Pìob stàilinn gun staten
Tuairisgeul goirid:
Sònrachadh Pìob stàilinn nach bu shiness air a bhlàthachadh: |
1. Bathar | Pìob tàthraichte stàilinn |
2. Stuth | 201,202,301,302,304,309,310S,316L,321,347,410,430,409Letc. |
3. Cothromachd | Astm, asme, din, en, ISO, JIS, GST, msaa. |
4. Raon meud | Od: Bho 6mm gu 1219mm (NPS bho 1/8 "gu 40") |
Wt: bho 0.7mm gu 38mm (clàr bho 5s gu xxs) | |
Fad: Fix Fad no Fad Un-socry, 30meatair Max | |
5. Toradh Pròiseas | làthaichte tàthar, teth; làthadh an aghaidh; leudachadh teirmeach msaa. |
6. uachdar | 2b, picilte, 180g, 320g, satain, hairline, 400g, 500g, 600g |
, 800g, crìochnachadh sgàthan | |
7. A 'comharrachadh | Sky, ìre, sàmhach, àbhaisteach, àbhaisteach, meud, teas nach eil. |
8. Pasgan | Bagaichean le clò dìon a-muigh. |
no bogsa plywood. | |
9. Fad | 5.8m, 6m, 12m no mar a dh 'fheumar |
Togalaichean meacanaigeach àbhaisteach airson 304 Alloys Steel Steel: |
Ìre | Neart teasile (MPA) | Neart teannachaidh (MPA) | Làimhseachadh Profof 0.2% (MPA) | Fada A5 (%) | Cructaradh Rockwell b |
304 | 520-720 | 210 | 210 | 45 min | 92 |
304l | 500-670 | 200 | 45 min | ||
304h | 520-720 | 210 | 45min |
Ìrean de phìob stàilinn nach bu shràid air a bhlàthachadh: |
Seòrsa | Ìre | Ìre | Pàirt ceimigeach% | ||||
Stàilinn austenitic stàilinn | C | Cr | Ni | Mn | |||
201 | 1cr17mn6ni5n | 0.15 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | ||
201l | 03cr17mnimsi5n | 0.030 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | ||
202 | 1cr18mn8ni5n | 0.15 | 17.00-19.00.00 | 4.00-6.00 | 7.50-10.00 | ||
204 | 03cr16mng8ni2n | 0.030 | 15.00-17.00 | 1.50-3.50 | 7.00-9.00.00 | ||
1cr18MN10ni5Mo3n | 0.10 | 17.00-19.00.00 | 4.00-6.00 | 8.50-12.00 | |||
2cr13mn9Ni4 | 0.15-0.25 | 12.00-14.00 | 3.70-5.00 | 8.00-10.00 | |||
2cr15mn15NI2N | 0.15-0.25 | 14.00-16.00 | 1.50-3.00 | 14.00-16.00 | |||
1cr18MN10ni5Mo3n | 0.15 | 17.00-19.00.00 | 4.00-6.00 | 8.50-12.00 | |||
301 | 1cr17Ni7 | 0.15 | 16.00-18.00 | 6.00-8.00 | 2.00 | ||
302 | 1cr18NI9 | 0.15 | 17.00-19.00.00 | 8.00-10.00 | 2.00 | ||
303 | Y1cr18NI9 | 0.15 | 17.00-19.00.00 | 8.00-10.00 | 2.00 | ||
303se | Y1cr18NI9se | 0.15 | 17.00-19.00.00 | 8.00-10.00 | 2.00 | ||
304 | 0cr18NI9 | 0.07 | 17.00-19.00.00 | 8.00-10.00 | 2.00 | ||
304l | 00cr19NI10 | 0.030 | 18.00-20.00.00 | 8.00-10.00 | 2.00 | ||
304n1 | 0cr19Ni9n | 0.08 | 18.00-20.00.00 | 7.00-10.50 | 2.00 | ||
304n2 | 0cr18NICIBN | 0.08 | 18.00-20.00.00 | 7.50-10.50 | 2.00 | ||
304ln | 00cr18NICI10n | 0.030 | 17.00-19.00.00 | 8.50-11.50 | 2.00 | ||
305 | 1cr18NI12 | 0.12 | 17.00-19.00.00 | 10.50-13.00 | 2.00 | ||
309s | 0cr23ni13 | 0.08 | 22.00-24.00 | 12.00-15.00 | 2.00 | ||
310an | 0cr25Ni20 | 0.08 | 24.00-26.00 | 19.00-22.00 | 2.00 | ||
316 | 0cr17Ni12Mo2 | 0.08 | 16.00-18.50 | 10.00-14.00 | 2.00 | ||
1cr18NI2MI12MO2TI6) | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 | |||
0cr18NI2MI12MO2TI | 0.08 | 16.00-19.00 | 11.00-14.00 | 2.00 | |||
316l | 00cr17NI14Mo2 | 0.030 | 16.00-18.00 | 12.00-15.00 | 2.00 | ||
316n | 0cr17Ni12Mo2n | 0.08 | 16.00-18.00 | 10.00-14.00 | 2.00 | ||
316n | 00cr17NI13Mo2N | 0.030 | 16.00-18.50 | 10.50-14.50 | 2.00 | ||
316J1 | 0cr18NI2MI2MO2 | 0.08 | 17.00-19.00.00 | 10.00-14.50 | 2.00 | ||
316J1l | 00cr18NI14Mo2Co2 | 0.030 | 17.00-19.00.00 | 12.00-16.00 | 2.00 | ||
317 | 0cr19Ni13Mo3 | 0.12 | 18.00-20.00.00 | 11.00-15.00 | 2.00 | ||
317l | 00cr19Ni13Mo3 | 0.08 | 18.00-20.00.00 | 11.00-15.00 | 2.00 | ||
1Cr18NI2MI12MO3TITI6 | 0.12 | 16.00-19.00 | 11.00-14.00 | 2.00 | |||
0cr18NI2MI12MO3Ti | 0.08 | 16.00-19.00 | 11.00-14.00 | 2.00 | |||
317J1 | 0cr18N16MO5 | 0.040 | 16.00-19.00 | 15.00-17.00 | 2.00 | ||
321 | 1Cr18NI9TI6 | 0.12 | 17.00-19.00.00 | 8.00-11.00 | 2.00 | ||
0cr18NICITI | 0.08 | 17.00-19.00.00 | 9.00-12.00 | 2.00 | |||
347 | 0cr18NI11NB | 0.08 | 17.00-19.00.00 | 9.00-13.00 | 2.00 | ||
Xm7 | 0cr18NI9CU3 | 0.08 | 17.00-19.00.00 | 8.50-10.50 | 2.00 | ||
Xm15j1 | 0CR18NI13SISI4 | 0.08 | 15.00-20.00 | 11.50-15.00 | 2.00 |
Austenite Stàilinn ferrite stàilinn | 329J1 | 0cr26ni5mo2 | 0.08 | 23.00-28.00 | 3.00-6.00 | 1.50 | 0.035 | 0.030 | 1.00-3.00 | 1.00 | - | - | 2) |
1Cr18NI11SI4ALTI | 0.10-0.18 | 17.50-19-19.50 | 10.-120 .. | 0.80 | 0.035 | 0.030 | - | 3.40-4.00 | - | - | Al 0.10-0.30; Ti 0.40-0.70 | ||
00cr18NIMIMOOSI2 | 0.030 | 18.00-19.50.50 | 4.50-5.50 | 1.00-2.00 | 0.035 | 0.030 | 2.50-3.00 | 1.30-2.00 | - | - | - | ||
Stàilinn ferrite stàilinn | 405 | 0cr13al | 0.08 | 11.50-14.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | Al 0.10-0.30 |
410l | 00cr12 | 0.030 | 11.00-13.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
430 | 1cr17 | 0.12 | 16.00-18.00 | 3) | 1.25 | 0.035 | 0.030 | - | 0.75 | - | - | - | |
430f | Y1cr17 | 0.12 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
434 | 1cr17mo | 0.12 | 16.00-18.00 | 3) | 1.00 | 0.035 | 0.030 | 0.75-1.25 | 1.00 | - | - | - | |
447J1 | 00cr30mo2 | 0.010 | 28.50-22.00 | - | 0.40 | 0.035 | 0.030 | 1.50-2.50 | 0.40 | - | 0.015 | - | |
Xm27 | 00cr27mo | 0.010 | 25.00-27.50 | - | 0.40 | 0.035 | 0.030 | 0.75-1.50 | 0.40 | - | 0.015 | - |
Stàilinn stàilinn martenssite | 403 | 1cr12 | 0.15 | 11.50-13.00 | 3) | 1.00 | 0.035 | 0.030 | - | 0.50 | - | - | - |
410 | 1cr13 | 0.15 | 11.50-13.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
405 | 0cr13 | 0.08 | 11.50-13.50 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
416 | Y1cr13 | 0.15 | 12.00-14.00 | 3) | 1.25 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
410j1 | 1cr13Mo | 0.08-0.18 | 11.50-14.00 | 3) | 1.00 | 0.035 | 0.030 | 0.30-0.60 | 0.60 | - | - | - | |
420j1 | 2cr13 | 0.16-0.25 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
420j2 | 3cr13 | 0.26-0.35 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | - | 1.00 | - | - | - | |
420f | Y3CR13 | 0.26-0.40 | 12.00-14.00 | 3) | 1.25 | 0.035 | 0.15 | 1) | 1.00 | - | - | - | |
3C13Mo | 0.28-0.35 | 12.00-14.00 | 3) | 1.00 | 0.035 | 0.030 | 0.50-1.00 | 0.80 | - | - | - | ||
4cr13 | 0.36-0.45 | 12.00-14.00 | 3) | 0.80 | 0.035 | 0.030 | - | 0.60 | - | - | - | ||
431 | 1cr17ni22 | 0.11-0.17 | 16.00-18.00 | 1.50-2.50 | 0.80 | 0.035 | 0.030 | - | 0.80 | - | - | - | |
440a | 7cr17 | 0.60-0.75 | 16.00-18.00 | 3) | 1.00 | 0.035 |