420 Stainless Steel Flat Bar

Short Description:


  • Standard:: A276 / A484 / DIN 1028
  • Material:: 303 304 316 321 410 420
  • Surface:: Brigt,Polished, Milling ,No.1
  • Techinque:: Hot Rolled & Cold Drawn & Cut
  • Product Detail

    Product Tags

    Din 1.4034 SS 430 Flat Bars, SS UNS S42000 Flat Bars, Stainless Steel 420 Flat Bar, 420 Stainless Steel Cold Drawn Bars Suppliers in China.

    Grade 420 stainless steel is a high-carbon steel with a minimum chromium content of 12%. Like any other stainless steel, grade 420 can also be hardened through heat treatment. It offers good ductility in its annealed state and excellent corrosion resistance properties when the metal is polished, surface grounded or hardened. This grade has the highest hardness – 50HRC – among all the stainless steel grades with 12% chromium.

    420 Stainless Steel Flat Bar Spections:
    Specification: A276/484 / DIN 1028
    Material: 304 316 321 904L 410 420 2205
    Stainless Steel Round Bars: Outside Diameter in the range of 4mm to 500mm
    Width: 1mm to 500mm
    Thickness: 1mm to 500mm
    Technique: Hot Rolled Annealed & Pickled (HRAP) & Cold drawn & Forged & Cut Sheet and Coil
    Length: 3 to 6 Meters / 12 to 20 feet
    Marking: Size, Grade, Manufacture name on Each Bars/Pieces
    Packing: Each steel bar has the singal, and several will be bundled by weaving bag or as per requirement.

     

    Stainless Steel 420 Flat Bars Equivalent Grades:
    STANDARD JIS WERKSTOFF NR. BS AFNOR SIS UNS AISI
    SS 420
    SUS 420 1.4021 420S29 - 2303 S42000 420

     

    SS 420 Flat Bars Chemical Composition (saky steel):
    Grade C Mn Si P S Cr Ni Mo
    SUS 420
    0.15 max 1.0 max 1.0 max 0.040 max 0.030 max 12.0-14.0 -
    -

     

    SS 420 Flat Bars Mechanical properties(saky steel):
    empering Temperature (°C) Tensile Strength (MPa) Yield Strength
    0.2% Proof (MPa)
    Elongation
    (% in 50mm)
    Hardness Brinell
    (HB)
    Annealed * 655 345 25 241 max
    399°F (204°C) 1600 1360 12 444
    600°F (316°C) 1580 1365 14 444
    800°F (427°C) 1620 1420 10 461
    1000°F (538°C) 1305 1095 15 375
    1099°F (593°C) 1035 810 18 302
    1202°F (650°C) 895 680 20 262
    * Annealed tensile properties are typical for Condition A of ASTM A276; annealed hardness is the specified maximum.

     

    SAKY STEEL’S Quality Assurance (including both Destructive and Non-Destructive) :

    1. Visual Dimension Test
    2. Mechanical examining like tensile, Elongation and reduction of area.
    3. Ultrasonic test
    4. Chemical examination analysis
    5. Hardness test
    6. Pitting protection test
    7. Penetrant Test
    8. Intergranular Corrosion Testing
    9. Impact analysis
    10. Metallography Experimental Test

     

    Packaging:

    1. Packing is quite important especially in a case of international shipments in which consignment pass through various channels to reach the ultimate destination, so we put special concern regarding packaging.
    2. Saky Steel’s pack our goods in numerous ways based on the products. We pack our products in multiple ways, such as,

    420 ss flat bar package 20220409


    Applications:

    Applications requiring moderate corrosion resistance and high mechanical properties are ideal for Alloy 420. Examples of applications that frequently used Alloy 420 include:

    Cutlery
    Steam and gas turbine blades
    Kitchen utensils
    Bolts, nuts, screws
    Pump and valve parts and shafts
    Mine ladder rugs
    Dental and surgical instruments
    Nozzles
    Hardened steel balls and seats for oil well pumps