    Hastelloy C-4 (UNS NO6455)

    Hastelloy C-4 Features and Applications Overview:
    The alloy is an austenitic low-carbon nickel-molybdenum-chromium alloy. The main difference between Nicrofer 6616 hMo and other alloys of similar chemical composition developed earlier is low carbon, silicon, iron and tungsten. This chemical composition provides excellent stability at 650-1040 ° C and improved resistance to intergranular corrosion, avoiding edge line corrosion susceptibility and weld HAZ corrosion under appropriate manufacturing conditions. Alloy used in flue gas desulfurization systems, pickling and acid regeneration plant, acetic acid and agricultural chemicals production, titanium dioxide production (chloride method), electrolytic plating.
    Hastelloy C-4 Similar brands:
    NS335 (China) W.Nr.2.4610 NiMo16Cr16Ti (Germany)
    Hastelloy C-4 Chemical composition:

    Alloy
    Grade

    %

    Ni

    Cr

    Fe

    Mo

    Nb

    Co

    C

    Mn

    Si

    S

    Cu

    Al

    Ti

    Hastelloy C-4

    Min

    Margin

    14.5

     

    14.0

                     

    Maximum

    17.5

    3.0

    17.0

     

    2.0

    0.009

    1.0

    0.05

    0.01

       

    0.7

    Hastelloy C-4 Physical Properties:

    Density
    g/cm3

    Melting point

    Thermal conductivity
    λ/(W/m•℃)

    Specific heat capacity
    J/kg•℃

    Elastic Modulus
    GPa

    Shear modulus
    GPa

    Resistivity
    μΩ•m

    Poisson’s ratio

    Linear expansion coefficient
    a/10-6℃-1

    8.6

    1335
    1380

    10.1(100℃)

    408

    211

     

    1.24

     

    10.9(100℃)

    Hastelloy C-4 Mechanical Properties: (minimum mechanical properties at 20 ℃):

    Heat treatment methods

    Tensile strengthσb/MPa

    Yield Strengthσp0.2/MPa

    Elongation rate σ5 /%

    Brinell hardness HBS

    Solution treatment

    690

    275

    40

     

    Hastelloy C-4 production standards:

    Standard

    Bar

    Forgings

    Plate (with) material

    Wire

    Pipe

    American Society for Testing and Materials

    ASTM B574

    ASTM B336

    ASTM B575

     

    ASTM B622
    ASTM B619
    ASTM B626

    American Aerospace Materials Technical Specification

             

    American Society of Mechanical Engineers

    ASME SB574

    ASME SB336

    ASME SB575

     

    ASTM SB622
    ASTM SB619
    ASTM SB626

    Hastelloy C-4 process performance and requirements:

    1, In the heat treatment process can not contact with sulfur, phosphorus, lead and other low melting point metal, or the alloy will become brittle, should pay attention to remove such as marking paint, temperature indicator paint, colored crayons, lubricants, fuel and other dirt. The lower the sulfur content of the fuel the better, the sulfur content of natural gas should be less than 0.1%, the sulfur content of heavy oil should be less than 0.5%. Electric furnace heating is a better choice, because the electric furnace can accurately control the temperature and the furnace gas is clean. If the gas stove gas pure enough, you can choose.
    2, alloy thermal processing temperature range of 1080 ℃ ~ 900 ℃, cooling method for water cooling or other rapid cooling. To ensure the best corrosion resistance, heat treatment should be carried out after solution heat treatment.