410 Stainless Steel Flat Bar
Short Description:
UNS S41000 Flat Bars, SS 410 Flat Bars, AISI SS 410 Stainless Steel 410 Flat Bars Supplier, Manufacturer and Exporter in China.
410 Stainless Steel is hardenable, straight-chromium stainless steels which combine superior wear resistance of high carbon alloys with the excellent corrosion resistance of chromium stainless steels. Oil quenching these alloys from temperatures between 1800°F to 1950°F (982-1066°C) produces the highest strength and/or wear resistance as well as corrosion resistance. 410 Stainless Steel is used where strength, hardness, and/or wear resistance must be combined with corrosion resistance.
| 410 Stainless Steel Flat Bar Spections: |
| Specification: | A276/484 / DIN 1028 |
| Material: | 303 304 316 321 410 420 |
| Stainless Steel Round Bars: | Outside Diameter in the range of 4mm to 500mm |
| Width: | 1mm to 500mm |
| Thickness: | 1mm to 500mm |
| Technique: | Hot Rolled Annealed & Pickled (HRAP) & Cold drawn & Forged & Cut Sheet and Coil |
| Length: | 3 to 6 Meters / 12 to 20 feet |
| Marking: | Size, Grade, Manufacture name on Each Bars/Pieces |
| Packing: | Each steel bar has the singal, and several will be bundled by weaving bag or as per requirement. |
| Stainless Steel 410 Flat Bars Equivalent Grades: |
| STANDARD | JIS | WERKSTOFF NR. | AFNOR | BS | GOST | UNS |
| SS 410 |
SUS 410 | 1.4006 | Z12C13 | 410 S21 | - | S43000 |
| 410 Flat Bars Chemical Composition and Mechanical properties(saky steel): |
| Grade | C | Mn | Si | P | S | Cr | Ni |
| SS 410 |
0.15 max | 1.0 max | 1.0 max | 0.040 max | 0.030 max | 11.5 – 13.5 | 0.75 |
| Tensile Strength | Yield Strength (0.2%Offset) | Elongation(in 2 in.) |
| MPa: 450 |
MPa – 205 |
20 % |
| SAKY STEEL’S Quality Assurance (including both Destructive and Non-Destructive) : |
1. Visual Dimension Test
2. Mechanical examining like tensile, Elongation and reduction of area.
3. Ultrasonic test
4. Chemical examination analysis
5. Hardness test
6. Pitting protection test
7. Penetrant Test
8. Intergranular Corrosion Testing
9. Impact analysis
10. Metallography Experimental Test
| Packaging: |
1. Packing is quite important especially in a case of international shipments in which consignment pass through various channels to reach the ultimate destination, so we put special concern regarding packaging.
2. Saky Steel’s pack our goods in numerous ways based on the products. We pack our products in multiple ways, such as,
Applications:
Applications requiring moderate corrosion resistance and high mechanical properties are ideal for Alloy 410. Examples of applications that frequently used Alloy 410 include:
Cutlery
Steam and gas turbine blades
Kitchen utensils
Bolts, nuts, screws
Pump and valve parts and shafts
Mine ladder rugs
Dental and surgical instruments
Nozzles
Hardened steel balls and seats for oil well pumps