawmStainless hlau t bar: |
Lub hom phiaj | ASTM A276, A484, A479, A580, A582, JIS G4303, DIN 1654-5, DIN 1646, GB / T 1220 |
Khoom | 201,202,205, XM-19 thiab lwm yam. 301,304,304L, 304h, 309s, 310s, 314,316L, 317,321h, 329,3430 thiab lwm yam. 409,410,416,420,430430F, 431,440 2205,2507, s31803,2203,631,15-5ph, 17-4-7PH, 904L, F51, F553MA thiab lwm yam. |
Nplaim | Ci, polishing, pickled, tev, dub, sib tsoo, zeb, daim iav, plaub hau thiab cov plaub hau |
Tej txuj ci tshiab | Khaub thuas nqus, kub dov, forged |
Cov lus qhia | raws li yuav tsum tau ua |
Kev nyiaj tau | H9, H11, H13, K9, K11, K13 lossis raws li yuav tsum tau ua |
Stainless hlau t tshooj khoom los ntawm Sakysteel: |
Qhov hnyav ntawmStainless hlau t bar |
Tus qauv | Qho hnyav | Tus qauv | Qho hnyav |
100 * 50 * 5 * 7 | 9.54 | 344 * 354 * 16 * 16 | 131 |
100 * 100 * 6 * 8 | 16 | 346 * 174 * 6 * 9 | 41.8 |
125 * 60 * 6 * 8 | 13.3 | 350 * 175 * 7 * 11 | 50 |
125 * 125 * 6.5 * 9 | 23.8 | 344 * 348 * 10 * 16 | 115 |
148 * 100 * 6 * 9 | 21.4 | 350 * 350 * 12 * 19 | 137 |
150 * 75 * 5 * 7 | 14.3 | 388 * 402 * 15 * 15 | 141 |
150 * 150 * 7 * 10 | 31.9 | 390 * 300 * 10 * 16 | 107 |
175 * 90 * 5 * 8 | 18.2 | 394 * 398 * 11 * 18 | 147 |
175 * 175 * 7.5 * 11 | 40.3 | 400 * 150 * 8 * 13 | 55.8 |
Xyoo 194 * 150 * 6 * 9 | 31,2 | 396 * 199 * 7 * 11 | 56.7 |
198 * 99 * 4.5 * 7 | 18.5 | 400 * 200 * 8 * 13 | 66 |
200 * 100 * 5.5 * 8 | 21.7 | 400 * 400 * 13 * 21 | 172 |
200 * 200 * 8 * 12 | 50.5 | 400 * 408 * 21 * 21 | 197 |
200 * 204 * 12 * 12 * 12 | 72.28 | 414 * 405 * 18 * 28 | 233 |
244 * 175 * 7 * 11 | 44.1 | 440 * 300 * 11 * 18 * 18 | 124 |
244 * 252 * 11 * 11 | 64.4 | 446 * 199 * 7 * 11 | 66.7 |
248 * 124 * 5 * 8 | 25.8 | 450 200 * 200 * 9-14 | 76.5 |
250 * 125 * 6 * 9 | 29.7 | 482 * 300 * 11 * 15 | 115 |
250 * 250 * 9 * 14 | 72.4 | 488 * 300 * 11 * 18 * 18 | 129 |
250 * 255 * 14 * 14 | 82.2 | 496 * 199 * 9 * 14 | 79.5 |
294 * 200 * 8 * 12 | 57.3 | 500 * 200 * 10 * 16 | 89.6 |
300 * 150 * 6.5 * 9 | 37.3 | 582 * 300 * 12 * 17 | 137 |
294 * 302 * 12 * 12 | 85 | 588 * 300 * 12 * 20 * 20 | 151 |
300 * 300 * 10 * 15 | 94.5 | 596 * 199 * 10 * 15 | 95.1 |
300 * 305 * 15 * 15 | 106 | 600 * 200 * 11 * 17 | 106 |
338 * 351 * 13 * 13 * 13 * 13 | 106 | 700 * 300 * 13 * 24 | 185 |
340 * 250 * 9 * 14 | 79.7 |
Ntau qib ntawmStainless hlau t bar: |
Ntaus | Teem nqi | Teem nqi | Kev Siv Tshuaj Tiv Thaiv% | ||||||||||
C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | Lwm | |||
Austenitic Stainless Hlau | 201 | 1Cr17mn6N65N | 0.15 | 16.00-18.00 | 3.505.50 | 5.50-7.50 | 0.060 | 0.030 | - | 1.00 | - | 0.25 | - |
201l | 03CR17MNN6NI5N | 0.030 | 16.00-18.00 | 3.505.50 | 5.50-7.50 | 0.060 | 0.030 | 1.00 | 0.25 | ||||
202 | 1Cr18mn8N115n | 0.15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | 0.060 | 0.030 | 1.00 | - | 0.25 | - | ||
204 | 03cr16mn8ni2n | 0.030 | 15.00-17.00 | 1.50-3.50 | 7.00-9.00 | 0.15-0.30 | |||||||
1cr18mn10ni5mo3n | 0.10 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 | 2.80-3.50 | 0.20-0.30 | |||||||
2Cr13mn9NI4 | 0.15-0.25 | 12.00-14.00 | 3.70-5.00 | 8.00-10.00 | |||||||||
2cr15mn15ni2n | 0.15-0.25 | 14.00-16.00 | 1.50-3.00 | 14.00-16.00 | 0.15-0.30 | ||||||||
1cr18mn10ni5mo3n | 0.15 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 | 0.060 | 0.030 | 2.8-3.5 | 1.00 | - | 0.20-0.30 | - | ||
301 | 1Cr17NI7 | 0.15 | 16.00-18.00 | 6.00-8.00 | 2.00 | 0.065 | 0.030 | - | 1.00 | - | - | - | |
302 | 1Cr18ni9 | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
303 | Y1cr18ni9 | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | 0.20 | 0.030 | 1) | 1.00 | - | - | - | |
303se | Y1CR18NI9SE | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | 0.20 | 0.030 | - | 1.00 | - | - | Se = 0.15 | |
304 | 0cr18ni9 | 0.07 | 17.00-19.00 | 8.00-10.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
30L | 00CR19NI | 0.030 | 18.00-20.00 | 8.00-10.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
30N1 | 0cr19NI9N | 0.08 | 18.00-20.00 | 7.00-10.50 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | 0.10-0.25 | - | |
30N2 | 0cr18ni10nbn | 0.08 | 18.00-20.00 | 7.50-10.50 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | 0.15-0.30 | Nb = 0.15 | |
Yog | 00cr18nin | 0.030 | 17.00-19.00 | 8.50-11.50 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | 0.12-0.22 | - | |
305 | 1Cr18NI12 | 0.12 | 17.00-19.00 | 10.50-13.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
309s | 0cr23ni13 | 0.08 | 22.00-24.00 | 12.00-15.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
310s | 0cr25ni20 | 0.08 | 24.00-26.00 | 19.00-22.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
316 | 0cr17ni12mo2 | 0.08 | 16.00-18.50 | 10.00-14.00 | 2.00 | 0.035 | 0.030 | 2.00-3.00 | 1.00 | - | - | - | |
1cr18ni12mo2ti6) | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 | 0.035 | 0.030 | 1.80-2.50 | 1.00 | - | - | Ti5 (C% -0.02) ~ 0.08 | ||
0cr18ni12mo2ti | 0.08 | 16.00-19.00 | 11.00-14.00 | 2.00 | 0.035 | 0.030 | 1.80-2.50 | 1.00 | - | - | TI5 * C% -0.70 | ||
316L | 00cr17ni14MO2 | 0.030 | 16.00-18.00 | 12.00-15.00 | 2.00 | 0.035 | 0.030 | 2.00-3.00 | 1.00 | - | - | - | |
316N | 0cr17ni12mo2n | 0.08 | 16.00-18.00 | 10.00-14.00 | 2.00 | 0.035 | 0.030 | 2.00-3.00 | 1.00 | - | 0.10-0.22 | - | |
316N | 00CR17NIN | 0.030 | 16.00-18.50 | 10.50-14.50 | 2.00 | 0.035 | 0.030 | 2.00-3.00 | 1.00 | - | 0.12-0.22 | - | |
316M11 | 0cr18ni12mo2cu2 | 0.08 | 17.00-19.00 | 10.00-14.50 | 2.00 | 0.035 | 0.030 | 1.20-2.75 | 1.00 | 1.00-2.50 | - | - | |
316J1l | 00cr18mo2cu2 | 0.030 | 17.00-19.00 | 12.00-16.00 | 2.00 | 0.035 | 0.030 | 1.20-2.75 | 1.00 | 1.00-2.50 | - | - | |
317 | 0cr19ni13mo3 | 0.12 | 18.00-20.00 | 11.00-15.00 | 2.00 | 0.035 | 0.030 | 3.00-4.00 | 1.00 | - | - | - | |
317L | 00CR19NI3MO3 | 0.08 | 18.00-20.00 | 11.00-15.00 | 2.00 | 0.035 | 0.030 | 3.00-4.00 | 1.00 | - | - | - | |
1cr18ni12mo3ti6 | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 | 0.035 | 0.030 | 2.50-3.50 | 1.00 | - | - | Ti5 (C% -0.02) ~ 0.08 | ||
0cr18ni12mo3ti | 0.08 | 16.00-19.00 | 11.00-14.00 | 2.00 | 0.035 | 0.030 | 2.50-3.50 | 1.00 | - | - | TI5 * C% -0.70 | ||
3171 | 0cr18ni16Mo5 | 0.040 | 16.00-19.00 | 15.00-17.00 | 2.00 | 0.035 | 0.030 | 4.00-6.00 | 1.00 | - | - | - | |
321 | 1Cr18NI6 | 0.12 | 17.00-19.00 | 8.00-11.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | Ti5 (C% -0.02) ~ 0.08 | |
0cr18ni10Ti | 0.08 | 17.00-19.00 | 9.00-12.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | Ti = 5 * c% | ||
347 | 0cr18ni11nb | 0.08 | 17.00-19.00 | 9.00-13.00 | 2.00 | 0.035 | 0.030 | - | 1.00 | - | - | Nb = 10 * c% | |
XM7 | 0cr18ni9CU3 | 0.08 | 17.00-19.00 | 8.50-10.50 | 2.00 | 0.035 | 0.030 | - | 1.00 | 3.00-4.00 | - | - | |
XM15J1 | 0crro8ni13si4 | 0.08 | 15.00-20.00 | 11.50-15.00 | 2.00 | 0.035 | 0.030 | - | 3.00-5.00 | - | - | 2) | |
Ib qho kev ua siab ntev | 329J1 | 0cr26ni5mo2 | 0.08 | 23.00-28.00 | 3.00-6.00 | 1.50 | 0.035 | 0.030 | 1.00-3.00 | 1.00 | - | - | 2) |
| | 1cr18ni11sifti | 0.10-0.18 | 17.50-19.50 | 10.-120 .. | 0.80 | 0.035 | 0.030 | - | 3.40-4.00 | - | - | Al 0.10-0.30; TI 0.40-0.70 | |
Ferrite Stainless Hlau | 00cr18mosi2 | 0.030 | 18.00-19.50 | 4.50-5.50 | 1.00-2.00 | 0.035 | 0.030 | 2.50-3.00 | 1.30-2.00 | - | - | - | |
Ferrite Stainless Hlau | 405 | 0C13al | 0.08 | 11.50-14.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | Al 0.10-0.30 |
410L | C00CR12 | 0.030 | 11.00-13.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
430 | 77 | 0.12 | 16.00-18.00 | 3) | 1.25 | 0.035 | 0.030 | - | 0.75 | - | - | - | |
430f | Y1CR17 | 0.12 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
434 | 1cr17mo | 0.12 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.030 | 0.75-1.25 | 1.00 | - | - | - | |
447J1 | 00CR30Mo2 | 0.010 | 28.50-32.00 | - | 0.40 | 0.035 | 0.030 | 1.50-2.50 | 0.40 | - | = 0.015 | - | |
XM27 | 00cr27mo | 0.010 | 25.00-27.50 | - | 0.40 | 0.035 | 0.030 | 0.75-1.50 | 0.40 | - | = 0.015 | - | |
MARTENSITE Stainless Hlau | 403 | 1Cr12 | 0.15 | 11.50-13.00 | 3) | 1.00 | 0.035 | 0.030 | - | 0.50 | - | - | - |
410 | 33 | 0.15 | 11.50-13.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
405 | 0C13 | 0.08 | 11.50-13.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
416 | Y1cr13 | 0.15 | 12.00-14.00 | 3) | 1.25 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
410J1 | 1C13mo | 0.08-0.18 | 11.50-14.00 | 3) | 1.00 | 0.035 | 0.030 | 0.30-0.60 | 0.60 | - | - | - | |
420J1 | 23 | 0.16-0.25 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
420J2 | PC13 | 0.26-0.35 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
420f | Y3cr13 | 0.26-0.40 | 12.00-14.00 | 3) | 1.25 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
PC13mo | 0.28-0.35 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | 0.50-1.00 | 0.80 | - | - | - | ||
4C3 | 0.36-0.45 | 12.00-14.00 | 3) | 0.80 | 0.035 | 0.030 | - | 0.60 | - | - | - | ||
431 | 1Cr17NI2 | 0.11-0.17 | 16.00-18.00 | 1.50-2.50 | 0.80 | 0.035 | 0.030 | - | 0.80 | - | - | - | |
440A | 7CR17 | 0.60-0.75 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.030 | 4) | 1.00 | - | - | - | |
440B | 8 | 0.75-0.95 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.030 | 4) | 1.00 | - | - | - | |
9CR18 | 0.90-1.00 | 17.00-19.00 | 3) | 0.80 | 0.035 | 0.030 | 4) | 0.80 | - | - | - | ||
440C | Nram mog | 0.95-1.20 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.030 | 4) | 1.00 | - | - | - | |
440F | Y11CR17 | 0.95-1.20 | 16.00-18.00 | 3) | 1.25 | 0.035 | 0.15 | 4) | 1.00 | - | - | - | |
9CR18MO | 0.95-1.10 | 16.00-18.00 | 3) | 0.80 | 0.035 | 0.030 | 0.40-0.70 | 0.80 | - | - | - | ||
9Cr128mov | 0.85-0.95 | 17.00-19.00 | 3) | 0.80 | 0.035 | 0.030 | 1.00-1.30 | 0.80 | - | - | V0.07-0.12 | ||
Ph cov hlau stainless | 630 | 0cr17ni4cu4nb | 0.07 | 15.50-17.50 | 6.50-7.50 | 1.00 | 0.035 | 0.030 | - | 1.00 | 3.00-5.00 | - | Nb 0.15-0.45 |
631 | 0cr17ni7al | 0.09 | 16.00-18.00 | 6.50-7.50 | 1.00 | 0.035 | 0.030 | - | 1.00 | 0.50 | - | Al 0.75-1.50 |