Stainless Steel T seksje
Koarte beskriuwing:
Stainless Steel T Bar, T seksje of tee-profyl mei graad 201.303.3000,304l, 316,316L, 316TI, 321,310S, 410.430
Spesifikaasjes fanStainless Steel T Bar: |
Standert | ASTM A276, A484, A479, A580, A582, Jis G4303, Jis G4311, Din 1654-5, Din 17440, KS D3706, GB / T 1220 |
Materiaal | 201,202,205, xm-19 ensfh. 301.303.304,304L, 304H, 309S, 310s, 314.316,316L, 316TI, 317.321,321h, 329.330,348 etc. 409.410.416,42030.430ef, 431.440 2205.2507, S31803.2209.630,631,15-5ph, 17-49ph, 17-7ph, 17-77L, F51, F51,253ma ensfh. |
Oerflak | Helder, polearjen, Polishing, skille, swart, grinding, mûne, spegel, haarline ensfh |
Technology | Kâld tekene, hot rôle, smeden |
Spesifikaasjes | as fereaske |
Tolerânsje | H9, H11, H13, K9, K11, K13 as as fereaske |
Supporter foar roestvrij stiel t seksje út sakysteel: |
Gewicht fanStainless Steel T Bar |
Model | Gewicht | Model | Gewicht |
100 * 50 * 5 * 7 | 9.54 | 344 * 354 * 16 * 16 | 131 |
100 * 100 * 6 * 8 | 17.2 | 346 * 174 * 6 * 9 | 41,8 |
125 * 60 * 6 * 8 | 13.3 | 350 * 175 * 7 * 11 | 50 |
125 * 125 * 6.5 * 9 | 23.8 | 344 * 348 * 10 * 16 | 115 |
148 * 100 * 6 * 9 | 21.4 | 350 * 350 * 12 * 19 | 137 |
150 * 75 * 5 * 7 | 14.3 | 388 * 402 * 15 * 15 | 141 |
150 * 150 * 7 * 10 | 31,9 | 390 * 300 * 10 * 16 | 107 |
175 * 90 * 5 * 8 | 18.2 | 394 * 398 * 11 * 18 | 147 |
175 * 175 * 7,5 * 11 | 40.3 | 400 * 150 * 8 * 13 | 55.8 |
194 * 150 * 6 * 9 | 31.2 | 396 * 199 * 7 * 11 | 56.7 |
198 * 99 * 4.5 * 7 | 18.5 | 400 * 200 * 8 * 13 | 66 |
200 * 100 * 5.5 * 8 | 21.7 | 400 * 400 * 13 * 21 | 172 |
200 * 200 * 8 * 12 | 50.5 | 400 * 408 * 21 * 21 | 197 |
200 * 204 * 12 * 12 | 72.28 | 414 * 405 * 18 * 28 | 233 |
244 * 175 * 7 * 11 | 44.1 | 440 * 300 * 11 * 18 | 124 |
244 * 252 * 11 * 11 | 64.4 | 446 * 199 * 7 * 11 | 66.7 |
248 * 124 * 5 * 8 | 25.8 | 450 * 200 * 9-14 | 76.5 |
250 * 125 * 6 * 9 | 29.7 | 482 * 300 * 11 * 15 | 115 |
250 * 250 * 9 * 14 | 72,4 | 488 * 300 * 11 * 18 | 129 |
250 * 255 * 14 * 14 | 82.2 | 496 * 199 * 9 * 14 | 79.5 |
294 * 200 * 8 * 12 | 57.3 | 500 * 200 * 10 * 16 | 89.6 |
300 * 150 * 6.5 * 9 | 37.3 | 582 * 300 * 12 * 17 | 137 |
294 * 302 * 12 * 12 | 85 | 588 * 300 * 12 * 20 | 151 |
300 * 300 * 10 * 15 | 94.5 | 596 * 199 * 10 * 15 | 95.1 |
300 * 305 * 15 * 15 | 106 | 600 * 200 * 11 * 17 | 106 |
338 * 351 * 13 * 13 | 106 | 700 * 300 * 13 * 24 | 185 |
340 * 250 * 9 * 14 | 79.7 |
Mear klasse fanStainless Steel T Bar: |
Type | Klasse | Klasse | Gemyske komponint% | ||||||||||
C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | Oar | |||
Austenityske roestfrij stiel | 201 | 1cr17mn6ni5n | 0,15 | 16.00-18,00 | 3.50-5.50 | 5.50-7.50 | 0,060 | 0.030 | - | 1,00 | - | 0,25 | - |
201l | 03Cr17mn6ni5n | 0.030 | 16.00-18,00 | 3.50-5.50 | 5.50-7.50 | 0,060 | 0.030 | 1,00 | 0,25 | ||||
202 | 1Cr18mn8ni5n | 0,15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | 0,060 | 0.030 | 1,00 | - | 0,25 | - | ||
204 | 03Cr16mn8ni2n | 0.030 | 15.00-17.00 | 1.50-3,50 | 7.00-9.00 | 0.15-0.30 | |||||||
1Cr18mn10ni5mo3n | 0.10 | 17.00-19.00 | 4.00-6.00 | 8.50-12,00 | 2.80-3.50 | 0.20-0.30 | |||||||
2Cr13mn9ni4 | 0.15-0.25 | 12.00-14.00 | 3,70-5.00 | 8-1-10,00 | |||||||||
2CR15MN15NI2N | 0.15-0.25 | 14.00-16.00 | 1.50-3.00 | 14.00-16.00 | 0.15-0.30 | ||||||||
1Cr18mn10ni5mo3n | 0,15 | 17.00-19.00 | 4.00-6.00 | 8.50-12,00 | 0,060 | 0.030 | 2.8-3.5 | 1,00 | - | 0.20-0.30 | - | ||
301 | 1cr17ni7 | 0,15 | 16.00-18,00 | 6.00-8.00 | 2.00 | 0.065 | 0.030 | - | 1,00 | - | - | - | |
302 | 1Cr18ni9 | 0,15 | 17.00-19.00 | 8-1-10,00 | 2.00 | 0,035 | 0.030 | - | 1,00 | - | - | - | |
303 | Y1cr18ni9 | 0,15 | 17.00-19.00 | 8-1-10,00 | 2.00 | 0.20 | 0.030 | 1) | 1,00 | - | - | - | |
303se | Y1cr18ni9se | 0,15 | 17.00-19.00 | 8-1-10,00 | 2.00 | 0.20 | 0.030 | - | 1,00 | - | - | SE = 0,15 | |
304 | 0cr18ni9 | 0,07 | 17.00-19.00 | 8-1-10,00 | 2.00 | 0,035 | 0.030 | - | 1,00 | - | - | - | |
304L | 00cr19ni10 | 0.030 | 18.00-20.00 | 8-1-10,00 | 2.00 | 0,035 | 0.030 | - | 1,00 | - | - | - | |
304n1 | 0cr19ni9n | 0.08 | 18.00-20.00 | 7--10,50 | 2.00 | 0,035 | 0.030 | - | 1,00 | - | 0.10-0.25 | - | |
304n2 | 0cr18ni10nbn | 0.08 | 18.00-20.00 | 7.50-10.50 | 2.00 | 0,035 | 0.030 | - | 1,00 | - | 0.15-0.30 | NB = 0,15 | |
304L | 00cr18ni10n | 0.030 | 17.00-19.00 | 8.50-11.50 | 2.00 | 0,035 | 0.030 | - | 1,00 | - | 0.12-0.22 | - | |
305 | 1Cr18ni12 | 0.12 | 17.00-19.00 | 10.50-13.00 | 2.00 | 0,035 | 0.030 | - | 1,00 | - | - | - | |
309s | 0cr23ni13 | 0.08 | 22.00-24.00 | 12.00-15,00 | 2.00 | 0,035 | 0.030 | - | 1,00 | - | - | - | |
310s | 0cr25ni20 | 0.08 | 24.00-26,00 | 19.00-22.00 | 2.00 | 0,035 | 0.030 | - | 1,00 | - | - | - | |
316 | 0cr17ni12mo2 | 0.08 | 16.00-18.50 | 10.00-14,00 | 2.00 | 0,035 | 0.030 | 2.00-3.00 | 1,00 | - | - | - | |
1Cr18ni12Mo2ti6) | 0.12 | 16.00-19.00 | 11.00-14,00 | 2.00 | 0,035 | 0.030 | 1.80-2.50 | 1,00 | - | - | TI5 (C% -0.02) ~ 0.08 | ||
0cr18ni12mo2ti | 0.08 | 16.00-19.00 | 11.00-14,00 | 2.00 | 0,035 | 0.030 | 1.80-2.50 | 1,00 | - | - | TI5 * c% -0.70 | ||
316L | 00cr17ni14mo2 | 0.030 | 16.00-18,00 | 12.00-15,00 | 2.00 | 0,035 | 0.030 | 2.00-3.00 | 1,00 | - | - | - | |
316N | 0cr17ni12mo2n | 0.08 | 16.00-18,00 | 10.00-14,00 | 2.00 | 0,035 | 0.030 | 2.00-3.00 | 1,00 | - | 0.10-0.22 | - | |
316N | 00cr17ni13mo2n | 0.030 | 16.00-18.50 | 10.50-14,50 | 2.00 | 0,035 | 0.030 | 2.00-3.00 | 1,00 | - | 0.12-0.22 | - | |
316J1 | 0cr18ni12co2cu2 | 0.08 | 17.00-19.00 | 10.00-14,50 | 2.00 | 0,035 | 0.030 | 1.20-2.75 | 1,00 | 1.00-2,50 | - | - | |
316J1L | 00cr18ni14mo2cu2 | 0.030 | 17.00-19.00 | 12.00-16,00 | 2.00 | 0,035 | 0.030 | 1.20-2.75 | 1,00 | 1.00-2,50 | - | - | |
317 | 0CR19ni13mo3 | 0.12 | 18.00-20.00 | 11.00-15,00 | 2.00 | 0,035 | 0.030 | 3.00-4.00 | 1,00 | - | - | - | |
317L | 00cr19ni13mo3 | 0.08 | 18.00-20.00 | 11.00-15,00 | 2.00 | 0,035 | 0.030 | 3.00-4.00 | 1,00 | - | - | - | |
1Cr18ni12mo3ti6 | 0.12 | 16.00-19.00 | 11.00-14,00 | 2.00 | 0,035 | 0.030 | 2,50-3,50 | 1,00 | - | - | TI5 (C% -0.02) ~ 0.08 | ||
0cr18ni12mo3ti | 0.08 | 16.00-19.00 | 11.00-14,00 | 2.00 | 0,035 | 0.030 | 2,50-3,50 | 1,00 | - | - | TI5 * c% -0.70 | ||
317j1 | 0cr18ni16mo5 | 0,040 | 16.00-19.00 | 15.00-17.00 | 2.00 | 0,035 | 0.030 | 4.00-6.00 | 1,00 | - | - | - | |
321 | 1Cr18ni9ti6 | 0.12 | 17.00-19.00 | 8.00-11.00 | 2.00 | 0,035 | 0.030 | - | 1,00 | - | - | TI5 (C% -0.02) ~ 0.08 | |
0cr18ni10ti | 0.08 | 17.00-19.00 | 9.00-12.00 | 2.00 | 0,035 | 0.030 | - | 1,00 | - | - | TI = 5 * c% | ||
347 | 0cr18ni11nb | 0.08 | 17.00-19.00 | 9.00-13.00 | 2.00 | 0,035 | 0.030 | - | 1,00 | - | - | NB = 10 * c% | |
Xm7 | 0cr18ni9cu3 | 0.08 | 17.00-19.00 | 8.50-10.50 | 2.00 | 0,035 | 0.030 | - | 1,00 | 3.00-4.00 | - | - | |
Xm15j1 | 0Cr18ni13si4 | 0.08 | 15.00-20.00 | 11.50-15,00 | 2.00 | 0,035 | 0.030 | - | 3.00-5.00 | - | - | 2) | |
Austenite | 329J1 | 0cr6ni5mo2 | 0.08 | 23.00-28.00 oere | 3.00-6.00 | 1,50 | 0,035 | 0.030 | 1.00-3.00 | 1,00 | - | - | 2) |
| | 1Cr18ni11i4alti | 0.10-0.18 | 17.50-19.50 | 10.-120 .. | 0,80 | 0,035 | 0.030 | - | 3.40-4.00 | - | - | Al 0.10-0.30; TI 0,40-0.70 | |
Ferriet stainless stiel | 00cr18ni5mosi2 | 0.030 | 18.00-19.50 | 4,50-5,50 | 1.00-2,00 | 0,035 | 0.030 | 2,50-3.00 | 1.30-2.00 | - | - | - | |
Ferriet stainless stiel | 405 | 0cr13al | 0.08 | 11.50-14,50 | 3) | 1,00 | 0,035 | 0.030 | - | 1,00 | - | - | AL 0.10-0.30 |
410l | 00cr12 | 0.030 | 11.00-13.00 | 3) | 1,00 | 0,035 | 0.030 | - | 1,00 | - | - | - | |
430 | 1cr17 | 0.12 | 16.00-18,00 | 3) | 1,25 | 0,035 | 0.030 | - | 0.75 | - | - | - | |
430f | Y1CR17 | 0.12 | 16.00-18,00 | 3) | 1,00 | 0,035 | 0,15 | 1) | 1,00 | - | - | - | |
434 | 1Cr17Mo | 0.12 | 16.00-18,00 | 3) | 1,00 | 0,035 | 0.030 | 0.75-1.25 | 1,00 | - | - | - | |
447j1 | 00cr30mo2 | 0.010 | 28.50-32.00 | - | 0,40 | 0,035 | 0.030 | 1,50-2,50 | 0,40 | - | = 0.015 | - | |
Xm27 | 00CR27MO | 0.010 | 25-27.50 | - | 0,40 | 0,035 | 0.030 | 0.75-1,50 | 0,40 | - | = 0.015 | - | |
Martensite Stainless Steel | 403 | 1Cr12 | 0,15 | 11.50-13.00 | 3) | 1,00 | 0,035 | 0.030 | - | 0,50 | - | - | - |
410 | 1cr13 | 0,15 | 11.50-13.50 | 3) | 1,00 | 0,035 | 0.030 | - | 1,00 | - | - | - | |
405 | 0cr13 | 0.08 | 11.50-13.50 | 3) | 1,00 | 0,035 | 0.030 | - | 1,00 | - | - | - | |
416 | Y1cr13 | 0,15 | 12.00-14.00 | 3) | 1,25 | 0,035 | 0,15 | 1) | 1,00 | - | - | - | |
410j1 | 1Cr13mo | 0,08-0.18 | 11.50-14,00 | 3) | 1,00 | 0,035 | 0.030 | 0.30-0.60 | 0,60 | - | - | - | |
420j1 | 2CR13 | 0.16-0.25 | 12.00-14.00 | 3) | 1,00 | 0,035 | 0.030 | - | 1,00 | - | - | - | |
420j2 | 3CR13 | 0.26-0.35 | 12.00-14.00 | 3) | 1,00 | 0,035 | 0.030 | - | 1,00 | - | - | - | |
420f | Y3cr13 | 0.26-0.40 | 12.00-14.00 | 3) | 1,25 | 0,035 | 0,15 | 1) | 1,00 | - | - | - | |
3Cr13mo | 0.28-0.35 | 12.00-14.00 | 3) | 1,00 | 0,035 | 0.030 | 0.50-1.00 | 0,80 | - | - | - | ||
4CR13 | 0,36-0.45 | 12.00-14.00 | 3) | 0,80 | 0,035 | 0.030 | - | 0,60 | - | - | - | ||
431 | 1cr17ni2 | 0.11-0.17 | 16.00-18,00 | 1,50-2,50 | 0,80 | 0,035 | 0.030 | - | 0,80 | - | - | - | |
440a | 7cr17 | 0.60-0.75 | 16.00-18,00 | 3) | 1,00 | 0,035 | 0.030 | 4) | 1,00 | - | - | - | |
440b | 8CR17 | 0.75-0.95 | 16.00-18,00 | 3) | 1,00 | 0,035 | 0.030 | 4) | 1,00 | - | - | - | |
9cr18 | 0.90-1.00 | 17.00-19.00 | 3) | 0,80 | 0,035 | 0.030 | 4) | 0,80 | - | - | - | ||
440c | 11Cr17 | 0.95-1.20 | 16.00-18,00 | 3) | 1,00 | 0,035 | 0.030 | 4) | 1,00 | - | - | - | |
440F | Y11CR17 | 0.95-1.20 | 16.00-18,00 | 3) | 1,25 | 0,035 | 0,15 | 4) | 1,00 | - | - | - | |
9CR18mo | 0.95-1.10 | 16.00-18,00 | 3) | 0,80 | 0,035 | 0.030 | 0,40-0.70 | 0,80 | - | - | - | ||
9cr18mov | 0,85-0,95 | 17.00-19.00 | 3) | 0,80 | 0,035 | 0.030 | 1.00-1.30 | 0,80 | - | - | V0.07-0.12 | ||
Ph rostfrij stiel | 630 | 0cr17ni4cu4nb | 0,07 | 15.50-17,50 | 6.50-7.50 | 1,00 | 0,035 | 0.030 | - | 1,00 | 3.00-5.00 | - | NB 0.15-0.45 |
631 | 0cr17ni727 | 0,09 | 16.00-18,00 | 6.50-7.50 | 1,00 | 0,035 | 0.030 | - | 1,00 | 0,50 | - | AL 0.75-1,50 |