Bakin karfe piple goge
A takaice bayanin:
Bayanai na Bakin Karfe na Bakin Karfe: |
1. Samfurin | Bakin karfe waldided bututu |
2. Abu | 201,202,301,302,304,309,310S,316L,321,347,410,430,409Letc. |
3. Standard | Astm, Asme, Din, en, Iso, Jis, Gost, da sauransu. |
4. Girman girman | Od: Daga 6mm zuwa 1219mm (NPS Daga 1/8 "zuwa 40") |
WT: Daga 0.7mm zuwa 38mm (Jadawalin daga 5s zuwa XXS) | |
Tsawon: Gyara Tsawon Tsawon Daidai | |
5. Samar da tsari | welded, zafi lanƙwasa; jin daɗin walwala; fadada da mahaifa da sauransu. |
6. Farfajiya | 2b, pickled, 180g, 320g, satin, gashi, 400g, 500g, 600g, 600g, 600g |
, 800g, madubi gama | |
7. Alamar alama | Saky, aji, sumba, misali, girman, zafi a'a. |
8. Kunshin | Bundles tare da zane mai hana ruwa a waje. |
ko akwatin plywood. | |
9. Tsawon | 5.8m, 6m, 12m ko kamar yadda ake buƙata |
Kayan aikin kayan yau da kullun don Alloy na karfe 304 bakin karfe: |
Sa | Tenerile ƙarfi (MPa) | Ingantaccen ƙarfin aiki (MPA) | Hujja ta damuwa 0.2% (MPa) | Elongation A5 (%) | Hardness Rockwell B |
304 | 520-720 | 210 | 210 | 45 min | 92 |
304l | 500-670 | 200 | 45 min | ||
304H | 520-720 | 210 | 45min |
Maki na bakin karfe piple da aka goge: |
Iri | Sa | Sa | Kayan sunadarai% | ||||
Ausenitic bakin karfe | C | Cr | Ni | Mn | |||
201 | 1Cr17NN6N8Ni5n | 0.15 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | ||
201l | 03CR17NMN8NI5N | 0.030 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | ||
202 | 1Cr18n8ni5n | 0.15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | ||
204 | 03cr16n8n8n | 0.030 | 15.00-17.00 | 1.50-3.50 | 7.00-9.00 | ||
1Cr18n10Na5mo3n | 0.10 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 | |||
2Cr13nn9ni4 | 0.15-0.2 | 12.00-14.00 | 3.70-5.00 | 8.00-10.00 | |||
2Cr15n15ni2n | 0.15-0.2 | 14.00-16.00 | 1.50-3.00 | 14.00-16.00 | |||
1Cr18n10Na5mo3n | 0.15 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 | |||
301 | 1Cr17ni7 | 0.15 | 16.00-18.00 | 6.00-8.00 | 2.00 | ||
302 | 1Cr18ni9 | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | ||
303 | Y1CR18NI9 | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | ||
303SE | Y1cr18ni9 | 0.15 | 17.00-19.00 | 8.00-10.00 | 2.00 | ||
304 | 0Cr18ni9 | 0.07 | 17.00-19.00 | 8.00-10.00 | 2.00 | ||
304l | 00cr19ni10 | 0.030 | 18.00-20.00 | 8.00-10.00 | 2.00 | ||
304n1 | 0Cr19ni9n | 0.08 | 18.00-20.00 | 7.00-10.50 | 2.00 | ||
304N2 | 0Cr18ni10nbn | 0.08 | 18.00-20.00 | 7.50-10.50 | 2.00 | ||
304ln | 00cr18ni10n | 0.030 | 17.00-19.00 | 8.50-11.50 | 2.00 | ||
305 | 1Cr18ni12 | 0.12 | 17.00-19.00 | 10.50-13.00 | 2.00 | ||
309s | 0Cr23ni13 | 0.08 | 22.00-24,00 | 12.00-15.00 | 2.00 | ||
310s | 0Cr25Ni20 | 0.08 | 24.00-26.00 | 19.00-22.00 | 2.00 | ||
316 | 0Cr17ni12mo2 | 0.08 | 16.00-18.50 | 10.00-14.00 | 2.00 | ||
1Cr18ni12mo2ti6) | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 | |||
0Cr18ni12mo2ti | 0.08 | 16.00-19.00 | 11.00-14.00 | 2.00 | |||
316l | 00CR17NI14mo2 | 0.030 | 16.00-18.00 | 12.00-15.00 | 2.00 | ||
316N | 0CR17NI12mo2n | 0.08 | 16.00-18.00 | 10.00-14.00 | 2.00 | ||
316N | 00CR17NI13mo2n | 0.030 | 16.00-18.50 | 10.50-14.50 | 2.00 | ||
316J1 | 0Cr18ni12mo2cu2 | 0.08 | 17.00-19.00 | 10.00-14.50 | 2.00 | ||
316J1L | 00CR18ni14mo2cu2 | 0.030 | 17.00-19.00 | 12.00-16.00 | 2.00 | ||
317 | 0Cr19ni13mo3 | 0.12 | 18.00-20.00 | 11.00-15.00 | 2.00 | ||
317l | 00CR19NI13mo3 | 0.08 | 18.00-20.00 | 11.00-15.00 | 2.00 | ||
1Cr18ni12mo3ti6 | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 | |||
0Cr18ni12mo3ti | 0.08 | 16.00-19.00 | 11.00-14.00 | 2.00 | |||
317J1 | 0Cr18ni16mo5 | 0.040 | 16.00-19.00 | 15.00-17.00 | 2.00 | ||
321 | 1Cr18ni9ti6 | 0.12 | 17.00-19.00 | 8.00-11.00 | 2.00 | ||
0Cr18ni10ti | 0.08 | 17.00-19.00 | 9.00-12.00 | 2.00 | |||
347 | 0Cr18ni11nb | 0.08 | 17.00-19.00 | 9.00-13.00 | 2.00 | ||
XM7 | 0Cr18ni9cu3 | 0.08 | 17.00-19.00 | 8.50-10.50 | 2.00 | ||
XM15J1 | 0Cr18ni13si4 | 0.08 | 15-00-20.00 | 11.50-15.00 | 2.00 |
Austenite Ferrite bakin karfe | 329J1 | 0Cr26ni5mo2 | 0.08 | 23.00-28,00 | 3.00-6.00 | 1.50 | 0.035 | 0.030 | 1.00-3.00 | 1.00 | - | - | 2) |
1Cr18ni11si1si4alti | 0.10-0.18 | 17.50-19.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.500 | 10. - 120 .. | 0.80 | 0.035 | 0.030 | - | 3.40-00 | - | - | Al 0.10-0.30; Ti 0.40-0.70 | ||
00CR18NI5MOOSII2 | 0.030 | 18.00-19.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.5.50 | 4.50-5.50 | 1.00-2.00 | 0.035 | 0.030 | 2.50-3.00 | 1.30-2.00 | - | - | - | ||
Ferrite bakin karfe | 405 | 0Cr13Al | 0.08 | 11.50-14.500 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | Al 0.10-0.30 |
410l | 00C12 | 0.030 | 11.00-13.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
430 | 1Cr17 | 0.12 | 16.00-18.00 | 3) | 1.25 | 0.035 | 0.030 | - | 0.75 | - | - | - | |
430f | Y1CR17 | 0.12 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
434 | 1Cr17mo | 0.12 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.030 | 0.75-1.25 | 1.00 | - | - | - | |
447J1 | 00C30mo2 | 0.010 | 28.50-32.00 | - | 0.40 | 0.035 | 0.030 | 1.50-2.50 | 0.40 | - | 0.015 | - | |
XM27 | 00cr27mo | 0.010 | 25.00-27.50 | - | 0.40 | 0.035 | 0.030 | 0.75-1.50 | 0.40 | - | 0.015 | - |
Martensite Bakin Karfe | 403 | 1Cr12 | 0.15 | 11.50-13.00 | 3) | 1.00 | 0.035 | 0.030 | - | 0.50 | - | - | - |
410 | 1Cr13 | 0.15 | 11.50-13.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
405 | 0CR13 | 0.08 | 11.50-13.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
416 | Y1CR13 | 0.15 | 12.00-14.00 | 3) | 1.25 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
410J1 | 1Cr13mo | 0.08-018 | 11.50-14.00 | 3) | 1.00 | 0.035 | 0.030 | 0.30-0.60 | 0.60 | - | - | - | |
420J1 | 2CR13 | 0.16-0.225 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
420j2 | 3CR13 | 0.26-0.35 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
420f | Y3cr13 | 0.26-0.40 | 12.00-14.00 | 3) | 1.25 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
3CR13MO | 0.28-0.35 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | 0.50-1.00 | 0.80 | - | - | - | ||
4CR13 | 0.36-0.45 | 12.00-14.00 | 3) | 0.80 | 0.035 | 0.030 | - | 0.60 | - | - | - | ||
431 | 1Cr17ni2 | 0.11-0.17 | 16.00-18.00 | 1.50-2.50 | 0.80 | 0.035 | 0.030 | - | 0.80 | - | - | - | |
440A | 7CR17 | 0.60-0.75 | 16.00-18.00 | 3) | 1.00 | 0.035 |