Cov lus piav qhia luv luv:
| Stainless hlau Coils ib qho chaw cia khoom Showcase: |
| 430 stainless hlau ntawvTshuaj lom neeg muaj pes tsawg leeg tshuaj thiab cov neeg kho tshuab: |
| C% | SI% | Mn% | P% | S% | Cr% | Ni% | N% | Mo% | Ti% |
| 0.12 | 1.00 | 1.00 | 0.040 | 0.030 | 16.0-18.0 | 0.75 | - | - | - |
| T * s | Y * s | Kev nyuaj | Elongation | |
| (MPa) | (MPa) | Hrb | HB | (%) |
| 520 | 205 | - | - | 40 |
| Cold Rolled430 Cov Ntawv Hlau Stainless Hlau: |
1. Qib: 200 & 300 series
200 tus nab: 201,202, j4
300 fab: 301, 304, 304L, 321, 316L, 309, 310s
2. Tus Qauv: JIS, ASTM, AISI, GB, DIN, EN, PEB SIV SIV ASTM THIAB GB Txuj Ci
3. Thickness: 0.14mm-3.0mm
4. Qhov dav: Raws li yuav tsum tau
5. Nto: 2b tiav lawm, BA tiav
6. Hardness: Mos, 1 / 4H, 1 / 2H, FH
7. Thickness kam zam: +/- 0.02mm
8. Qhov Dav Deev: +/- 10mm (Zeb Ntug)
| Ntau ntau ntau ntawm 430 SS daim ntawv: |
| Ntaus | Teem nqi | Teem nqi | Kev Siv Tshuaj Tiv Thaiv% | |||
| Austenitic Stainless Hlau | C | Cr | Ni | Mn | ||
| 201 | 1Cr17mn6N65N | 0.15 | 16.00-18.00 | 3.505.50 | 5.50-7.50 | |
| 201l | 03CR17MNN6NI5N | 0.030 | 16.00-18.00 | 3.505.50 | 5.50-7.50 | |
| 202 | 1Cr18mn8N115n | 0.15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | |
| 204 | 03cr16mn8ni2n | 0.030 | 15.00-17.00 | 1.50-3.50 | 7.00-9.00 | |
| 1cr18mn10ni5mo3n | 0.10 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 | ||
| 2Cr13mn9NI4 | 0.15-0.25 | 12.00-14.00 | 3.70-5.00 | 8.00-10.00 | ||
| 2cr15mn15ni2n | 0.15-0.25 | 14.00-16.00 | 1.50-3.00 | 14.00-16.00 | ||
| 1cr18mn10ni5mo3n | 0.15 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 | ||
| 301 | 1Cr17NI7 | 0.15 | 16.00-18.00 | 6.00-8.00 | 2.00 | |
| 302 | 1Cr18ni9 | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | |
| 303 | Y1cr18ni9 | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | |
| 303se | Y1CR18NI9SE | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | |
| 304 | 0cr18ni9 | 0.07 | 17.00-19.00 | 8.00-10.00 | 2.00 | |
| 30L | 00CR19NI | 0.030 | 18.00-20.00 | 8.00-10.00 | 2.00 | |
| 30N1 | 0cr19NI9N | 0.08 | 18.00-20.00 | 7.00-10.50 | 2.00 | |
| 30N2 | 0cr18ni10nbn | 0.08 | 18.00-20.00 | 7.50-10.50 | 2.00 | |
| Yog | 00cr18nin | 0.030 | 17.00-19.00 | 8.50-11.50 | 2.00 | |
| 305 | 1Cr18NI12 | 0.12 | 17.00-19.00 | 10.50-13.00 | 2.00 | |
| 309s | 0cr23ni13 | 0.08 | 22.00-24.00 | 12.00-15.00 | 2.00 | |
| 310s | 0cr25ni20 | 0.08 | 24.00-26.00 | 19.00-22.00 | 2.00 | |
| 316 | 0cr17ni12mo2 | 0.08 | 16.00-18.50 | 10.00-14.00 | 2.00 | |
| 1cr18ni12mo2ti6) | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 | ||
| 0cr18ni12mo2ti | 0.08 | 16.00-19.00 | 11.00-14.00 | 2.00 | ||
| 316L | 00cr17ni14MO2 | 0.030 | 16.00-18.00 | 12.00-15.00 | 2.00 | |
| 316N | 0cr17ni12mo2n | 0.08 | 16.00-18.00 | 10.00-14.00 | 2.00 | |
| 316N | 00CR17NIN | 0.030 | 16.00-18.50 | 10.50-14.50 | 2.00 | |
| 316M11 | 0cr18ni12mo2cu2 | 0.08 | 17.00-19.00 | 10.00-14.50 | 2.00 | |
| 316J1l | 00cr18mo2cu2 | 0.030 | 17.00-19.00 | 12.00-16.00 | 2.00 | |
| 317 | 0cr19ni13mo3 | 0.12 | 18.00-20.00 | 11.00-15.00 | 2.00 | |
| 317L | 00CR19NI3MO3 | 0.08 | 18.00-20.00 | 11.00-15.00 | 2.00 | |
| 1cr18ni12mo3ti6 | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 | ||
| 0cr18ni12mo3ti | 0.08 | 16.00-19.00 | 11.00-14.00 | 2.00 | ||
| 3171 | 0cr18ni16Mo5 | 0.040 | 16.00-19.00 | 15.00-17.00 | 2.00 | |
| 321 | 1Cr18NI6 | 0.12 | 17.00-19.00 | 8.00-11.00 | 2.00 | |
| 0cr18ni10Ti | 0.08 | 17.00-19.00 | 9.00-12.00 | 2.00 | ||
| 347 | 0cr18ni11nb | 0.08 | 17.00-19.00 | 9.00-13.00 | 2.00 | |
| XM7 | 0cr18ni9CU3 | 0.08 | 17.00-19.00 | 8.50-10.50 | 2.00 | |
| XM15J1 | 0crro8ni13si4 | 0.08 | 15.00-20.00 | 11.50-15.00 | 2.00 | |